Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_625350_tcpodr.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 24.22 T-atoms per nm^3
Material density = 2.416 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6354 Angstrom
T1  -- O2  = 1.6285 Angstrom
T1  -- O4  = 1.6297 Angstrom
T1  -- O3  = 1.6168 Angstrom
      mean = 1.6276 Angstrom
        t1 = 0.015079  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011706  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6129 Angstrom
T2  -- O4  = 1.6136 Angstrom
T2  -- O2  = 1.6225 Angstrom
T2  -- O5  = 1.6048 Angstrom
      mean = 1.6134 Angstrom
        t1 = 0.013102  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010262  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6048 A <--> 1.6354 A
          Mean   = 1.6205 A
          StdDev = 0.0100 A

       t1 Range  = 0.0131 <-- 0.0141 --> 0.0151
       t2 Range  = 0.0103 <-- 0.0110 --> 0.0117

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.230 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 111.438 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 111.224 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 108.151 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 107.332 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.332 deg; O4  -- O3  = 3 A
       107.332 deg <-- 109.451 deg --> 111.438 deg

O3  -- T2  -- O4  = 110.617 deg; O3  -- O4  = 3 A
O3  -- T2  -- O2  = 110.611 deg; O3  -- O2  = 3 A
O3  -- T2  -- O5  = 107.560 deg; O3  -- O5  = 3 A
O4  -- T2  -- O2  = 109.243 deg; O4  -- O2  = 3 A
O4  -- T2  -- O5  = 106.706 deg; O4  -- O5  = 3 A
O2  -- T2  -- O5  = 112.032 deg; O2  -- O5  = 3 A
       106.706 deg <-- 109.462 deg --> 112.032 deg

        O-T-O SUMMARY
          Range  = 106.7062 deg <--> 112.0315 deg
          Mean   = 109.4562 deg
          StdDev = 1.7157 deg

        O--O SUMMARY
          Range  = 2.5822 A <--> 2.6979 A
          Mean   = 2.6458 A
          StdDev = 0.0339 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.583 deg; T1  -- T2  = 4.4218 A
T1  - O1  - T1  - O4  - T2  = 130.029 deg; T1  -- T2  = 5.6054 A
T1  - O1  - T1  - O3  - T2  = 107.674 deg; T1  -- T2  = 5.1924 A
T2  - O2  - T1  - O4  - T2  = 108.622 deg; T2  -- T2  = 4.7542 A
T2  - O2  - T1  - O3  - T2  = 111.826 deg; T2  -- T2  = 5.0556 A
T2  - O4  - T1  - O3  - T2  = 106.830 deg; T2  -- T2  = 4.8773 A

T1  - O3  - T2  - O4  - T1  = 106.830 deg; T1  -- T1  = 4.8773 A
T1  - O3  - T2  - O2  - T1  = 111.826 deg; T1  -- T1  = 5.0556 A
T1  - O3  - T2  - O5  - T2  = 118.683 deg; T1  -- T2  = 5.4794 A
T1  - O4  - T2  - O2  - T1  = 108.622 deg; T1  -- T1  = 4.7542 A
T1  - O4  - T2  - O5  - T2  =  85.990 deg; T1  -- T2  = 4.1796 A
T1  - O2  - T2  - O5  - T2  = 120.078 deg; T1  -- T2  = 5.3315 A

        T-T-T SUMMARY
          Range  = 85.9904 deg <--> 130.0285 deg
          Mean   = 108.9660 deg
          StdDev = 11.6274 deg

        T--T SUMMARY
          Range  = 4.1796 A <--> 5.6054 A
          Mean   = 4.9654 A
          StdDev = 0.4058 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2708 A

T1  -- O2  -- T2  = 129.670 deg ; T1  -- T2   2.9424 A

T1  -- O3  -- T2  = 156.183 deg ; T1  -- T2   3.1602 A

T1  -- O4  -- T2  = 127.680 deg ; T1  -- T2   2.9111 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2095 A


        T-O-T SUMMARY
          Range  = 127.6796° <--> 180.0000 deg
          Mean   = 154.7065 deg
          StdDev = 24.2166 deg

        T--T SUMMARY
          Range  = 2.9111 A <--> 3.2708 A
          Mean   = 3.0988 A
          StdDev = 0.1530 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 12 24 42 64 92 124 162 204 252 304 334 325 325 316 303
TD10 = 981
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 12 24 42 64 92 124 162 204 252 304 334 338 325 313 303
TD10 = 981
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29

<TD10> = 981.000
Average ring size = 6.0000