Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_627654_9NKtSI.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 23.45 T-atoms per nm^3
Material density = 2.339 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6253 Angstrom
T1  -- O3  = 1.6575 Angstrom
T1  -- O4  = 1.6184 Angstrom
T1  -- O2  = 1.6260 Angstrom
      mean = 1.6318 Angstrom
        t1 = 0.022982  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016045  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6065 Angstrom
T2  -- O4  = 1.6229 Angstrom
T2  -- O5  = 1.6219 Angstrom
T2  -- O3  = 1.6613 Angstrom
      mean = 1.6282 Angstrom
        t1 = 0.035615  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.035945  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6065 A <--> 1.6613 A
          Mean   = 1.6300 A
          StdDev = 0.0186 A

       t1 Range  = 0.0230 <-- 0.0293 --> 0.0356
       t2 Range  = 0.0160 <-- 0.0260 --> 0.0359

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 111.249 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 113.288 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 104.718 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 109.826 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 109.804 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 107.750 deg; O4  -- O2  = 3 A
       104.718 deg <-- 109.439 deg --> 113.288 deg

O2  -- T2  -- O4  = 111.589 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 103.482 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 107.550 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 108.789 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 106.146 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 119.324 deg; O5  -- O3  = 3 A
       103.482 deg <-- 109.480 deg --> 119.324 deg

        O-T-O SUMMARY
          Range  = 103.4821 deg <--> 119.3237 deg
          Mean   = 109.4596 deg
          StdDev = 4.1301 deg

        O--O SUMMARY
          Range  = 2.5350 A <--> 2.8337 A
          Mean   = 2.6601 A
          StdDev = 0.0740 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T2  = 107.904 deg; T1  -- T2  = 4.8553 A
T1  - O1  - T1  - O4  - T2  = 134.655 deg; T1  -- T2  = 5.7373 A
T1  - O1  - T1  - O2  - T2  = 118.690 deg; T1  -- T2  = 5.4503 A
T2  - O3  - T1  - O4  - T2  = 110.876 deg; T2  -- T2  = 4.7034 A
T2  - O3  - T1  - O2  - T2  =  84.256 deg; T2  -- T2  = 3.9173 A
T2  - O4  - T1  - O2  - T2  =  88.000 deg; T2  -- T2  = 4.2039 A

T2  - O2  - T2  - O4  - T1  = 153.494 deg; T2  -- T1  = 5.8288 A
T2  - O2  - T2  - O5  - T1  =  86.933 deg; T2  -- T1  = 4.2768 A
T2  - O2  - T2  - O3  - T1  = 103.327 deg; T2  -- T1  = 4.9648 A
T1  - O4  - T2  - O5  - T1  = 110.876 deg; T1  -- T1  = 4.7034 A
T1  - O4  - T2  - O3  - T1  =  95.744 deg; T1  -- T1  = 4.3281 A
T1  - O5  - T2  - O3  - T1  =  92.000 deg; T1  -- T1  = 4.3532 A

        T-T-T SUMMARY
          Range  = 84.2559 deg <--> 153.4940 deg
          Mean   = 107.2296 deg
          StdDev = 20.3011 deg

        T--T SUMMARY
          Range  = 3.9173 A <--> 5.8288 A
          Mean   = 4.7769 A
          StdDev = 0.6067 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2505 A

T1  -- O2  -- T2  = 145.191 deg ; T1  -- T2   3.0845 A

T1  -- O3  -- T2  = 111.494 deg ; T1  -- T2   2.7432 A

T1  -- O4  -- T2  = 132.440 deg ; T1  -- T2   2.9661 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2439 A


        T-O-T SUMMARY
          Range  = 111.4936° <--> 180.0000 deg
          Mean   = 149.8249 deg
          StdDev = 28.3395 deg

        T--T SUMMARY
          Range  = 2.7432 A <--> 3.2505 A
          Mean   = 3.0576 A
          StdDev = 0.1999 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7432 Angstrom
T2  -- T1  = 2.7432 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 217 262 266 310 309 364
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 217 261 265 312 308 361
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000