Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_651498_WzMQQH.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 21.03 T-atoms per nm^3
Material density = 2.098 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6176 Angstrom
T1  -- O2  = 1.6250 Angstrom
T1  -- O3  = 1.6200 Angstrom
T1  -- O4  = 1.6220 Angstrom
      mean = 1.6211 Angstrom
        t1 = 0.017864  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014054  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6133 Angstrom
T2  -- O2  = 1.6334 Angstrom
T2  -- O3  = 1.6196 Angstrom
T2  -- O4  = 1.6231 Angstrom
      mean = 1.6223 Angstrom
        t1 = 0.008110  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001761  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6133 A <--> 1.6334 A
          Mean   = 1.6217 A
          StdDev = 0.0057 A

       t1 Range  = 0.0081 <-- 0.0130 --> 0.0179
       t2 Range  = 0.0018 <-- 0.0079 --> 0.0141

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 114.469 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.246 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.941 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 107.482 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.243 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 107.123 deg; O3  -- O4  = 3 A
       107.123 deg <-- 109.417 deg --> 114.469 deg

O5  -- T2  -- O2  = 109.526 deg; O5  -- O2  = 3 A
O5  -- T2  -- O3  = 110.110 deg; O5  -- O3  = 3 A
O5  -- T2  -- O4  = 110.369 deg; O5  -- O4  = 3 A
O2  -- T2  -- O3  = 109.242 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 108.948 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 108.618 deg; O3  -- O4  = 3 A
       108.618 deg <-- 109.469 deg --> 110.369 deg

        O-T-O SUMMARY
          Range  = 107.1227 deg <--> 114.4686 deg
          Mean   = 109.4431 deg
          StdDev = 1.9798 deg

        O--O SUMMARY
          Range  = 2.6066 A <--> 2.7266 A
          Mean   = 2.6474 A
          StdDev = 0.0322 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  93.480 deg; T2  -- T1  = 4.5726 A
T2  - O1  - T1  - O3  - T2  = 107.635 deg; T2  -- T2  = 4.9108 A
T2  - O1  - T1  - O4  - T2  =  80.770 deg; T2  -- T2  = 3.8245 A
T1  - O2  - T1  - O3  - T2  = 122.057 deg; T1  -- T2  = 5.4933 A
T1  - O2  - T1  - O4  - T2  = 136.005 deg; T1  -- T2  = 5.6509 A
T2  - O3  - T1  - O4  - T2  = 100.966 deg; T2  -- T2  = 4.5535 A

T2  - O5  - T2  - O2  - T1  = 118.606 deg; T2  -- T1  = 5.3902 A
T2  - O5  - T2  - O3  - T1  = 105.342 deg; T2  -- T1  = 4.9866 A
T2  - O5  - T2  - O4  - T1  = 137.230 deg; T2  -- T1  = 5.6668 A
T1  - O2  - T2  - O3  - T1  = 107.635 deg; T1  -- T1  = 4.9108 A
T1  - O2  - T2  - O4  - T1  =  99.230 deg; T1  -- T1  = 4.4947 A
T1  - O3  - T2  - O4  - T1  =  79.034 deg; T1  -- T1  = 3.7573 A

        T-T-T SUMMARY
          Range  = 79.0343 deg <--> 137.2298 deg
          Mean   = 107.3324 deg
          StdDev = 18.3409 deg

        T--T SUMMARY
          Range  = 3.7573 A <--> 5.6668 A
          Mean   = 4.8510 A
          StdDev = 0.6309 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2351 A

T1  -- O2  -- T2  = 122.564 deg ; T1  -- T2   2.8576 A

T1  -- O3  -- T2  = 139.688 deg ; T1  -- T2   3.0411 A

T1  -- O4  -- T2  = 139.352 deg ; T1  -- T2   3.0430 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2265 A


        T-O-T SUMMARY
          Range  = 122.5636° <--> 180.0000 deg
          Mean   = 152.3207 deg
          StdDev = 24.7006 deg

        T--T SUMMARY
          Range  = 2.8576 A <--> 3.2351 A
          Mean   = 3.0807 A
          StdDev = 0.1475 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 535
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 476 533
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000