Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_651006__Dd9sD.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 21.09 T-atoms per nm^3
Material density = 2.104 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6395 Angstrom
T1  -- O3  = 1.6127 Angstrom
T1  -- O4  = 1.6087 Angstrom
T1  -- O2  = 1.6388 Angstrom
      mean = 1.6249 Angstrom
        t1 = 0.037769  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025642  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6087 Angstrom
T2  -- O4  = 1.6112 Angstrom
T2  -- O5  = 1.5736 Angstrom
T2  -- O3  = 1.5830 Angstrom
      mean = 1.5941 Angstrom
        t1 = 0.038068  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.033093  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5736 A <--> 1.6395 A
          Mean   = 1.6095 A
          StdDev = 0.0224 A

       t1 Range  = 0.0378 <-- 0.0379 --> 0.0381
       t2 Range  = 0.0256 <-- 0.0294 --> 0.0331

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 117.125 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 106.571 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 114.357 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 104.074 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 102.312 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 112.061 deg; O4  -- O2  = 3 A
       102.312 deg <-- 109.417 deg --> 117.125 deg

O2  -- T2  -- O4  = 111.587 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 115.775 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 106.283 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 112.150 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 110.701 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  =  99.458 deg; O5  -- O3  = 2 A
       99.458 deg <-- 109.326 deg --> 115.775 deg

        O-T-O SUMMARY
          Range  = 99.4576 deg <--> 117.1248 deg
          Mean   = 109.3710 deg
          StdDev = 5.4468 deg

        O--O SUMMARY
          Range  = 2.4085 A <--> 2.7749 A
          Mean   = 2.6242 A
          StdDev = 0.1017 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T2  = 110.631 deg; T1  -- T2  = 5.3341 A
T1  - O1  - T1  - O4  - T2  = 105.815 deg; T1  -- T2  = 4.9499 A
T1  - O1  - T1  - O2  - T2  = 138.287 deg; T1  -- T2  = 5.8309 A
T2  - O3  - T1  - O4  - T2  =  89.370 deg; T2  -- T2  = 4.3141 A
T2  - O3  - T1  - O2  - T2  =  88.055 deg; T2  -- T2  = 4.2898 A
T2  - O4  - T1  - O2  - T2  = 111.529 deg; T2  -- T2  = 4.8612 A

T2  - O2  - T2  - O4  - T1  = 117.101 deg; T2  -- T1  = 5.4214 A
T2  - O2  - T2  - O5  - T1  =  94.045 deg; T2  -- T1  = 4.4696 A
T2  - O2  - T2  - O3  - T1  = 141.936 deg; T2  -- T1  = 5.7365 A
T1  - O4  - T2  - O5  - T1  =  91.945 deg; T1  -- T1  = 4.4375 A
T1  - O4  - T2  - O3  - T1  =  90.630 deg; T1  -- T1  = 4.3616 A
T1  - O5  - T2  - O3  - T1  = 111.529 deg; T1  -- T1  = 4.8612 A

        T-T-T SUMMARY
          Range  = 88.0547 deg <--> 141.9355 deg
          Mean   = 107.5727 deg
          StdDev = 17.9014 deg

        T--T SUMMARY
          Range  = 4.2898 A <--> 5.8309 A
          Mean   = 4.9056 A
          StdDev = 0.5466 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2790 A

T1  -- O2  -- T2  = 128.123 deg ; T1  -- T2   2.9205 A

T1  -- O3  -- T2  = 135.666 deg ; T1  -- T2   2.9595 A

T1  -- O4  -- T2  = 169.956 deg ; T1  -- T2   3.2076 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.1472 A


        T-O-T SUMMARY
          Range  = 128.1234° <--> 180.0000 deg
          Mean   = 158.7490 deg
          StdDev = 23.5681 deg

        T--T SUMMARY
          Range  = 2.9205 A <--> 3.2790 A
          Mean   = 3.1028 A
          StdDev = 0.1474 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 304 347 378 411 436
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 302 346 382 409 434
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000