Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_42_2_86_yOxNli.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 23.16 T-atoms per nm^3
Material density = 2.311 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6161 Angstrom
T1  -- O2  = 1.6330 Angstrom
T1  -- O2  = 1.6416 Angstrom
T1  -- O3  = 1.6294 Angstrom
      mean = 1.6300 Angstrom
        t1 = 0.028480  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016755  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6187 Angstrom
T2  -- O4  = 1.5222 Angstrom
T2  -- O4  = 1.6515 Angstrom
T2  -- O3  = 1.6187 Angstrom
      mean = 1.6028 Angstrom
        t1 = 0.061122  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.062377  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5222 A <--> 1.6515 A
          Mean   = 1.6209 A
          StdDev = 0.0318 A

       t1 Range  = 0.0285 <-- 0.0448 --> 0.0611
       t2 Range  = 0.0168 <-- 0.0396 --> 0.0624

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.746 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 108.448 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.523 deg; O1  -- O3  = 3 A
O2  -- T1  -- O2  = 111.225 deg; O2  -- O2  = 3 A
O2  -- T1  -- O3  = 117.472 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 104.089 deg; O2  -- O3  = 3 A
       104.089 deg <-- 109.417 deg --> 117.472 deg

O3  -- T2  -- O4  = 103.062 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  = 118.331 deg; O3  -- O4  = 3 A
O3  -- T2  -- O3  = 110.096 deg; O3  -- O3  = 3 A
O4  -- T2  -- O4  = 100.832 deg; O4  -- O4  = 2 A
O4  -- T2  -- O3  = 103.062 deg; O4  -- O3  = 2 A
O4  -- T2  -- O3  = 118.331 deg; O4  -- O3  = 3 A
       100.832 deg <-- 108.953 deg --> 118.331 deg

        O-T-O SUMMARY
          Range  = 100.8318 deg <--> 118.3314 deg
          Mean   = 109.5480 deg
          StdDev = 5.7691 deg

        O--O SUMMARY
          Range  = 2.4473 A <--> 2.8080 A
          Mean   = 2.6407 A
          StdDev = 0.1221 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.2854 A
T1  - O1  - T1  - O2  - T1  = 120.827 deg; T1  -- T1  = 4.8946 A
T1  - O1  - T1  - O3  - T2  = 136.284 deg; T1  -- T2  = 5.5583 A
T1  - O2  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.2854 A
T1  - O2  - T1  - O3  - T2  = 115.114 deg; T1  -- T2  = 5.4051 A
T1  - O2  - T1  - O3  - T2  =  95.621 deg; T1  -- T2  = 4.4425 A

T2  - O3  - T2  - O4  - T1  = 123.174 deg; T2  -- T1  = 5.5804 A
T2  - O3  - T2  - O4  - T1  = 123.174 deg; T2  -- T1  = 5.5804 A
T2  - O3  - T2  - O3  - T2  = 100.989 deg; T2  -- T2  = 4.8946 A
T1  - O4  - T2  - O4  - T1  = 112.432 deg; T1  -- T1  = 5.2741 A
T1  - O4  - T2  - O3  - T2  =  89.588 deg; T1  -- T2  = 4.4702 A
T1  - O4  - T2  - O3  - T2  =  89.588 deg; T1  -- T2  = 4.4702 A

        T-T-T SUMMARY
          Range  = 89.5880 deg <--> 136.2844 deg
          Mean   = 107.0067 deg
          StdDev = 16.2024 deg

        T--T SUMMARY
          Range  = 4.2854 A <--> 5.5804 A
          Mean   = 4.9134 A
          StdDev = 0.5136 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 178.070 deg ; T1  -- T1   3.2318 A

T1  -- O2  -- T1  = 118.505 deg ; T1  -- T1   2.8142 A

T1  -- O3  -- T2  = 155.277 deg ; T1  -- T2   3.1728 A

T2  -- O4  -- T2  = 176.141 deg ; T2  -- T2   3.1719 A


        T-O-T SUMMARY
          Range  = 118.5054° <--> 178.0699 deg
          Mean   = 154.2638 deg
          StdDev = 24.6325 deg

        T--T SUMMARY
          Range  = 2.8142 A <--> 3.2318 A
          Mean   = 3.0871 A
          StdDev = 0.1759 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 22 41 63 85 114 155 199 240 283 340 409 472 533 605
TD10 = 934
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 25 38 59 90 122 154 188 238 297 348 399 460 540 618
TD10 = 931
Circuit symbol = 6.6.6.6.6.6_{2}
Weight = 24
Vertex symbol  = 6.6.6.6.6.6_{2}
Weight = 24

<TD10> = 933.000
Average ring size = 5.4286