Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_46_2_918_1FsJFI.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 27.74 T-atoms per nm^3
Material density = 2.768 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6076 Angstrom
T1  -- O3  = 1.6829 Angstrom
T1  -- O1  = 1.6408 Angstrom
T1  -- O2  = 1.6069 Angstrom
      mean = 1.6346 Angstrom
        t1 = 0.037040  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025877  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6242 Angstrom
T2  -- O4  = 1.6669 Angstrom
T2  -- O4  = 1.6144 Angstrom
T2  -- O5  = 1.6752 Angstrom
      mean = 1.6452 Angstrom
        t1 = 0.091906  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.122354  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6069 A <--> 1.6829 A
          Mean   = 1.6399 A
          StdDev = 0.0295 A

       t1 Range  = 0.0370 <-- 0.0645 --> 0.0919
       t2 Range  = 0.0259 <-- 0.0741 --> 0.1224

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  = 109.779 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 106.624 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  = 108.882 deg; O2  -- O2  = 3 A
O3  -- T1  -- O1  = 118.181 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  = 107.552 deg; O3  -- O2  = 3 A
O1  -- T1  -- O2  = 105.489 deg; O1  -- O2  = 3 A
       105.489 deg <-- 109.418 deg --> 118.181 deg

O3  -- T2  -- O4  = 108.601 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  =  86.157 deg; O3  -- O4  = 2 A
O3  -- T2  -- O5  = 126.624 deg; O3  -- O5  = 3 A
O4  -- T2  -- O4  = 123.197 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 108.037 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 104.397 deg; O4  -- O5  = 3 A
       86.157 deg <-- 109.502 deg --> 126.624 deg

        O-T-O SUMMARY
          Range  = 86.1573 deg <--> 126.6238 deg
          Mean   = 109.4600 deg
          StdDev = 9.8778 deg

        O--O SUMMARY
          Range  = 2.2120 A <--> 2.9480 A
          Mean   = 2.6689 A
          StdDev = 0.1808 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O2  - T1  - O3  - T2  =  96.463 deg; T1  -- T2  = 4.2300 A
T1  - O2  - T1  - O1  - T1  = 100.335 deg; T1  -- T1  = 4.5803 A
T1  - O2  - T1  - O2  - T1  = 158.764 deg; T1  -- T1  = 5.2302 A
T2  - O3  - T1  - O1  - T1  =  95.231 deg; T2  -- T1  = 4.6453 A
T2  - O3  - T1  - O2  - T1  =  76.834 deg; T2  -- T1  = 3.5292 A
T1  - O1  - T1  - O2  - T1  = 100.335 deg; T1  -- T1  = 4.5803 A

T2  - O3  - T2  - O4  - T2  =  90.000 deg; T2  -- T2  = 3.9545 A
T2  - O3  - T2  - O4  - T1  =  72.577 deg; T2  -- T1  = 3.5292 A
T2  - O3  - T2  - O5  - T2  = 124.118 deg; T2  -- T2  = 5.2302 A
T2  - O4  - T2  - O4  - T1  = 159.062 deg; T2  -- T1  = 5.5315 A
T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 3.9545 A
T1  - O4  - T2  - O5  - T2  =  90.371 deg; T1  -- T2  = 4.2300 A

        T-T-T SUMMARY
          Range  = 72.5765 deg <--> 159.0620 deg
          Mean   = 104.5073 deg
          StdDev = 27.3708 deg

        T--T SUMMARY
          Range  = 3.5292 A <--> 5.5315 A
          Mean   = 4.4354 A
          StdDev = 0.6318 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 178.941 deg ; T1  -- T1   3.2814 A

T1  -- O2  -- T1  = 111.724 deg ; T1  -- T1   2.6607 A

T1  -- O3  -- T2  = 130.422 deg ; T1  -- T2   3.0025 A

T2  -- O4  -- T2  = 128.874 deg ; T2  -- T2   2.9602 A

T2  -- O5  -- T2  = 103.007 deg ; T2  -- T2   2.6222 A


        T-O-T SUMMARY
          Range  = 103.0071° <--> 178.9407 deg
          Mean   = 130.5936 deg
          StdDev = 26.6314 deg

        T--T SUMMARY
          Range  = 2.6222 A <--> 3.2814 A
          Mean   = 2.9054 A
          StdDev = 0.2455 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O4  = 2.2120 A
T1  -- T1  = 2.6607 Angstrom
T1  -- T1  = 2.6607 Angstrom
T2  -- T2  = 2.6222 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 19 31 48 69 93 120 150 186 226 268 313 361 416 475
TD10 = 731
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12_{2}
Weight = 29

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 8 14 25 42 63 84 110 148 186 214 250 310 371 408 449
TD10 = 685
Circuit symbol = 4.4.4.4.6_{2}.6_{2}
Weight = 9
Vertex symbol  = 4.4.4.4.12_{2}.*
Weight = 24

<TD10> = 708.000
Average ring size = 5.5714