Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_624960_JAOeJl.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 21.45 T-atoms per nm^3
Material density = 2.141 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6141 Angstrom
T1  -- O2  = 1.6312 Angstrom
T1  -- O3  = 1.6223 Angstrom
T1  -- O4  = 1.6193 Angstrom
      mean = 1.6217 Angstrom
        t1 = 0.012474  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010032  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6369 Angstrom
T2  -- O5  = 1.6150 Angstrom
T2  -- O3  = 1.6203 Angstrom
T2  -- O4  = 1.6257 Angstrom
      mean = 1.6245 Angstrom
        t1 = 0.009952  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002681  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6141 A <--> 1.6369 A
          Mean   = 1.6231 A
          StdDev = 0.0076 A

       t1 Range  = 0.0100 <-- 0.0112 --> 0.0125
       t2 Range  = 0.0027 <-- 0.0064 --> 0.0100

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 112.188 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.836 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.810 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.909 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.550 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.444 deg; O3  -- O4  = 3 A
       107.836 deg <-- 109.456 deg --> 112.188 deg

O2  -- T2  -- O5  = 110.174 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 108.988 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.765 deg; O2  -- O4  = 3 A
O5  -- T2  -- O3  = 109.643 deg; O5  -- O3  = 3 A
O5  -- T2  -- O4  = 109.049 deg; O5  -- O4  = 3 A
O3  -- T2  -- O4  = 109.206 deg; O3  -- O4  = 3 A
       108.988 deg <-- 109.471 deg --> 110.174 deg

        O-T-O SUMMARY
          Range  = 107.8361 deg <--> 112.1875 deg
          Mean   = 109.4634 deg
          StdDev = 1.1079 deg

        O--O SUMMARY
          Range  = 2.6156 A <--> 2.6935 A
          Mean   = 2.6503 A
          StdDev = 0.0212 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 138.795 deg; T2  -- T1  = 5.6641 A
T2  - O1  - T1  - O3  - T2  =  79.220 deg; T2  -- T2  = 3.7312 A
T2  - O1  - T1  - O4  - T2  = 100.569 deg; T2  -- T2  = 4.5074 A
T1  - O2  - T1  - O3  - T2  =  97.762 deg; T1  -- T2  = 4.7135 A
T1  - O2  - T1  - O4  - T2  = 118.799 deg; T1  -- T2  = 5.3926 A
T2  - O3  - T1  - O4  - T2  = 108.812 deg; T2  -- T2  = 4.9294 A

T1  - O2  - T2  - O5  - T2  = 136.368 deg; T1  -- T2  = 5.6198 A
T1  - O2  - T2  - O3  - T1  = 100.780 deg; T1  -- T1  = 4.5066 A
T1  - O2  - T2  - O4  - T1  =  79.431 deg; T1  -- T1  = 3.7461 A
T2  - O5  - T2  - O3  - T1  = 120.433 deg; T2  -- T1  = 5.4308 A
T2  - O5  - T2  - O4  - T1  =  98.576 deg; T2  -- T1  = 4.7513 A
T1  - O3  - T2  - O4  - T1  = 108.812 deg; T1  -- T1  = 4.9294 A

        T-T-T SUMMARY
          Range  = 79.2196 deg <--> 138.7949 deg
          Mean   = 107.3630 deg
          StdDev = 18.5711 deg

        T--T SUMMARY
          Range  = 3.7312 A <--> 5.6641 A
          Mean   = 4.8268 A
          StdDev = 0.6343 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2282 A

T1  -- O2  -- T2  = 119.353 deg ; T1  -- T2   2.8210 A

T1  -- O3  -- T2  = 137.889 deg ; T1  -- T2   3.0261 A

T1  -- O4  -- T2  = 138.640 deg ; T1  -- T2   3.0359 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2301 A


        T-O-T SUMMARY
          Range  = 119.3532° <--> 180.0000 deg
          Mean   = 151.1766 deg
          StdDev = 25.8543 deg

        T--T SUMMARY
          Range  = 2.8210 A <--> 3.2301 A
          Mean   = 3.0683 A
          StdDev = 0.1604 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 538
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 476 537
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000