Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_46_2_379_i45Iyu.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 18.32 T-atoms per nm^3
Material density = 1.828 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6060 Angstrom
T1  -- O3  = 1.6462 Angstrom
T1  -- O1  = 1.6166 Angstrom
T1  -- O2  = 1.6138 Angstrom
      mean = 1.6206 Angstrom
        t1 = 0.023295  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014139  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6220 Angstrom
T2  -- O4  = 1.6310 Angstrom
T2  -- O5  = 1.6343 Angstrom
T2  -- O4  = 1.6225 Angstrom
      mean = 1.6275 Angstrom
        t1 = 0.019412  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018241  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6060 A <--> 1.6462 A
          Mean   = 1.6241 A
          StdDev = 0.0120 A

       t1 Range  = 0.0194 <-- 0.0214 --> 0.0233
       t2 Range  = 0.0141 <-- 0.0162 --> 0.0182

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  = 105.797 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 110.424 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  = 105.598 deg; O2  -- O2  = 3 A
O3  -- T1  -- O1  = 110.003 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  = 115.065 deg; O3  -- O2  = 3 A
O1  -- T1  -- O2  = 109.762 deg; O1  -- O2  = 3 A
       105.598 deg <-- 109.441 deg --> 115.065 deg

O3  -- T2  -- O4  = 108.749 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 113.349 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 105.771 deg; O3  -- O4  = 3 A
O4  -- T2  -- O5  = 108.586 deg; O4  -- O5  = 3 A
O4  -- T2  -- O4  = 111.947 deg; O4  -- O4  = 3 A
O5  -- T2  -- O4  = 108.480 deg; O5  -- O4  = 3 A
       105.771 deg <-- 109.480 deg --> 113.349 deg

        O-T-O SUMMARY
          Range  = 105.5978 deg <--> 115.0653 deg
          Mean   = 109.4609 deg
          StdDev = 2.8760 deg

        O--O SUMMARY
          Range  = 2.5647 A <--> 2.7505 A
          Mean   = 2.6512 A
          StdDev = 0.0522 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O2  - T1  - O3  - T2  =  82.645 deg; T1  -- T2  = 3.9509 A
T1  - O2  - T1  - O1  - T1  = 114.350 deg; T1  -- T1  = 5.3124 A
T1  - O2  - T1  - O2  - T1  = 106.305 deg; T1  -- T1  = 5.0072 A
T2  - O3  - T1  - O1  - T1  = 137.914 deg; T2  -- T1  = 5.6380 A
T2  - O3  - T1  - O2  - T1  =  95.039 deg; T2  -- T1  = 4.4106 A
T1  - O1  - T1  - O2  - T1  = 114.350 deg; T1  -- T1  = 5.3124 A

T1  - O3  - T2  - O4  - T2  =  97.503 deg; T1  -- T2  = 4.4106 A
T1  - O3  - T2  - O5  - T2  = 172.012 deg; T1  -- T2  = 5.5875 A
T1  - O3  - T2  - O4  - T2  =  84.654 deg; T1  -- T2  = 3.9509 A
T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.0863 A
T2  - O4  - T2  - O4  - T2  = 112.102 deg; T2  -- T2  = 5.0072 A
T2  - O5  - T2  - O4  - T2  =  90.000 deg; T2  -- T2  = 4.0863 A

        T-T-T SUMMARY
          Range  = 82.6454 deg <--> 172.0124 deg
          Mean   = 108.0729 deg
          StdDev = 24.6350 deg

        T--T SUMMARY
          Range  = 3.9509 A <--> 5.6380 A
          Mean   = 4.7300 A
          StdDev = 0.6250 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 161.958 deg ; T1  -- T1   3.1931 A

T1  -- O2  -- T1  = 152.652 deg ; T1  -- T1   3.1286 A

T1  -- O3  -- T2  = 121.127 deg ; T1  -- T2   2.8463 A

T2  -- O4  -- T2  = 136.137 deg ; T2  -- T2   3.0181 A

T2  -- O5  -- T2  = 114.875 deg ; T2  -- T2   2.7548 A


        T-O-T SUMMARY
          Range  = 114.8751° <--> 161.9584 deg
          Mean   = 137.3500 deg
          StdDev = 18.1701 deg

        T--T SUMMARY
          Range  = 2.7548 A <--> 3.1931 A
          Mean   = 2.9882 A
          StdDev = 0.1678 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T2  = 2.7548 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 19 31 48 69 93 120 150 186 226 268 313 361 416 475
TD10 = 731
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12_{2}
Weight = 29

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 8 14 25 42 63 84 110 148 186 214 250 310 371 408 449
TD10 = 685
Circuit symbol = 4.4.4.4.6_{2}.6_{2}
Weight = 9
Vertex symbol  = 4.4.4.4.12_{2}.*
Weight = 24

<TD10> = 708.000
Average ring size = 5.5714