Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_626562_NTmD4e.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 23.22 T-atoms per nm^3
Material density = 2.316 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6250 Angstrom
T1  -- O3  = 1.6326 Angstrom
T1  -- O4  = 1.6192 Angstrom
T1  -- O2  = 1.6441 Angstrom
      mean = 1.6302 Angstrom
        t1 = 0.027453  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027704  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6150 Angstrom
T2  -- O4  = 1.6280 Angstrom
T2  -- O3  = 1.6094 Angstrom
T2  -- O5  = 1.5994 Angstrom
      mean = 1.6130 Angstrom
        t1 = 0.032553  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.023405  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5994 A <--> 1.6441 A
          Mean   = 1.6216 A
          StdDev = 0.0135 A

       t1 Range  = 0.0275 <-- 0.0300 --> 0.0326
       t2 Range  = 0.0234 <-- 0.0256 --> 0.0277

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 111.617 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 104.383 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 111.309 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 105.109 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 113.854 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 109.942 deg; O4  -- O2  = 3 A
       104.383 deg <-- 109.369 deg --> 113.854 deg

O2  -- T2  -- O4  = 112.242 deg; O2  -- O4  = 3 A
O2  -- T2  -- O3  = 106.325 deg; O2  -- O3  = 3 A
O2  -- T2  -- O5  = 114.985 deg; O2  -- O5  = 3 A
O4  -- T2  -- O3  = 102.294 deg; O4  -- O3  = 3 A
O4  -- T2  -- O5  = 115.263 deg; O4  -- O5  = 3 A
O3  -- T2  -- O5  = 104.058 deg; O3  -- O5  = 3 A
       102.294 deg <-- 109.194 deg --> 115.263 deg

        O-T-O SUMMARY
          Range  = 102.2937 deg <--> 115.2631 deg
          Mean   = 109.2818 deg
          StdDev = 4.5131 deg

        O--O SUMMARY
          Range  = 2.5212 A <--> 2.7458 A
          Mean   = 2.6431 A
          StdDev = 0.0796 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T2  = 123.003 deg; T1  -- T2  = 5.4706 A
T1  - O1  - T1  - O4  - T2  =  90.400 deg; T1  -- T2  = 4.4510 A
T1  - O1  - T1  - O2  - T2  = 130.622 deg; T1  -- T2  = 5.5549 A
T2  - O3  - T1  - O4  - T2  = 103.773 deg; T2  -- T2  = 4.7143 A
T2  - O3  - T1  - O2  - T2  = 106.278 deg; T2  -- T2  = 4.6684 A
T2  - O4  - T1  - O2  - T2  =  80.154 deg; T2  -- T2  = 3.7875 A

T1  - O2  - T2  - O4  - T1  = 103.773 deg; T1  -- T1  = 4.7143 A
T1  - O2  - T2  - O3  - T1  =  73.722 deg; T1  -- T1  = 3.5010 A
T1  - O2  - T2  - O5  - T2  =  96.457 deg; T1  -- T2  = 4.6055 A
T1  - O4  - T2  - O3  - T1  =  99.846 deg; T1  -- T1  = 4.5003 A
T1  - O4  - T2  - O5  - T2  = 121.083 deg; T1  -- T2  = 5.4144 A
T1  - O3  - T2  - O5  - T2  = 139.029 deg; T1  -- T2  = 5.6781 A

        T-T-T SUMMARY
          Range  = 73.7222 deg <--> 139.0292 deg
          Mean   = 105.6783 deg
          StdDev = 19.3474 deg

        T--T SUMMARY
          Range  = 3.5010 A <--> 5.6781 A
          Mean   = 4.7550 A
          StdDev = 0.6684 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2500 A

T1  -- O2  -- T2  = 122.783 deg ; T1  -- T2   2.8612 A

T1  -- O3  -- T2  = 132.992 deg ; T1  -- T2   2.9731 A

T1  -- O4  -- T2  = 136.755 deg ; T1  -- T2   3.0187 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.1989 A


        T-O-T SUMMARY
          Range  = 122.7826° <--> 180.0000 deg
          Mean   = 150.5059 deg
          StdDev = 25.8380 deg

        T--T SUMMARY
          Range  = 2.8612 A <--> 3.2500 A
          Mean   = 3.0604 A
          StdDev = 0.1521 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000