Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_626144_R1miT8.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 24.98 T-atoms per nm^3
Material density = 2.492 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6534 Angstrom
T1  -- O4  = 1.6087 Angstrom
T1  -- O2  = 1.6666 Angstrom
T1  -- O3  = 1.6245 Angstrom
      mean = 1.6383 Angstrom
        t1 = 0.039018  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.024628  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6236 Angstrom
T2  -- O5  = 1.6329 Angstrom
T2  -- O3  = 1.5768 Angstrom
T2  -- O4  = 1.6084 Angstrom
      mean = 1.6104 Angstrom
        t1 = 0.144840  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.161828  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5768 A <--> 1.6666 A
          Mean   = 1.6244 A
          StdDev = 0.0270 A

       t1 Range  = 0.0390 <-- 0.0919 --> 0.1448
       t2 Range  = 0.0246 <-- 0.0932 --> 0.1618

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O4  = 103.784 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 104.539 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 116.885 deg; O1  -- O3  = 3 A
O4  -- T1  -- O2  = 102.424 deg; O4  -- O2  = 3 A
O4  -- T1  -- O3  = 112.066 deg; O4  -- O3  = 3 A
O2  -- T1  -- O3  = 115.508 deg; O2  -- O3  = 3 A
       102.424 deg <-- 109.201 deg --> 116.885 deg

O2  -- T2  -- O5  = 130.145 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  =  74.826 deg; O2  -- O3  = 2 A
O2  -- T2  -- O4  = 117.737 deg; O2  -- O4  = 3 A
O5  -- T2  -- O3  =  85.426 deg; O5  -- O3  = 2 A
O5  -- T2  -- O4  = 109.246 deg; O5  -- O4  = 3 A
O3  -- T2  -- O4  =  95.473 deg; O3  -- O4  = 2 A
       74.826 deg <-- 102.142 deg --> 130.145 deg

        O-T-O SUMMARY
          Range  = 74.8264 deg <--> 130.1451 deg
          Mean   = 105.6717 deg
          StdDev = 14.7483 deg

        O--O SUMMARY
          Range  = 1.9448 A <--> 2.9531 A
          Mean   = 2.5705 A
          StdDev = 0.2785 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O4  - T2  =  93.982 deg; T1  -- T2  = 4.7358 A
T1  - O1  - T1  - O2  - T2  = 118.980 deg; T1  -- T2  = 5.3200 A
T1  - O1  - T1  - O3  - T2  = 133.431 deg; T1  -- T2  = 5.7558 A
T2  - O4  - T1  - O2  - T2  =  80.713 deg; T2  -- T2  = 3.9123 A
T2  - O4  - T1  - O3  - T2  =  97.177 deg; T2  -- T2  = 4.5964 A
T2  - O2  - T1  - O3  - T2  = 107.421 deg; T2  -- T2  = 4.6917 A

T1  - O2  - T2  - O5  - T1  =  82.823 deg; T1  -- T1  = 4.0552 A
T1  - O2  - T2  - O3  - T2  =  78.641 deg; T1  -- T2  = 3.9508 A
T1  - O2  - T2  - O4  - T1  = 107.421 deg; T1  -- T1  = 4.6917 A
T1  - O5  - T2  - O3  - T2  = 102.581 deg; T1  -- T2  = 5.0212 A
T1  - O5  - T2  - O4  - T1  =  99.287 deg; T1  -- T1  = 4.6001 A
T2  - O3  - T2  - O4  - T1  = 157.904 deg; T2  -- T1  = 6.0155 A

        T-T-T SUMMARY
          Range  = 78.6414 deg <--> 157.9041 deg
          Mean   = 105.0302 deg
          StdDev = 22.4806 deg

        T--T SUMMARY
          Range  = 3.9123 A <--> 6.0155 A
          Mean   = 4.7789 A
          StdDev = 0.6513 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.3067 A

T1  -- O2  -- T2  = 120.927 deg ; T1  -- T2   2.8627 A

T1  -- O3  -- T2  = 134.995 deg ; T1  -- T2   2.9576 A

T1  -- O4  -- T2  = 160.025 deg ; T1  -- T2   3.1683 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2659 A


        T-O-T SUMMARY
          Range  = 120.9273° <--> 180.0000 deg
          Mean   = 155.1895 deg
          StdDev = 25.1052 deg

        T--T SUMMARY
          Range  = 2.8627 A <--> 3.3067 A
          Mean   = 3.1122 A
          StdDev = 0.1830 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O3  = 1.9448 A
O3  -- O5  = 2.1777 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 253 293 328 352 379 410
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 253 293 328 352 380 412
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000