Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_651493_z3tH8i.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 20.67 T-atoms per nm^3
Material density = 2.062 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6158 Angstrom
T1  -- O4  = 1.6174 Angstrom
T1  -- O3  = 1.6289 Angstrom
T1  -- O2  = 1.6172 Angstrom
      mean = 1.6198 Angstrom
        t1 = 0.008577  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006788  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6153 Angstrom
T2  -- O5  = 1.6266 Angstrom
T2  -- O3  = 1.6246 Angstrom
T2  -- O4  = 1.6183 Angstrom
      mean = 1.6212 Angstrom
        t1 = 0.015105  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012783  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6153 A <--> 1.6289 A
          Mean   = 1.6205 A
          StdDev = 0.0052 A

       t1 Range  = 0.0086 <-- 0.0118 --> 0.0151
       t2 Range  = 0.0068 <-- 0.0098 --> 0.0128

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O4  = 109.028 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 110.651 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.749 deg; O1  -- O2  = 3 A
O4  -- T1  -- O3  = 108.254 deg; O4  -- O3  = 3 A
O4  -- T1  -- O2  = 108.775 deg; O4  -- O2  = 3 A
O3  -- T1  -- O2  = 110.338 deg; O3  -- O2  = 3 A
       108.254 deg <-- 109.466 deg --> 110.651 deg

O2  -- T2  -- O5  = 107.445 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 107.153 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 112.067 deg; O2  -- O4  = 3 A
O5  -- T2  -- O3  = 112.586 deg; O5  -- O3  = 3 A
O5  -- T2  -- O4  = 108.351 deg; O5  -- O4  = 3 A
O3  -- T2  -- O4  = 109.280 deg; O3  -- O4  = 3 A
       107.153 deg <-- 109.480 deg --> 112.586 deg

        O-T-O SUMMARY
          Range  = 107.1532 deg <--> 112.5858 deg
          Mean   = 109.4729 deg
          StdDev = 1.6574 deg

        O--O SUMMARY
          Range  = 2.6070 A <--> 2.7046 A
          Mean   = 2.6461 A
          StdDev = 0.0281 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O4  - T2  = 110.738 deg; T1  -- T2  = 5.0138 A
T1  - O1  - T1  - O3  - T2  = 125.576 deg; T1  -- T2  = 5.6120 A
T1  - O1  - T1  - O2  - T2  = 127.246 deg; T1  -- T2  = 5.6088 A
T2  - O4  - T1  - O3  - T2  =  82.913 deg; T2  -- T2  = 3.9325 A
T2  - O4  - T1  - O2  - T2  = 111.054 deg; T2  -- T2  = 4.8519 A
T2  - O3  - T1  - O2  - T2  =  90.229 deg; T2  -- T2  = 4.3266 A

T1  - O2  - T2  - O5  - T2  =  91.366 deg; T1  -- T2  = 4.4970 A
T1  - O2  - T2  - O3  - T1  = 111.054 deg; T1  -- T1  = 4.8519 A
T1  - O2  - T2  - O4  - T1  =  89.771 deg; T1  -- T1  = 4.3094 A
T2  - O5  - T2  - O3  - T1  = 141.096 deg; T2  -- T1  = 5.7623 A
T2  - O5  - T2  - O4  - T1  = 115.001 deg; T2  -- T1  = 5.3409 A
T1  - O3  - T2  - O4  - T1  =  97.087 deg; T1  -- T1  = 4.4501 A

        T-T-T SUMMARY
          Range  = 82.9133 deg <--> 141.0964 deg
          Mean   = 107.7611 deg
          StdDev = 17.5014 deg

        T--T SUMMARY
          Range  = 3.9325 A <--> 5.7623 A
          Mean   = 4.8798 A
          StdDev = 0.5852 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2317 A

T1  -- O2  -- T2  = 139.024 deg ; T1  -- T2   3.0281 A

T1  -- O3  -- T2  = 122.775 deg ; T1  -- T2   2.8562 A

T1  -- O4  -- T2  = 144.114 deg ; T1  -- T2   3.0783 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2533 A


        T-O-T SUMMARY
          Range  = 122.7748° <--> 180.0000 deg
          Mean   = 153.1825 deg
          StdDev = 24.2473 deg

        T--T SUMMARY
          Range  = 2.8562 A <--> 3.2533 A
          Mean   = 3.0895 A
          StdDev = 0.1530 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 159 192 186 226 215 257 246
TD10 = 778
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 159 192 186 226 215 257 246
TD10 = 778
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 778.000
Average ring size = 5.6000