Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_650721_MkmcEb.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 21.63 T-atoms per nm^3
Material density = 2.158 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6162 Angstrom
T1  -- O2  = 1.6249 Angstrom
T1  -- O3  = 1.6227 Angstrom
T1  -- O4  = 1.6231 Angstrom
      mean = 1.6217 Angstrom
        t1 = 0.012227  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006377  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6348 Angstrom
T2  -- O3  = 1.6249 Angstrom
T2  -- O4  = 1.6219 Angstrom
T2  -- O5  = 1.6158 Angstrom
      mean = 1.6243 Angstrom
        t1 = 0.009239  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002101  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6158 A <--> 1.6348 A
          Mean   = 1.6230 A
          StdDev = 0.0057 A

       t1 Range  = 0.0092 <-- 0.0107 --> 0.0122
       t2 Range  = 0.0021 <-- 0.0042 --> 0.0064

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 112.525 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.367 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.665 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.374 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.527 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.252 deg; O3  -- O4  = 3 A
       107.665 deg <-- 109.452 deg --> 112.525 deg

O2  -- T2  -- O3  = 109.293 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.431 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.781 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 108.986 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.735 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 109.597 deg; O4  -- O5  = 3 A
       108.986 deg <-- 109.471 deg --> 109.781 deg

        O-T-O SUMMARY
          Range  = 107.6651 deg <--> 112.5252 deg
          Mean   = 109.4613 deg
          StdDev = 1.1884 deg

        O--O SUMMARY
          Range  = 2.6150 A <--> 2.6952 A
          Mean   = 2.6501 A
          StdDev = 0.0197 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 101.477 deg; T2  -- T2  = 4.5300 A
T2  - O1  - T1  - O3  - T2  =  79.154 deg; T2  -- T2  = 3.7258 A
T2  - O1  - T1  - O4  - T1  = 136.473 deg; T2  -- T1  = 5.6343 A
T2  - O2  - T1  - O3  - T2  = 108.585 deg; T2  -- T2  = 4.8949 A
T2  - O2  - T1  - O4  - T1  = 120.930 deg; T2  -- T1  = 5.4379 A
T2  - O3  - T1  - O4  - T1  =  94.965 deg; T2  -- T1  = 4.6047 A

T1  - O2  - T2  - O3  - T1  = 100.846 deg; T1  -- T1  = 4.5057 A
T1  - O2  - T2  - O4  - T2  = 136.630 deg; T1  -- T2  = 5.6366 A
T1  - O2  - T2  - O5  - T1  =  78.523 deg; T1  -- T1  = 3.7042 A
T1  - O3  - T2  - O4  - T2  = 119.693 deg; T1  -- T2  = 5.3995 A
T1  - O3  - T2  - O5  - T1  = 108.585 deg; T1  -- T1  = 4.8949 A
T2  - O4  - T2  - O5  - T1  = 100.642 deg; T2  -- T1  = 4.8107 A

        T-T-T SUMMARY
          Range  = 78.5233 deg <--> 136.6295 deg
          Mean   = 107.2086 deg
          StdDev = 18.5242 deg

        T--T SUMMARY
          Range  = 3.7042 A <--> 5.6366 A
          Mean   = 4.8149 A
          StdDev = 0.6413 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2323 A

T1  -- O2  -- T2  = 120.658 deg ; T1  -- T2   2.8323 A

T1  -- O3  -- T2  = 136.511 deg ; T1  -- T2   3.0165 A

T1  -- O4  -- T2  = 136.276 deg ; T1  -- T2   3.0116 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2315 A


        T-O-T SUMMARY
          Range  = 120.6578° <--> 180.0000 deg
          Mean   = 150.6891 deg
          StdDev = 25.9438 deg

        T--T SUMMARY
          Range  = 2.8323 A <--> 3.2323 A
          Mean   = 3.0649 A
          StdDev = 0.1599 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000