Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_651480_2Gbgqr.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 23.56 T-atoms per nm^3
Material density = 2.351 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6168 Angstrom
T1  -- O2  = 1.6218 Angstrom
T1  -- O4  = 1.6099 Angstrom
T1  -- O3  = 1.6157 Angstrom
      mean = 1.6160 Angstrom
        t1 = 0.013583  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009240  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6276 Angstrom
T2  -- O5  = 1.6112 Angstrom
T2  -- O2  = 1.6240 Angstrom
T2  -- O4  = 1.6334 Angstrom
      mean = 1.6241 Angstrom
        t1 = 0.013751  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007926  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6099 A <--> 1.6334 A
          Mean   = 1.6201 A
          StdDev = 0.0079 A

       t1 Range  = 0.0136 <-- 0.0137 --> 0.0138
       t2 Range  = 0.0079 <-- 0.0086 --> 0.0092

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.274 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 110.783 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.473 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 107.977 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 112.127 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 106.131 deg; O4  -- O3  = 3 A
       106.131 deg <-- 109.461 deg --> 112.127 deg

O3  -- T2  -- O5  = 108.316 deg; O3  -- O5  = 3 A
O3  -- T2  -- O2  = 110.374 deg; O3  -- O2  = 3 A
O3  -- T2  -- O4  = 109.037 deg; O3  -- O4  = 3 A
O5  -- T2  -- O2  = 107.281 deg; O5  -- O2  = 3 A
O5  -- T2  -- O4  = 111.874 deg; O5  -- O4  = 3 A
O2  -- T2  -- O4  = 109.939 deg; O2  -- O4  = 3 A
       107.281 deg <-- 109.470 deg --> 111.874 deg

        O-T-O SUMMARY
          Range  = 106.1306 deg <--> 112.1269 deg
          Mean   = 109.4654 deg
          StdDev = 1.7677 deg

        O--O SUMMARY
          Range  = 2.5783 A <--> 2.6879 A
          Mean   = 2.6452 A
          StdDev = 0.0328 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  97.601 deg; T2  -- T1  = 4.8073 A
T2  - O1  - T1  - O4  - T2  =  89.656 deg; T2  -- T2  = 4.2880 A
T2  - O1  - T1  - O3  - T2  =  87.879 deg; T2  -- T2  = 4.2447 A
T1  - O2  - T1  - O4  - T2  = 109.280 deg; T1  -- T2  = 5.0239 A
T1  - O2  - T1  - O3  - T2  = 120.507 deg; T1  -- T2  = 5.3780 A
T2  - O4  - T1  - O3  - T2  = 130.039 deg; T2  -- T2  = 5.3313 A

T1  - O3  - T2  - O5  - T1  =  92.121 deg; T1  -- T1  = 4.4045 A
T1  - O3  - T2  - O2  - T2  =  98.581 deg; T1  -- T2  = 4.8345 A
T1  - O3  - T2  - O4  - T1  =  90.344 deg; T1  -- T1  = 4.3137 A
T1  - O5  - T2  - O2  - T2  = 108.203 deg; T1  -- T2  = 5.0094 A
T1  - O5  - T2  - O4  - T1  = 130.039 deg; T1  -- T1  = 5.3313 A
T2  - O2  - T2  - O4  - T1  = 120.696 deg; T2  -- T1  = 5.3425 A

        T-T-T SUMMARY
          Range  = 87.8794 deg <--> 130.0392 deg
          Mean   = 106.2455 deg
          StdDev = 15.4804 deg

        T--T SUMMARY
          Range  = 4.2447 A <--> 5.3780 A
          Mean   = 4.8591 A
          StdDev = 0.4383 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2336 A

T1  -- O2  -- T2  = 131.438 deg ; T1  -- T2   2.9587 A

T1  -- O3  -- T2  = 128.619 deg ; T1  -- T2   2.9228 A

T1  -- O4  -- T2  = 153.216 deg ; T1  -- T2   3.1551 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2224 A


        T-O-T SUMMARY
          Range  = 128.6194° <--> 180.0000 deg
          Mean   = 154.6547 deg
          StdDev = 23.5876 deg

        T--T SUMMARY
          Range  = 2.9228 A <--> 3.2336 A
          Mean   = 3.0985 A
          StdDev = 0.1392 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 209 251 277 331 337 394 373
TD10 = 828
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 209 251 277 331 336 393 372
TD10 = 828
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 828.000
Average ring size = 5.6000