Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_626216_JFhDoD.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 21.70 T-atoms per nm^3
Material density = 2.165 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6200 Angstrom
T1  -- O4  = 1.6277 Angstrom
T1  -- O2  = 1.6202 Angstrom
T1  -- O3  = 1.6185 Angstrom
      mean = 1.6216 Angstrom
        t1 = 0.017067  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014766  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6218 Angstrom
T2  -- O4  = 1.6326 Angstrom
T2  -- O5  = 1.6187 Angstrom
T2  -- O3  = 1.6259 Angstrom
      mean = 1.6248 Angstrom
        t1 = 0.010047  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002787  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6185 A <--> 1.6326 A
          Mean   = 1.6232 A
          StdDev = 0.0049 A

       t1 Range  = 0.0100 <-- 0.0136 --> 0.0171
       t2 Range  = 0.0028 <-- 0.0088 --> 0.0148

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O4  = 113.542 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 106.765 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.025 deg; O1  -- O3  = 3 A
O4  -- T1  -- O2  = 107.223 deg; O4  -- O2  = 3 A
O4  -- T1  -- O3  = 111.302 deg; O4  -- O3  = 3 A
O2  -- T1  -- O3  = 107.673 deg; O2  -- O3  = 3 A
       106.765 deg <-- 109.422 deg --> 113.542 deg

O2  -- T2  -- O4  = 108.840 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.695 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 108.462 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 110.131 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 109.050 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 110.622 deg; O5  -- O3  = 3 A
       108.462 deg <-- 109.466 deg --> 110.622 deg

        O-T-O SUMMARY
          Range  = 106.7655 deg <--> 113.5424 deg
          Mean   = 109.4442 deg
          StdDev = 1.8472 deg

        O--O SUMMARY
          Range  = 2.6007 A <--> 2.7167 A
          Mean   = 2.6499 A
          StdDev = 0.0311 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O4  - T2  = 132.699 deg; T1  -- T2  = 5.5799 A
T1  - O1  - T1  - O2  - T2  =  89.959 deg; T1  -- T2  = 4.4207 A
T1  - O1  - T1  - O3  - T2  = 124.571 deg; T1  -- T2  = 5.5252 A
T2  - O4  - T1  - O2  - T2  =  80.688 deg; T2  -- T2  = 3.7949 A
T2  - O4  - T1  - O3  - T2  = 102.331 deg; T2  -- T2  = 4.5572 A
T2  - O2  - T1  - O3  - T2  = 107.473 deg; T2  -- T2  = 4.8457 A

T2  - O2  - T2  - O4  - T1  = 138.586 deg; T2  -- T1  = 5.6950 A
T2  - O2  - T2  - O5  - T1  = 106.715 deg; T2  -- T1  = 5.0066 A
T2  - O2  - T2  - O3  - T1  = 117.279 deg; T2  -- T1  = 5.3358 A
T1  - O4  - T2  - O5  - T1  =  77.669 deg; T1  -- T1  = 3.6697 A
T1  - O4  - T2  - O3  - T1  =  99.312 deg; T1  -- T1  = 4.4668 A
T1  - O5  - T2  - O3  - T1  = 107.473 deg; T1  -- T1  = 4.8457 A

        T-T-T SUMMARY
          Range  = 77.6688 deg <--> 138.5865 deg
          Mean   = 107.0630 deg
          StdDev = 18.6431 deg

        T--T SUMMARY
          Range  = 3.6697 A <--> 5.6950 A
          Mean   = 4.8119 A
          StdDev = 0.6507 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2400 A

T1  -- O2  -- T2  = 136.366 deg ; T1  -- T2   3.0098 A

T1  -- O3  -- T2  = 135.223 deg ; T1  -- T2   2.9999 A

T1  -- O4  -- T2  = 121.829 deg ; T1  -- T2   2.8492 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2373 A


        T-O-T SUMMARY
          Range  = 121.8286° <--> 180.0000 deg
          Mean   = 150.6834 deg
          StdDev = 25.8007 deg

        T--T SUMMARY
          Range  = 2.8492 A <--> 3.2400 A
          Mean   = 3.0672 A
          StdDev = 0.1593 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 538
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 476 537
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000