Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_4_2_182_oRqlqX.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 24.98 T-atoms per nm^3
Material density = 2.492 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6204 Angstrom
T1  -- O3  = 1.6225 Angstrom
T1  -- O1  = 1.6258 Angstrom
T1  -- O2  = 1.6159 Angstrom
      mean = 1.6211 Angstrom
        t1 = 0.007621  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002594  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6147 Angstrom
T2  -- O4  = 1.6249 Angstrom
T2  -- O4  = 1.6246 Angstrom
T2  -- O3  = 1.6234 Angstrom
      mean = 1.6219 Angstrom
        t1 = 0.008013  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003488  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6147 A <--> 1.6258 A
          Mean   = 1.6215 A
          StdDev = 0.0041 A

       t1 Range  = 0.0076 <-- 0.0078 --> 0.0080
       t2 Range  = 0.0026 <-- 0.0030 --> 0.0035

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 108.838 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 108.865 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 110.377 deg; O1  -- O2  = 3 A
O3  -- T1  -- O1  = 109.891 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  = 109.796 deg; O3  -- O2  = 3 A
O1  -- T1  -- O2  = 109.059 deg; O1  -- O2  = 3 A
       108.838 deg <-- 109.471 deg --> 110.377 deg

O2  -- T2  -- O4  = 109.123 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 110.440 deg; O2  -- O4  = 3 A
O2  -- T2  -- O3  = 109.252 deg; O2  -- O3  = 3 A
O4  -- T2  -- O4  = 109.370 deg; O4  -- O4  = 3 A
O4  -- T2  -- O3  = 109.732 deg; O4  -- O3  = 3 A
O4  -- T2  -- O3  = 108.912 deg; O4  -- O3  = 3 A
       108.912 deg <-- 109.471 deg --> 110.440 deg

        O-T-O SUMMARY
          Range  = 108.8383 deg <--> 110.4396 deg
          Mean   = 109.4713 deg
          StdDev = 0.5547 deg

        O--O SUMMARY
          Range  = 2.6374 A <--> 2.6606 A
          Mean   = 2.6479 A
          StdDev = 0.0086 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T1  = 103.685 deg; T1  -- T1  = 4.6799 A
T1  - O1  - T1  - O1  - T2  =  86.264 deg; T1  -- T2  = 4.2251 A
T1  - O1  - T1  - O2  - T2  = 141.361 deg; T1  -- T2  = 5.6609 A
T1  - O3  - T1  - O1  - T2  = 124.363 deg; T1  -- T2  = 5.4626 A
T1  - O3  - T1  - O2  - T2  = 103.304 deg; T1  -- T2  = 4.7046 A
T2  - O1  - T1  - O2  - T2  = 100.620 deg; T2  -- T2  = 4.7894 A

T2  - O2  - T2  - O4  - T2  = 102.807 deg; T2  -- T2  = 4.6799 A
T2  - O2  - T2  - O4  - T1  = 129.489 deg; T2  -- T1  = 5.6021 A
T2  - O2  - T2  - O3  - T1  = 102.976 deg; T2  -- T1  = 4.7080 A
T2  - O4  - T2  - O4  - T1  =  90.581 deg; T2  -- T1  = 4.4039 A
T2  - O4  - T2  - O3  - T1  = 140.551 deg; T2  -- T1  = 5.6637 A
T1  - O4  - T2  - O3  - T1  =  95.523 deg; T1  -- T1  = 4.6082 A

        T-T-T SUMMARY
          Range  = 86.2636 deg <--> 141.3611 deg
          Mean   = 110.1268 deg
          StdDev = 18.4783 deg

        T--T SUMMARY
          Range  = 4.2251 A <--> 5.6637 A
          Mean   = 4.9324 A
          StdDev = 0.5048 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 132.905 deg ; T1  -- T1   2.9758 A

T1  -- O2  -- T2  = 164.080 deg ; T1  -- T2   3.1995 A

T1  -- O3  -- T2  = 137.268 deg ; T1  -- T2   3.0228 A

T2  -- O4  -- T2  = 134.250 deg ; T2  -- T2   2.9940 A


        T-O-T SUMMARY
          Range  = 132.9055° <--> 164.0802 deg
          Mean   = 142.1260 deg
          StdDev = 13.6553 deg

        T--T SUMMARY
          Range  = 2.9758 A <--> 3.1995 A
          Mean   = 3.0480 A
          StdDev = 0.0952 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 12 26 48 74 104 144 186 234 292 350 416 469 486 509 563
TD10 = 1125
Circuit symbol = 6.6.6_{2}.6_{2}.6_{3}.6_{3}
Weight = 25
Vertex symbol  = 6.6.6_{2}.6_{2}.6_{3}.6_{3}
Weight = 25

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 12 26 48 74 104 144 186 234 292 350 416 469 488 511 551
TD10 = 1125
Circuit symbol = 6.6.6_{2}.6_{2}.6_{3}.6_{3}
Weight = 25
Vertex symbol  = 6.6.6_{2}.6_{2}.6_{3}.6_{3}
Weight = 25

<TD10> = 1125.000
Average ring size = 6.0000