Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_652904_gDKg9I.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 22.87 T-atoms per nm^3
Material density = 2.282 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6344 Angstrom
T1  -- O2  = 1.6100 Angstrom
T1  -- O4  = 1.5983 Angstrom
T1  -- O3  = 1.6340 Angstrom
      mean = 1.6192 Angstrom
        t1 = 0.059346  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.063360  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6715 Angstrom
T2  -- O5  = 1.6061 Angstrom
T2  -- O4  = 1.6819 Angstrom
T2  -- O2  = 1.6046 Angstrom
      mean = 1.6410 Angstrom
        t1 = 0.038228  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.048201  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5983 A <--> 1.6819 A
          Mean   = 1.6301 A
          StdDev = 0.0307 A

       t1 Range  = 0.0382 <-- 0.0488 --> 0.0593
       t2 Range  = 0.0482 <-- 0.0558 --> 0.0634

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.190 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  =  96.931 deg; O1  -- O4  = 2 A
O1  -- T1  -- O3  = 125.947 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 112.918 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 107.675 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 100.999 deg; O4  -- O3  = 2 A
       96.931 deg <-- 109.277 deg --> 125.947 deg

O3  -- T2  -- O5  = 108.951 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 117.201 deg; O3  -- O4  = 3 A
O3  -- T2  -- O2  = 107.845 deg; O3  -- O2  = 3 A
O5  -- T2  -- O4  = 107.876 deg; O5  -- O4  = 3 A
O5  -- T2  -- O2  = 106.706 deg; O5  -- O2  = 3 A
O4  -- T2  -- O2  = 107.794 deg; O4  -- O2  = 3 A
       106.706 deg <-- 109.396 deg --> 117.201 deg

        O-T-O SUMMARY
          Range  = 96.9313 deg <--> 125.9467 deg
          Mean   = 109.3362 deg
          StdDev = 7.1869 deg

        O--O SUMMARY
          Range  = 2.4200 A <--> 2.9115 A
          Mean   = 2.6553 A
          StdDev = 0.1314 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  99.806 deg; T2  -- T1  = 4.7681 A
T2  - O1  - T1  - O4  - T2  =  92.448 deg; T2  -- T2  = 4.4093 A
T2  - O1  - T1  - O3  - T2  =  85.702 deg; T2  -- T2  = 3.8863 A
T1  - O2  - T1  - O4  - T2  =  99.550 deg; T1  -- T2  = 4.8976 A
T1  - O2  - T1  - O3  - T2  = 151.322 deg; T1  -- T2  = 5.8335 A
T2  - O4  - T1  - O3  - T2  = 108.365 deg; T2  -- T2  = 4.7864 A

T2  - O3  - T2  - O5  - T1  = 118.715 deg; T2  -- T1  = 5.3111 A
T2  - O3  - T2  - O4  - T1  = 125.910 deg; T2  -- T1  = 5.3152 A
T2  - O3  - T2  - O2  - T1  = 114.191 deg; T2  -- T1  = 5.3375 A
T1  - O5  - T2  - O4  - T1  =  94.298 deg; T1  -- T1  = 4.1885 A
T1  - O5  - T2  - O2  - T1  =  87.552 deg; T1  -- T1  = 4.2251 A
T1  - O4  - T2  - O2  - T1  = 108.365 deg; T1  -- T1  = 4.7864 A

        T-T-T SUMMARY
          Range  = 85.7022 deg <--> 151.3224 deg
          Mean   = 107.1854 deg
          StdDev = 18.2412 deg

        T--T SUMMARY
          Range  = 3.8863 A <--> 5.8335 A
          Mean   = 4.8121 A
          StdDev = 0.5583 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2687 A

T1  -- O2  -- T2  = 156.109 deg ; T1  -- T2   3.1450 A

T1  -- O3  -- T2  = 112.645 deg ; T1  -- T2   2.7509 A

T1  -- O4  -- T2  = 128.854 deg ; T1  -- T2   2.9590 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2122 A


        T-O-T SUMMARY
          Range  = 112.6449° <--> 180.0000 deg
          Mean   = 151.5215 deg
          StdDev = 28.5513 deg

        T--T SUMMARY
          Range  = 2.7509 A <--> 3.2687 A
          Mean   = 3.0672 A
          StdDev = 0.1997 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7509 Angstrom
T2  -- T1  = 2.7509 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 254 298 340 376 415 450
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 254 298 340 376 415 449
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000