Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_51_3_20266_BAYeK1.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 22.85 T-atoms per nm^3
Material density = 2.280 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5836 Angstrom
T1  -- O2  = 1.6226 Angstrom
T1  -- O3  = 1.6367 Angstrom
T1  -- O4  = 1.6202 Angstrom
      mean = 1.6158 Angstrom
        t1 = 0.025302  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016676  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6226 Angstrom
T2  -- O7  = 1.6239 Angstrom
T2  -- O5  = 1.6184 Angstrom
T2  -- O6  = 1.6292 Angstrom
      mean = 1.6235 Angstrom
        t1 = 0.014752  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007693  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6379 Angstrom
T3  -- O7  = 1.6288 Angstrom
T3  -- O8  = 1.6177 Angstrom
T3  -- O9  = 1.6246 Angstrom
      mean = 1.6272 Angstrom
        t1 = 0.012953  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004847  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5836 A <--> 1.6379 A
          Mean   = 1.6222 A
          StdDev = 0.0133 A

       t1 Range  = 0.0130 <-- 0.0177 --> 0.0253
       t2 Range  = 0.0048 <-- 0.0097 --> 0.0167

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 104.611 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.585 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 106.808 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 111.680 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 112.163 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 112.498 deg; O3  -- O4  = 3 A
       104.611 deg <-- 109.391 deg --> 112.498 deg

O4  -- T2  -- O7  = 105.976 deg; O4  -- O7  = 3 A
O4  -- T2  -- O5  = 109.616 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 112.317 deg; O4  -- O6  = 3 A
O7  -- T2  -- O5  = 109.674 deg; O7  -- O5  = 3 A
O7  -- T2  -- O6  = 110.109 deg; O7  -- O6  = 3 A
O5  -- T2  -- O6  = 109.095 deg; O5  -- O6  = 3 A
       105.976 deg <-- 109.465 deg --> 112.317 deg

O6  -- T3  -- O7  = 110.954 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 109.016 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 110.075 deg; O6  -- O9  = 3 A
O7  -- T3  -- O8  = 108.582 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 109.066 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 109.112 deg; O8  -- O9  = 3 A
       108.582 deg <-- 109.467 deg --> 110.954 deg

        O-T-O SUMMARY
          Range  = 104.6107 deg <--> 112.4983 deg
          Mean   = 109.5590 deg
          StdDev = 1.9880 deg

        O--O SUMMARY
          Range  = 2.5371 A <--> 2.7080 A
          Mean   = 2.6514 A
          StdDev = 0.0419 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 100.063 deg; T2  -- T1  = 4.8254 A
T2  - O1  - T1  - O3  - T1  = 146.163 deg; T2  -- T1  = 5.8384 A
T2  - O1  - T1  - O4  - T1  = 114.510 deg; T2  -- T1  = 5.1274 A
T1  - O2  - T1  - O3  - T1  = 103.021 deg; T1  -- T1  = 4.7737 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3081 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.1687 A

T1  - O4  - T2  - O7  - T2  = 114.510 deg; T1  -- T2  = 5.2604 A
T1  - O4  - T2  - O5  - T3  =  83.455 deg; T1  -- T3  = 4.0889 A
T1  - O4  - T2  - O6  - T3  = 120.875 deg; T1  -- T3  = 5.3870 A
T2  - O7  - T2  - O5  - T3  = 114.586 deg; T2  -- T3  = 5.1276 A
T2  - O7  - T2  - O6  - T3  = 114.137 deg; T2  -- T3  = 5.1582 A
T3  - O5  - T2  - O6  - T3  = 104.627 deg; T3  -- T3  = 4.7737 A

T2  - O6  - T3  - O7  - T3  = 117.071 deg; T2  -- T3  = 5.0511 A
T2  - O6  - T3  - O8  - T3  = 114.586 deg; T2  -- T3  = 5.0994 A
T2  - O6  - T3  - O9  - T2  = 104.627 deg; T2  -- T2  = 4.7737 A
T3  - O7  - T3  - O8  - T3  =  90.000 deg; T3  -- T3  = 4.2452 A
T3  - O7  - T3  - O9  - T2  = 116.570 deg; T3  -- T2  = 5.0822 A
T3  - O8  - T3  - O9  - T2  = 114.137 deg; T3  -- T2  = 5.1302 A

        T-T-T SUMMARY
          Range  = 83.4548 deg <--> 146.1626 deg
          Mean   = 107.5779 deg
          StdDev = 13.5529 deg

        T--T SUMMARY
          Range  = 4.0889 A <--> 5.8384 A
          Mean   = 4.8710 A
          StdDev = 0.4420 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 166.531 deg ; T1  -- T1   3.1454 A

T1  -- O2  -- T1  = 130.875 deg ; T1  -- T1   2.9515 A

T1  -- O3  -- T1  = 128.136 deg ; T1  -- T1   2.9439 A

T1  -- O4  -- T2  = 152.639 deg ; T1  -- T2   3.1508 A

T2  -- O5  -- T2  = 146.984 deg ; T2  -- T2   3.1035 A

T2  -- O6  -- T3  = 137.226 deg ; T2  -- T3   3.0421 A

T2  -- O7  -- T3  = 133.623 deg ; T2  -- T3   2.9899 A

T3  -- O8  -- T3  = 143.228 deg ; T3  -- T3   3.0702 A

T3  -- O9  -- T3  = 128.931 deg ; T3  -- T3   2.9318 A


        T-O-T SUMMARY
          Range  = 128.1362° <--> 166.5314 deg
          Mean   = 140.9083 deg
          StdDev = 12.1509 deg

        T--T SUMMARY
          Range  = 2.9318 A <--> 3.1508 A
          Mean   = 3.0366 A
          StdDev = 0.0819 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 38 61 87 118 160 206 249 296 358 430 495 559 638
TD10 = 955
Circuit symbol = 4.6.4.6.6_{2}.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6_{2}
Weight = 19

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 25 40 63 95 129 161 198 255 316 365 419 491 577 652
TD10 = 983
Circuit symbol = 6.6_{2}.6.6_{2}.6_{2}.8_{4}
Weight = 29
Vertex symbol  = 6.6_{2}.6.6_{2}.6_{2}.8_{2}
Weight = 29

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 43 66 90 121 165 212 253 298 363 437 498 560 643
TD10 = 990
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

<TD10> = 976.000
Average ring size = 5.7778