Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_650928_Qu0znh.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 21.93 T-atoms per nm^3
Material density = 2.188 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6148 Angstrom
T1  -- O2  = 1.6382 Angstrom
T1  -- O3  = 1.6236 Angstrom
T1  -- O4  = 1.6229 Angstrom
      mean = 1.6249 Angstrom
        t1 = 0.010005  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002532  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6306 Angstrom
T2  -- O3  = 1.6225 Angstrom
T2  -- O4  = 1.6217 Angstrom
T2  -- O5  = 1.6137 Angstrom
      mean = 1.6221 Angstrom
        t1 = 0.013382  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007210  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6137 A <--> 1.6382 A
          Mean   = 1.6235 A
          StdDev = 0.0077 A

       t1 Range  = 0.0100 <-- 0.0117 --> 0.0134
       t2 Range  = 0.0025 <-- 0.0049 --> 0.0072

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.195 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.831 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.101 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.130 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.385 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.180 deg; O3  -- O4  = 3 A
       109.101 deg <-- 109.470 deg --> 110.195 deg

O2  -- T2  -- O3  = 110.648 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 108.642 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 112.330 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 108.223 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.589 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 107.262 deg; O4  -- O5  = 3 A
       107.262 deg <-- 109.449 deg --> 112.330 deg

        O-T-O SUMMARY
          Range  = 107.2625 deg <--> 112.3301 deg
          Mean   = 109.4598 deg
          StdDev = 1.2404 deg

        O--O SUMMARY
          Range  = 2.6052 A <--> 2.6949 A
          Mean   = 2.6509 A
          StdDev = 0.0227 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 140.674 deg; T2  -- T1  = 5.6825 A
T2  - O1  - T1  - O3  - T2  =  77.305 deg; T2  -- T2  = 3.6329 A
T2  - O1  - T1  - O4  - T2  =  99.049 deg; T2  -- T2  = 4.4278 A
T1  - O2  - T1  - O3  - T2  = 107.116 deg; T1  -- T2  = 5.0196 A
T1  - O2  - T1  - O4  - T2  = 115.473 deg; T1  -- T2  = 5.2820 A
T2  - O3  - T1  - O4  - T2  = 108.013 deg; T2  -- T2  = 4.8733 A

T1  - O2  - T2  - O3  - T2  = 132.475 deg; T1  -- T2  = 5.5216 A
T1  - O2  - T2  - O4  - T1  = 102.695 deg; T1  -- T1  = 4.5396 A
T1  - O2  - T2  - O5  - T1  =  80.951 deg; T1  -- T1  = 3.7801 A
T2  - O3  - T2  - O4  - T1  = 124.329 deg; T2  -- T1  = 5.5148 A
T2  - O3  - T2  - O5  - T1  =  89.955 deg; T2  -- T1  = 4.4151 A
T1  - O4  - T2  - O5  - T1  = 108.013 deg; T1  -- T1  = 4.8733 A

        T-T-T SUMMARY
          Range  = 77.3055 deg <--> 140.6736 deg
          Mean   = 107.1706 deg
          StdDev = 18.8571 deg

        T--T SUMMARY
          Range  = 3.6329 A <--> 5.6825 A
          Mean   = 4.7969 A
          StdDev = 0.6500 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2297 A

T1  -- O2  -- T2  = 118.053 deg ; T1  -- T2   2.8027 A

T1  -- O3  -- T2  = 135.834 deg ; T1  -- T2   3.0079 A

T1  -- O4  -- T2  = 136.659 deg ; T1  -- T2   3.0152 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2274 A


        T-O-T SUMMARY
          Range  = 118.0531° <--> 180.0000 deg
          Mean   = 150.1091 deg
          StdDev = 26.6634 deg

        T--T SUMMARY
          Range  = 2.8027 A <--> 3.2297 A
          Mean   = 3.0566 A
          StdDev = 0.1684 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000