Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_648866_jQbSF1.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 24.36 T-atoms per nm^3
Material density = 2.430 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6372 Angstrom
T1  -- O2  = 1.6172 Angstrom
T1  -- O4  = 1.6215 Angstrom
T1  -- O3  = 1.6395 Angstrom
      mean = 1.6289 Angstrom
        t1 = 0.040661  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026540  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6067 Angstrom
T2  -- O3  = 1.6081 Angstrom
T2  -- O6  = 1.6195 Angstrom
T2  -- O4  = 1.6242 Angstrom
      mean = 1.6146 Angstrom
        t1 = 0.037558  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.042957  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6067 A <--> 1.6395 A
          Mean   = 1.6217 A
          StdDev = 0.0115 A

       t1 Range  = 0.0376 <-- 0.0391 --> 0.0407
       t2 Range  = 0.0265 <-- 0.0347 --> 0.0430

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 119.255 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 106.726 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 107.121 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 104.451 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 102.644 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 117.261 deg; O4  -- O3  = 3 A
       102.644 deg <-- 109.576 deg --> 119.255 deg

O5  -- T2  -- O3  = 102.027 deg; O5  -- O3  = 2 A
O5  -- T2  -- O6  = 119.193 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 106.287 deg; O5  -- O4  = 3 A
O3  -- T2  -- O6  = 104.247 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 114.491 deg; O3  -- O4  = 3 A
O6  -- T2  -- O4  = 110.631 deg; O6  -- O4  = 3 A
       102.027 deg <-- 109.479 deg --> 119.193 deg

        O-T-O SUMMARY
          Range  = 102.0267 deg <--> 119.2546 deg
          Mean   = 108.6463 deg
          StdDev = 5.7948 deg

        O--O SUMMARY
          Range  = 2.4988 A <--> 2.8078 A
          Mean   = 2.6319 A
          StdDev = 0.0972 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  81.313 deg; T2  -- T1  = 4.0377 A
T2  - O1  - T1  - O4  - T1  = 120.406 deg; T2  -- T1  = 5.3330 A
T2  - O1  - T1  - O3  - T2  = 138.158 deg; T2  -- T2  = 5.3902 A
T1  - O2  - T1  - O4  - T1  = 119.255 deg; T1  -- T1  = 5.6156 A
T1  - O2  - T1  - O3  - T2  =  85.097 deg; T1  -- T2  = 4.1609 A
T1  - O4  - T1  - O3  - T2  = 100.768 deg; T1  -- T2  = 4.7026 A

T1  - O5  - T2  - O3  - T2  =  96.044 deg; T1  -- T2  = 4.5553 A
T1  - O5  - T2  - O6  - T2  =  85.021 deg; T1  -- T2  = 4.1609 A
T1  - O5  - T2  - O4  - T1  = 138.158 deg; T1  -- T1  = 5.3902 A
T2  - O3  - T2  - O6  - T2  = 119.193 deg; T2  -- T2  = 5.5650 A
T2  - O3  - T2  - O4  - T1  = 124.781 deg; T2  -- T1  = 5.3864 A
T2  - O6  - T2  - O4  - T1  =  82.620 deg; T2  -- T1  = 4.0377 A

        T-T-T SUMMARY
          Range  = 81.3130 deg <--> 138.1584 deg
          Mean   = 109.7861 deg
          StdDev = 20.5993 deg

        T--T SUMMARY
          Range  = 4.0377 A <--> 5.6156 A
          Mean   = 4.9306 A
          StdDev = 0.6127 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2744 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2344 A

T1  -- O3  -- T2  = 127.140 deg ; T1  -- T2   2.9082 A

T1  -- O4  -- T2  = 123.745 deg ; T1  -- T2   2.8625 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2133 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   3.2390 A


        T-O-T SUMMARY
          Range  = 123.7454° <--> 180.0000 deg
          Mean   = 161.8142 deg
          StdDev = 26.8817 deg

        T--T SUMMARY
          Range  = 2.8625 A <--> 3.2744 A
          Mean   = 3.1220 A
          StdDev = 0.1763 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 40 62 90 122 160 202 250 298 340 371 393 405 413
TD10 = 962
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.10_{12}
Weight = 31

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 40 62 90 122 160 202 250 298 340 371 393 406 413
TD10 = 962
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.10_{12}
Weight = 31

<TD10> = 962.000
Average ring size = 7.7273