Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_46_2_865_dIe4_Z.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 18.27 T-atoms per nm^3
Material density = 1.823 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6060 Angstrom
T1  -- O3  = 1.6465 Angstrom
T1  -- O1  = 1.6162 Angstrom
T1  -- O2  = 1.6133 Angstrom
      mean = 1.6205 Angstrom
        t1 = 0.022836  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013843  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6222 Angstrom
T2  -- O4  = 1.6310 Angstrom
T2  -- O5  = 1.6351 Angstrom
T2  -- O4  = 1.6225 Angstrom
      mean = 1.6277 Angstrom
        t1 = 0.019384  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018359  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6060 A <--> 1.6465 A
          Mean   = 1.6241 A
          StdDev = 0.0122 A

       t1 Range  = 0.0194 <-- 0.0211 --> 0.0228
       t2 Range  = 0.0138 <-- 0.0161 --> 0.0184

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  = 105.969 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 110.358 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  = 105.682 deg; O2  -- O2  = 3 A
O3  -- T1  -- O1  = 109.957 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  = 114.967 deg; O3  -- O2  = 3 A
O1  -- T1  -- O2  = 109.726 deg; O1  -- O2  = 3 A
       105.682 deg <-- 109.443 deg --> 114.967 deg

O3  -- T2  -- O4  = 108.633 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 113.375 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 105.896 deg; O3  -- O4  = 3 A
O4  -- T2  -- O5  = 108.598 deg; O4  -- O5  = 3 A
O4  -- T2  -- O4  = 111.915 deg; O4  -- O4  = 3 A
O5  -- T2  -- O4  = 108.466 deg; O5  -- O4  = 3 A
       105.896 deg <-- 109.481 deg --> 113.375 deg

        O-T-O SUMMARY
          Range  = 105.6823 deg <--> 114.9669 deg
          Mean   = 109.4619 deg
          StdDev = 2.8192 deg

        O--O SUMMARY
          Range  = 2.5657 A <--> 2.7489 A
          Mean   = 2.6513 A
          StdDev = 0.0513 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O2  - T1  - O3  - T2  =  82.808 deg; T1  -- T2  = 3.9599 A
T1  - O2  - T1  - O1  - T1  = 114.288 deg; T1  -- T1  = 5.3167 A
T1  - O2  - T1  - O2  - T1  = 106.383 deg; T1  -- T1  = 5.0178 A
T2  - O3  - T1  - O1  - T1  = 137.986 deg; T2  -- T1  = 5.6403 A
T2  - O3  - T1  - O2  - T1  =  94.919 deg; T2  -- T1  = 4.4093 A
T1  - O1  - T1  - O2  - T1  = 114.288 deg; T1  -- T1  = 5.3167 A

T1  - O3  - T2  - O4  - T2  =  97.334 deg; T1  -- T2  = 4.4093 A
T1  - O3  - T2  - O5  - T2  = 172.196 deg; T1  -- T2  = 5.5865 A
T1  - O3  - T2  - O4  - T2  =  84.786 deg; T1  -- T2  = 3.9599 A
T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.0914 A
T2  - O4  - T2  - O4  - T2  = 112.065 deg; T2  -- T2  = 5.0178 A
T2  - O5  - T2  - O4  - T2  =  90.000 deg; T2  -- T2  = 4.0914 A

        T-T-T SUMMARY
          Range  = 82.8079 deg <--> 172.1958 deg
          Mean   = 108.0877 deg
          StdDev = 24.6658 deg

        T--T SUMMARY
          Range  = 3.9599 A <--> 5.6403 A
          Mean   = 4.7347 A
          StdDev = 0.6240 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 162.644 deg ; T1  -- T1   3.1955 A

T1  -- O2  -- T1  = 153.494 deg ; T1  -- T1   3.1336 A

T1  -- O3  -- T2  = 120.994 deg ; T1  -- T2   2.8449 A

T2  -- O4  -- T2  = 136.813 deg ; T2  -- T2   3.0251 A

T2  -- O5  -- T2  = 114.776 deg ; T2  -- T2   2.7547 A


        T-O-T SUMMARY
          Range  = 114.7763° <--> 162.6436 deg
          Mean   = 137.7442 deg
          StdDev = 18.5473 deg

        T--T SUMMARY
          Range  = 2.7547 A <--> 3.1955 A
          Mean   = 2.9907 A
          StdDev = 0.1698 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T2  = 2.7547 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 19 31 48 69 93 120 150 186 226 268 313 361 416 475
TD10 = 731
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12_{2}
Weight = 29

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 8 14 25 42 63 84 110 148 186 214 250 310 371 408 449
TD10 = 685
Circuit symbol = 4.4.4.4.6_{2}.6_{2}
Weight = 9
Vertex symbol  = 4.4.4.4.12_{2}.*
Weight = 24

<TD10> = 708.000
Average ring size = 5.5714