Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_624651_cjuWUO.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 21.97 T-atoms per nm^3
Material density = 2.192 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6053 Angstrom
T1  -- O2  = 1.5960 Angstrom
T1  -- O3  = 1.6145 Angstrom
T1  -- O4  = 1.5679 Angstrom
      mean = 1.5959 Angstrom
        t1 = 0.071773  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.045723  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6153 Angstrom
T2  -- O4  = 1.6553 Angstrom
T2  -- O3  = 1.6076 Angstrom
T2  -- O5  = 1.6678 Angstrom
      mean = 1.6365 Angstrom
        t1 = 0.037945  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021913  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5679 A <--> 1.6678 A
          Mean   = 1.6162 A
          StdDev = 0.0308 A

       t1 Range  = 0.0379 <-- 0.0549 --> 0.0718
       t2 Range  = 0.0219 <-- 0.0338 --> 0.0457

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  97.474 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 109.031 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 131.320 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 117.921 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  96.991 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  = 104.395 deg; O3  -- O4  = 3 A
       96.991 deg <-- 109.522 deg --> 131.320 deg

O2  -- T2  -- O4  = 110.032 deg; O2  -- O4  = 3 A
O2  -- T2  -- O3  = 110.836 deg; O2  -- O3  = 3 A
O2  -- T2  -- O5  = 103.442 deg; O2  -- O5  = 3 A
O4  -- T2  -- O3  = 107.883 deg; O4  -- O3  = 3 A
O4  -- T2  -- O5  = 118.802 deg; O4  -- O5  = 3 A
O3  -- T2  -- O5  = 105.683 deg; O3  -- O5  = 3 A
       103.442 deg <-- 109.446 deg --> 118.802 deg

        O-T-O SUMMARY
          Range  = 96.9915 deg <--> 131.3204 deg
          Mean   = 109.4842 deg
          StdDev = 9.4035 deg

        O--O SUMMARY
          Range  = 2.3695 A <--> 2.8912 A
          Mean   = 2.6312 A
          StdDev = 0.1542 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  97.744 deg; T2  -- T1  = 4.6264 A
T2  - O1  - T1  - O3  - T2  =  86.233 deg; T2  -- T2  = 4.0954 A
T2  - O1  - T1  - O4  - T2  = 131.696 deg; T2  -- T2  = 5.3296 A
T1  - O2  - T1  - O3  - T2  = 113.890 deg; T1  -- T2  = 5.2595 A
T1  - O2  - T1  - O4  - T2  = 128.726 deg; T1  -- T2  = 5.5235 A
T2  - O3  - T1  - O4  - T2  =  85.980 deg; T2  -- T2  = 4.0779 A

T1  - O2  - T2  - O4  - T1  =  93.767 deg; T1  -- T1  = 4.3736 A
T1  - O2  - T2  - O3  - T1  = 131.696 deg; T1  -- T1  = 5.3296 A
T1  - O2  - T2  - O5  - T2  = 120.289 deg; T1  -- T2  = 5.4348 A
T1  - O4  - T2  - O3  - T1  =  94.020 deg; T1  -- T1  = 4.3741 A
T1  - O4  - T2  - O5  - T2  = 101.334 deg; T1  -- T2  = 4.9528 A
T1  - O3  - T2  - O5  - T2  = 104.620 deg; T1  -- T2  = 4.9526 A

        T-T-T SUMMARY
          Range  = 85.9800 deg <--> 131.6955 deg
          Mean   = 107.4995 deg
          StdDev = 16.8187 deg

        T--T SUMMARY
          Range  = 4.0779 A <--> 5.5235 A
          Mean   = 4.8608 A
          StdDev = 0.5202 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2105 A

T1  -- O2  -- T2  = 131.365 deg ; T1  -- T2   2.9264 A

T1  -- O3  -- T2  = 129.518 deg ; T1  -- T2   2.9145 A

T1  -- O4  -- T2  = 143.801 deg ; T1  -- T2   3.0638 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.3356 A


        T-O-T SUMMARY
          Range  = 129.5184° <--> 180.0000 deg
          Mean   = 152.9370 deg
          StdDev = 23.8609 deg

        T--T SUMMARY
          Range  = 2.9145 A <--> 3.3356 A
          Mean   = 3.0902 A
          StdDev = 0.1720 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 294 318 328 332 325
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 293 319 331 334 331
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000