Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_624958_keAfRS.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 21.40 T-atoms per nm^3
Material density = 2.135 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6143 Angstrom
T1  -- O2  = 1.6235 Angstrom
T1  -- O3  = 1.6173 Angstrom
T1  -- O4  = 1.6269 Angstrom
      mean = 1.6205 Angstrom
        t1 = 0.020151  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021870  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6336 Angstrom
T2  -- O3  = 1.6154 Angstrom
T2  -- O4  = 1.6257 Angstrom
T2  -- O5  = 1.6179 Angstrom
      mean = 1.6231 Angstrom
        t1 = 0.011868  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005717  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6143 A <--> 1.6336 A
          Mean   = 1.6218 A
          StdDev = 0.0065 A

       t1 Range  = 0.0119 <-- 0.0160 --> 0.0202
       t2 Range  = 0.0057 <-- 0.0138 --> 0.0219

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 115.042 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.261 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.080 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.894 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.857 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 107.298 deg; O3  -- O4  = 3 A
       105.261 deg <-- 109.405 deg --> 115.042 deg

O2  -- T2  -- O3  = 109.035 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.245 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 110.225 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 108.868 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 107.761 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 111.652 deg; O4  -- O5  = 3 A
       107.761 deg <-- 109.464 deg --> 111.652 deg

        O-T-O SUMMARY
          Range  = 105.2608 deg <--> 115.0421 deg
          Mean   = 109.4348 deg
          StdDev = 2.3725 deg

        O--O SUMMARY
          Range  = 2.5682 A <--> 2.7313 A
          Mean   = 2.6473 A
          StdDev = 0.0403 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 132.603 deg; T2  -- T1  = 5.5289 A
T2  - O1  - T1  - O3  - T2  =  83.663 deg; T2  -- T2  = 3.9074 A
T2  - O1  - T1  - O4  - T2  = 100.978 deg; T2  -- T2  = 4.5040 A
T1  - O2  - T1  - O3  - T2  =  88.181 deg; T1  -- T2  = 4.3677 A
T1  - O2  - T1  - O4  - T2  = 125.966 deg; T1  -- T2  = 5.5748 A
T2  - O3  - T1  - O4  - T2  = 106.847 deg; T2  -- T2  = 4.8780 A

T1  - O2  - T2  - O3  - T1  =  96.337 deg; T1  -- T1  = 4.3637 A
T1  - O2  - T2  - O4  - T2  = 140.457 deg; T1  -- T2  = 5.6882 A
T1  - O2  - T2  - O5  - T1  =  79.022 deg; T1  -- T1  = 3.7164 A
T1  - O3  - T2  - O4  - T2  = 113.226 deg; T1  -- T2  = 5.2461 A
T1  - O3  - T2  - O5  - T1  = 106.847 deg; T1  -- T1  = 4.8780 A
T2  - O4  - T2  - O5  - T1  = 114.108 deg; T2  -- T1  = 5.2580 A

        T-T-T SUMMARY
          Range  = 79.0221 deg <--> 140.4574 deg
          Mean   = 107.3528 deg
          StdDev = 18.7754 deg

        T--T SUMMARY
          Range  = 3.7164 A <--> 5.6882 A
          Mean   = 4.8259 A
          StdDev = 0.6440 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2285 A

T1  -- O2  -- T2  = 119.016 deg ; T1  -- T2   2.8067 A

T1  -- O3  -- T2  = 140.862 deg ; T1  -- T2   3.0459 A

T1  -- O4  -- T2  = 137.206 deg ; T1  -- T2   3.0284 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2358 A


        T-O-T SUMMARY
          Range  = 119.0164° <--> 180.0000 deg
          Mean   = 151.4169 deg
          StdDev = 25.8075 deg

        T--T SUMMARY
          Range  = 2.8067 A <--> 3.2358 A
          Mean   = 3.0691 A
          StdDev = 0.1662 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000