Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_651448__QlE6R.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 21.60 T-atoms per nm^3
Material density = 2.155 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6166 Angstrom
T1  -- O2  = 1.6333 Angstrom
T1  -- O4  = 1.6270 Angstrom
T1  -- O3  = 1.6257 Angstrom
      mean = 1.6257 Angstrom
        t1 = 0.010002  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001746  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6245 Angstrom
T2  -- O5  = 1.6158 Angstrom
T2  -- O2  = 1.6239 Angstrom
T2  -- O4  = 1.6185 Angstrom
      mean = 1.6207 Angstrom
        t1 = 0.017675  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013917  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6158 A <--> 1.6333 A
          Mean   = 1.6232 A
          StdDev = 0.0057 A

       t1 Range  = 0.0100 <-- 0.0138 --> 0.0177
       t2 Range  = 0.0017 <-- 0.0078 --> 0.0139

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.912 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.631 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 110.130 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.231 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.275 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 108.637 deg; O4  -- O3  = 3 A
       108.637 deg <-- 109.469 deg --> 110.130 deg

O3  -- T2  -- O5  = 109.665 deg; O3  -- O5  = 3 A
O3  -- T2  -- O2  = 111.391 deg; O3  -- O2  = 3 A
O3  -- T2  -- O4  = 107.035 deg; O3  -- O4  = 3 A
O5  -- T2  -- O2  = 114.031 deg; O5  -- O2  = 3 A
O5  -- T2  -- O4  = 106.663 deg; O5  -- O4  = 3 A
O2  -- T2  -- O4  = 107.691 deg; O2  -- O4  = 3 A
       106.663 deg <-- 109.412 deg --> 114.031 deg

        O-T-O SUMMARY
          Range  = 106.6627 deg <--> 114.0305 deg
          Mean   = 109.4409 deg
          StdDev = 1.9322 deg

        O--O SUMMARY
          Range  = 2.5943 A <--> 2.7175 A
          Mean   = 2.6498 A
          StdDev = 0.0323 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 138.713 deg; T1  -- T2  = 5.6882 A
T1  - O1  - T1  - O4  - T2  = 107.715 deg; T1  -- T2  = 5.0440 A
T1  - O1  - T1  - O3  - T2  = 117.028 deg; T1  -- T2  = 5.3335 A
T2  - O2  - T1  - O4  - T2  =  78.046 deg; T2  -- T2  = 3.6882 A
T2  - O2  - T1  - O3  - T2  =  98.791 deg; T2  -- T2  = 4.4528 A
T2  - O4  - T1  - O3  - T2  = 107.225 deg; T2  -- T2  = 4.8545 A

T1  - O3  - T2  - O5  - T2  = 132.669 deg; T1  -- T2  = 5.5663 A
T1  - O3  - T2  - O2  - T1  = 101.954 deg; T1  -- T1  = 4.5491 A
T1  - O3  - T2  - O4  - T1  =  81.209 deg; T1  -- T1  = 3.8182 A
T2  - O5  - T2  - O2  - T1  = 124.965 deg; T2  -- T1  = 5.5370 A
T2  - O5  - T2  - O4  - T1  =  89.748 deg; T2  -- T1  = 4.4131 A
T1  - O2  - T2  - O4  - T1  = 107.225 deg; T1  -- T1  = 4.8545 A

        T-T-T SUMMARY
          Range  = 78.0461 deg <--> 138.7133 deg
          Mean   = 107.1075 deg
          StdDev = 18.6090 deg

        T--T SUMMARY
          Range  = 3.6882 A <--> 5.6882 A
          Mean   = 4.8166 A
          StdDev = 0.6460 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2333 A

T1  -- O2  -- T2  = 121.607 deg ; T1  -- T2   2.8434 A

T1  -- O3  -- T2  = 135.718 deg ; T1  -- T2   3.0106 A

T1  -- O4  -- T2  = 137.000 deg ; T1  -- T2   3.0196 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2316 A


        T-O-T SUMMARY
          Range  = 121.6067° <--> 180.0000 deg
          Mean   = 150.8650 deg
          StdDev = 25.7139 deg

        T--T SUMMARY
          Range  = 2.8434 A <--> 3.2333 A
          Mean   = 3.0677 A
          StdDev = 0.1565 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 476 525
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 476 531
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000