Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_625079_ZKEUx5.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 21.49 T-atoms per nm^3
Material density = 2.144 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6152 Angstrom
T1  -- O2  = 1.6229 Angstrom
T1  -- O3  = 1.6214 Angstrom
T1  -- O4  = 1.6225 Angstrom
      mean = 1.6205 Angstrom
        t1 = 0.012397  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010932  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6330 Angstrom
T2  -- O3  = 1.6218 Angstrom
T2  -- O5  = 1.6165 Angstrom
T2  -- O4  = 1.6254 Angstrom
      mean = 1.6242 Angstrom
        t1 = 0.009121  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001523  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6152 A <--> 1.6330 A
          Mean   = 1.6223 A
          StdDev = 0.0053 A

       t1 Range  = 0.0091 <-- 0.0108 --> 0.0124
       t2 Range  = 0.0015 <-- 0.0062 --> 0.0109

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 112.740 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.463 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.368 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.414 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.446 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.264 deg; O3  -- O4  = 3 A
       107.463 deg <-- 109.449 deg --> 112.740 deg

O2  -- T2  -- O3  = 109.275 deg; O2  -- O3  = 3 A
O2  -- T2  -- O5  = 109.399 deg; O2  -- O5  = 3 A
O2  -- T2  -- O4  = 109.525 deg; O2  -- O4  = 3 A
O3  -- T2  -- O5  = 109.654 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 108.892 deg; O3  -- O4  = 3 A
O5  -- T2  -- O4  = 110.078 deg; O5  -- O4  = 3 A
       108.892 deg <-- 109.471 deg --> 110.078 deg

        O-T-O SUMMARY
          Range  = 107.4632 deg <--> 112.7402 deg
          Mean   = 109.4600 deg
          StdDev = 1.2866 deg

        O--O SUMMARY
          Range  = 2.6095 A <--> 2.6961 A
          Mean   = 2.6489 A
          StdDev = 0.0211 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  79.413 deg; T2  -- T2  = 3.7401 A
T2  - O1  - T1  - O3  - T2  = 101.125 deg; T2  -- T2  = 4.5236 A
T2  - O1  - T1  - O4  - T1  = 136.698 deg; T2  -- T1  = 5.6369 A
T2  - O2  - T1  - O3  - T2  = 108.555 deg; T2  -- T2  = 4.9040 A
T2  - O2  - T1  - O4  - T1  =  94.980 deg; T2  -- T1  = 4.6081 A
T2  - O3  - T1  - O4  - T1  = 121.006 deg; T2  -- T1  = 5.4434 A

T1  - O2  - T2  - O3  - T1  = 100.587 deg; T1  -- T1  = 4.5023 A
T1  - O2  - T2  - O5  - T2  = 136.324 deg; T1  -- T2  = 5.6321 A
T1  - O2  - T2  - O4  - T1  =  78.875 deg; T1  -- T1  = 3.7222 A
T1  - O3  - T2  - O5  - T2  = 119.858 deg; T1  -- T2  = 5.4106 A
T1  - O3  - T2  - O4  - T1  = 108.555 deg; T1  -- T1  = 4.9040 A
T2  - O5  - T2  - O4  - T1  = 101.211 deg; T2  -- T1  = 4.8361 A

        T-T-T SUMMARY
          Range  = 78.8748 deg <--> 136.6981 deg
          Mean   = 107.2657 deg
          StdDev = 18.4464 deg

        T--T SUMMARY
          Range  = 3.7222 A <--> 5.6369 A
          Mean   = 4.8220 A
          StdDev = 0.6382 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2303 A

T1  -- O2  -- T2  = 120.902 deg ; T1  -- T2   2.8324 A

T1  -- O3  -- T2  = 137.027 deg ; T1  -- T2   3.0178 A

T1  -- O4  -- T2  = 137.071 deg ; T1  -- T2   3.0226 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2330 A


        T-O-T SUMMARY
          Range  = 120.9020° <--> 180.0000 deg
          Mean   = 151.0001 deg
          StdDev = 25.7213 deg

        T--T SUMMARY
          Range  = 2.8324 A <--> 3.2330 A
          Mean   = 3.0672 A
          StdDev = 0.1589 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 538
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 476 537
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000