Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_651925_8sN7od.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 24.00 T-atoms per nm^3
Material density = 2.395 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6153 Angstrom
T1  -- O2  = 1.6142 Angstrom
T1  -- O3  = 1.6456 Angstrom
T1  -- O4  = 1.6359 Angstrom
      mean = 1.6277 Angstrom
        t1 = 0.021390  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013316  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6235 Angstrom
T2  -- O3  = 1.6437 Angstrom
T2  -- O2  = 1.6151 Angstrom
T2  -- O4  = 1.6302 Angstrom
      mean = 1.6281 Angstrom
        t1 = 0.029208  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027325  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6142 A <--> 1.6456 A
          Mean   = 1.6279 A
          StdDev = 0.0125 A

       t1 Range  = 0.0214 <-- 0.0253 --> 0.0292
       t2 Range  = 0.0133 <-- 0.0203 --> 0.0273

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.066 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.492 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 114.999 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.811 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.269 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.098 deg; O3  -- O4  = 3 A
       106.066 deg <-- 109.456 deg --> 114.999 deg

O5  -- T2  -- O3  = 118.117 deg; O5  -- O3  = 3 A
O5  -- T2  -- O2  = 104.858 deg; O5  -- O2  = 3 A
O5  -- T2  -- O4  = 108.348 deg; O5  -- O4  = 3 A
O3  -- T2  -- O2  = 107.100 deg; O3  -- O2  = 3 A
O3  -- T2  -- O4  = 108.678 deg; O3  -- O4  = 3 A
O2  -- T2  -- O4  = 109.479 deg; O2  -- O4  = 3 A
       104.858 deg <-- 109.430 deg --> 118.117 deg

        O-T-O SUMMARY
          Range  = 104.8584 deg <--> 118.1174 deg
          Mean   = 109.4431 deg
          StdDev = 3.6105 deg

        O--O SUMMARY
          Range  = 2.5669 A <--> 2.8023 A
          Mean   = 2.6568 A
          StdDev = 0.0627 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 109.847 deg; T1  -- T2  = 5.2793 A
T1  - O1  - T1  - O3  - T2  =  92.802 deg; T1  -- T2  = 4.3727 A
T1  - O1  - T1  - O4  - T2  = 144.361 deg; T1  -- T2  = 5.7848 A
T2  - O2  - T1  - O3  - T2  =  89.711 deg; T2  -- T2  = 4.2521 A
T2  - O2  - T1  - O4  - T2  =  89.984 deg; T2  -- T2  = 4.2960 A
T2  - O3  - T1  - O4  - T2  = 117.364 deg; T2  -- T2  = 4.8162 A

T2  - O5  - T2  - O3  - T1  = 149.799 deg; T2  -- T1  = 5.8326 A
T2  - O5  - T2  - O2  - T1  = 104.977 deg; T2  -- T1  = 5.1300 A
T2  - O5  - T2  - O4  - T1  =  89.026 deg; T2  -- T1  = 4.2801 A
T1  - O3  - T2  - O2  - T1  =  90.289 deg; T1  -- T1  = 4.2734 A
T1  - O3  - T2  - O4  - T1  = 117.364 deg; T1  -- T1  = 4.8162 A
T1  - O2  - T2  - O4  - T1  =  90.016 deg; T1  -- T1  = 4.2972 A

        T-T-T SUMMARY
          Range  = 89.0262 deg <--> 149.7989 deg
          Mean   = 107.1284 deg
          StdDev = 21.1316 deg

        T--T SUMMARY
          Range  = 4.2521 A <--> 5.8326 A
          Mean   = 4.7859 A
          StdDev = 0.5831 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2306 A

T1  -- O2  -- T2  = 171.448 deg ; T1  -- T2   3.2202 A

T1  -- O3  -- T2  = 116.233 deg ; T1  -- T2   2.7931 A

T1  -- O4  -- T2  = 121.127 deg ; T1  -- T2   2.8444 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2469 A


        T-O-T SUMMARY
          Range  = 116.2327° <--> 180.0000 deg
          Mean   = 153.7615 deg
          StdDev = 30.4163 deg

        T--T SUMMARY
          Range  = 2.7931 A <--> 3.2469 A
          Mean   = 3.0671 A
          StdDev = 0.2146 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7931 Angstrom
T2  -- T1  = 2.7931 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 538
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 476 537
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000