Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_626122_qKkTRU.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 21.29 T-atoms per nm^3
Material density = 2.124 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6192 Angstrom
T1  -- O2  = 1.6234 Angstrom
T1  -- O4  = 1.5941 Angstrom
T1  -- O3  = 1.6235 Angstrom
      mean = 1.6150 Angstrom
        t1 = 0.039077  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.056904  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6098 Angstrom
T2  -- O3  = 1.6329 Angstrom
T2  -- O4  = 1.6351 Angstrom
T2  -- O2  = 1.5668 Angstrom
      mean = 1.6112 Angstrom
        t1 = 0.074668  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.062090  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5668 A <--> 1.6351 A
          Mean   = 1.6131 A
          StdDev = 0.0220 A

       t1 Range  = 0.0391 <-- 0.0569 --> 0.0747
       t2 Range  = 0.0569 <-- 0.0595 --> 0.0621

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.619 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  =  97.601 deg; O1  -- O4  = 2 A
O1  -- T1  -- O3  = 111.787 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 113.258 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 114.843 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 108.457 deg; O4  -- O3  = 3 A
       97.601 deg <-- 109.261 deg --> 114.843 deg

O5  -- T2  -- O3  =  91.528 deg; O5  -- O3  = 2 A
O5  -- T2  -- O4  = 115.697 deg; O5  -- O4  = 3 A
O5  -- T2  -- O2  = 126.363 deg; O5  -- O2  = 3 A
O3  -- T2  -- O4  =  94.328 deg; O3  -- O4  = 2 A
O3  -- T2  -- O2  = 101.549 deg; O3  -- O2  = 2 A
O4  -- T2  -- O2  = 114.825 deg; O4  -- O2  = 3 A
       91.528 deg <-- 107.382 deg --> 126.363 deg

        O-T-O SUMMARY
          Range  = 91.5284 deg <--> 126.3628 deg
          Mean   = 108.3214 deg
          StdDev = 9.9626 deg

        O--O SUMMARY
          Range  = 2.3234 A <--> 2.8350 A
          Mean   = 2.6055 A
          StdDev = 0.1582 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 102.600 deg; T1  -- T2  = 4.9832 A
T1  - O1  - T1  - O4  - T2  = 101.789 deg; T1  -- T2  = 4.8924 A
T1  - O1  - T1  - O3  - T2  = 137.943 deg; T1  -- T2  = 5.7539 A
T2  - O2  - T1  - O4  - T2  =  88.781 deg; T2  -- T2  = 4.3456 A
T2  - O2  - T1  - O3  - T2  = 102.988 deg; T2  -- T2  = 4.7531 A
T2  - O4  - T1  - O3  - T2  = 111.556 deg; T2  -- T2  = 4.9534 A

T1  - O5  - T2  - O3  - T1  =  77.012 deg; T1  -- T1  = 3.7840 A
T1  - O5  - T2  - O4  - T2  = 128.491 deg; T1  -- T2  = 5.7338 A
T1  - O5  - T2  - O2  - T1  =  91.219 deg; T1  -- T1  = 4.4390 A
T1  - O3  - T2  - O4  - T2  =  85.180 deg; T1  -- T2  = 4.1640 A
T1  - O3  - T2  - O2  - T1  = 111.556 deg; T1  -- T1  = 4.9534 A
T2  - O4  - T2  - O2  - T1  = 140.047 deg; T2  -- T1  = 5.9067 A

        T-T-T SUMMARY
          Range  = 77.0122 deg <--> 140.0472 deg
          Mean   = 106.5967 deg
          StdDev = 19.9345 deg

        T--T SUMMARY
          Range  = 3.7840 A <--> 5.9067 A
          Mean   = 4.8885 A
          StdDev = 0.6445 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2383 A

T1  -- O2  -- T2  = 147.776 deg ; T1  -- T2   3.0649 A

T1  -- O3  -- T2  = 127.846 deg ; T1  -- T2   2.9249 A

T1  -- O4  -- T2  = 154.006 deg ; T1  -- T2   3.1465 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2196 A


        T-O-T SUMMARY
          Range  = 127.8464° <--> 180.0000 deg
          Mean   = 157.9257 deg
          StdDev = 21.0697 deg

        T--T SUMMARY
          Range  = 2.9249 A <--> 3.2383 A
          Mean   = 3.1189 A
          StdDev = 0.1208 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 210 243 273 297 319 349 376
TD10 = 829
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 210 243 273 298 320 349 376
TD10 = 829
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 829.000
Average ring size = 5.6000