Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_627308_1IKFrc.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 21.81 T-atoms per nm^3
Material density = 2.176 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6131 Angstrom
T1  -- O2  = 1.6342 Angstrom
T1  -- O3  = 1.6311 Angstrom
T1  -- O4  = 1.6237 Angstrom
      mean = 1.6255 Angstrom
        t1 = 0.013726  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007114  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6319 Angstrom
T2  -- O4  = 1.6199 Angstrom
T2  -- O5  = 1.6146 Angstrom
T2  -- O2  = 1.6272 Angstrom
      mean = 1.6234 Angstrom
        t1 = 0.019020  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010905  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6131 A <--> 1.6342 A
          Mean   = 1.6245 A
          StdDev = 0.0077 A

       t1 Range  = 0.0137 <-- 0.0164 --> 0.0190
       t2 Range  = 0.0071 <-- 0.0090 --> 0.0109

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.151 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.712 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.004 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 111.824 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.007 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.104 deg; O3  -- O4  = 3 A
       108.007 deg <-- 109.467 deg --> 111.824 deg

O3  -- T2  -- O4  = 108.053 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.220 deg; O3  -- O5  = 3 A
O3  -- T2  -- O2  = 106.913 deg; O3  -- O2  = 3 A
O4  -- T2  -- O5  = 106.449 deg; O4  -- O5  = 3 A
O4  -- T2  -- O2  = 111.127 deg; O4  -- O2  = 3 A
O5  -- T2  -- O2  = 114.905 deg; O5  -- O2  = 3 A
       106.449 deg <-- 109.445 deg --> 114.905 deg

        O-T-O SUMMARY
          Range  = 106.4488 deg <--> 114.9052 deg
          Mean   = 109.4558 deg
          StdDev = 2.3431 deg

        O--O SUMMARY
          Range  = 2.5908 A <--> 2.7326 A
          Mean   = 2.6519 A
          StdDev = 0.0380 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 128.705 deg; T2  -- T1  = 5.6196 A
T2  - O1  - T1  - O3  - T2  = 104.617 deg; T2  -- T2  = 4.6042 A
T2  - O1  - T1  - O4  - T2  = 106.815 deg; T2  -- T2  = 4.8410 A
T1  - O2  - T1  - O3  - T2  = 125.763 deg; T1  -- T2  = 5.3757 A
T1  - O2  - T1  - O4  - T2  =  90.904 deg; T1  -- T2  = 4.4556 A
T2  - O3  - T1  - O4  - T2  =  81.465 deg; T2  -- T2  = 3.8092 A

T1  - O3  - T2  - O4  - T1  =  75.383 deg; T1  -- T1  = 3.5597 A
T1  - O3  - T2  - O5  - T2  = 111.331 deg; T1  -- T2  = 5.1509 A
T1  - O3  - T2  - O2  - T1  = 106.815 deg; T1  -- T1  = 4.8410 A
T1  - O4  - T2  - O5  - T2  = 145.488 deg; T1  -- T2  = 5.7684 A
T1  - O4  - T2  - O2  - T1  =  98.535 deg; T1  -- T1  = 4.4217 A
T2  - O5  - T2  - O2  - T1  = 110.737 deg; T2  -- T1  = 5.1455 A

        T-T-T SUMMARY
          Range  = 75.3831 deg <--> 145.4877 deg
          Mean   = 107.2132 deg
          StdDev = 19.3925 deg

        T--T SUMMARY
          Range  = 3.5597 A <--> 5.7684 A
          Mean   = 4.7994 A
          StdDev = 0.6598 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2261 A

T1  -- O2  -- T2  = 118.973 deg ; T1  -- T2   2.8097 A

T1  -- O3  -- T2  = 134.288 deg ; T1  -- T2   3.0068 A

T1  -- O4  -- T2  = 137.458 deg ; T1  -- T2   3.0227 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2291 A


        T-O-T SUMMARY
          Range  = 118.9734° <--> 180.0000 deg
          Mean   = 150.1439 deg
          StdDev = 26.5276 deg

        T--T SUMMARY
          Range  = 2.8097 A <--> 3.2291 A
          Mean   = 3.0589 A
          StdDev = 0.1654 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 296 326 346 369 387
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 295 325 349 368 384
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000