Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_625609_Xzta2w.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 20.74 T-atoms per nm^3
Material density = 2.069 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5895 Angstrom
T1  -- O2  = 1.6182 Angstrom
T1  -- O4  = 1.6134 Angstrom
T1  -- O3  = 1.6281 Angstrom
      mean = 1.6123 Angstrom
        t1 = 0.023184  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026467  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6158 Angstrom
T2  -- O2  = 1.6129 Angstrom
T2  -- O4  = 1.6228 Angstrom
T2  -- O5  = 1.6125 Angstrom
      mean = 1.6160 Angstrom
        t1 = 0.019913  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027798  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5895 A <--> 1.6281 A
          Mean   = 1.6141 A
          StdDev = 0.0109 A

       t1 Range  = 0.0199 <-- 0.0215 --> 0.0232
       t2 Range  = 0.0265 <-- 0.0271 --> 0.0278

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.684 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 104.892 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 105.079 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 112.997 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 110.504 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 111.281 deg; O4  -- O3  = 3 A
       104.892 deg <-- 109.406 deg --> 112.997 deg

O3  -- T2  -- O2  = 109.229 deg; O3  -- O2  = 3 A
O3  -- T2  -- O4  = 102.895 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.309 deg; O3  -- O5  = 3 A
O2  -- T2  -- O4  = 111.472 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 113.550 deg; O2  -- O5  = 3 A
O4  -- T2  -- O5  = 109.834 deg; O4  -- O5  = 3 A
       102.895 deg <-- 109.382 deg --> 113.550 deg

        O-T-O SUMMARY
          Range  = 102.8951 deg <--> 113.5500 deg
          Mean   = 109.3940 deg
          StdDev = 3.3095 deg

        O--O SUMMARY
          Range  = 2.5327 A <--> 2.6981 A
          Mean   = 2.6336 A
          StdDev = 0.0579 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 120.175 deg; T1  -- T2  = 5.4277 A
T1  - O1  - T1  - O4  - T2  = 128.087 deg; T1  -- T2  = 5.4854 A
T1  - O1  - T1  - O3  - T2  = 100.536 deg; T1  -- T2  = 4.7169 A
T2  - O2  - T1  - O4  - T2  = 102.313 deg; T2  -- T2  = 4.6766 A
T2  - O2  - T1  - O3  - T2  =  85.336 deg; T2  -- T2  = 4.0907 A
T2  - O4  - T1  - O3  - T2  = 111.982 deg; T2  -- T2  = 4.8676 A

T1  - O3  - T2  - O2  - T1  =  94.664 deg; T1  -- T1  = 4.4377 A
T1  - O3  - T2  - O4  - T2  = 126.059 deg; T1  -- T2  = 5.6218 A
T1  - O3  - T2  - O5  - T1  =  77.687 deg; T1  -- T1  = 3.7671 A
T1  - O2  - T2  - O4  - T2  = 134.317 deg; T1  -- T2  = 5.6931 A
T1  - O2  - T2  - O5  - T1  = 111.982 deg; T1  -- T1  = 4.8676 A
T2  - O4  - T2  - O5  - T1  =  97.690 deg; T2  -- T1  = 4.6314 A

        T-T-T SUMMARY
          Range  = 77.6868 deg <--> 134.3172 deg
          Mean   = 107.5690 deg
          StdDev = 17.2064 deg

        T--T SUMMARY
          Range  = 3.7671 A <--> 5.6931 A
          Mean   = 4.8570 A
          StdDev = 0.5941 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.1791 A

T1  -- O2  -- T2  = 131.984 deg ; T1  -- T2   2.9516 A

T1  -- O3  -- T2  = 128.394 deg ; T1  -- T2   2.9204 A

T1  -- O4  -- T2  = 144.543 deg ; T1  -- T2   3.0825 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2249 A


        T-O-T SUMMARY
          Range  = 128.3936° <--> 180.0000 deg
          Mean   = 152.9842 deg
          StdDev = 23.9288 deg

        T--T SUMMARY
          Range  = 2.9204 A <--> 3.2249 A
          Mean   = 3.0717 A
          StdDev = 0.1269 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 126 159 151 186 178 215 204 245
TD10 = 731
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 126 159 151 186 178 215 204 245
TD10 = 731
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 731.000
Average ring size = 5.6000