Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_622174_sR5JEE.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 24.65 T-atoms per nm^3
Material density = 2.460 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6355 Angstrom
T1  -- O4  = 1.6318 Angstrom
T1  -- O2  = 1.6203 Angstrom
T1  -- O3  = 1.6251 Angstrom
      mean = 1.6282 Angstrom
        t1 = 0.030383  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.031842  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6078 Angstrom
T2  -- O3  = 1.6341 Angstrom
T2  -- O6  = 1.6110 Angstrom
T2  -- O4  = 1.6206 Angstrom
      mean = 1.6184 Angstrom
        t1 = 0.041350  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.047796  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6078 A <--> 1.6355 A
          Mean   = 1.6233 A
          StdDev = 0.0100 A

       t1 Range  = 0.0304 <-- 0.0359 --> 0.0414
       t2 Range  = 0.0318 <-- 0.0398 --> 0.0478

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O4  = 108.634 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 116.482 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.949 deg; O1  -- O3  = 3 A
O4  -- T1  -- O2  = 107.413 deg; O4  -- O2  = 3 A
O4  -- T1  -- O3  = 114.580 deg; O4  -- O3  = 3 A
O2  -- T1  -- O3  = 103.993 deg; O2  -- O3  = 3 A
       103.993 deg <-- 109.508 deg --> 116.482 deg

O5  -- T2  -- O3  = 112.796 deg; O5  -- O3  = 3 A
O5  -- T2  -- O6  = 121.025 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 102.674 deg; O5  -- O4  = 3 A
O3  -- T2  -- O6  = 108.266 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 110.627 deg; O3  -- O4  = 3 A
O6  -- T2  -- O4  = 100.277 deg; O6  -- O4  = 2 A
       100.277 deg <-- 109.277 deg --> 121.025 deg

        O-T-O SUMMARY
          Range  = 100.2771 deg <--> 121.0252 deg
          Mean   = 108.5420 deg
          StdDev = 5.3440 deg

        O--O SUMMARY
          Range  = 2.4806 A <--> 2.8019 A
          Mean   = 2.6335 A
          StdDev = 0.0896 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O4  - T2  =  82.626 deg; T1  -- T2  = 4.0959 A
T1  - O1  - T1  - O2  - T2  =  81.756 deg; T1  -- T2  = 4.0271 A
T1  - O1  - T1  - O3  - T1  = 116.482 deg; T1  -- T1  = 5.5368 A
T2  - O4  - T1  - O2  - T2  = 135.603 deg; T2  -- T2  = 5.3561 A
T2  - O4  - T1  - O3  - T1  = 121.858 deg; T2  -- T1  = 5.3872 A
T2  - O2  - T1  - O3  - T1  = 102.288 deg; T2  -- T1  = 4.7600 A

T2  - O5  - T2  - O3  - T1  =  84.492 deg; T2  -- T1  = 4.0959 A
T2  - O5  - T2  - O6  - T2  = 121.025 deg; T2  -- T2  = 5.6038 A
T2  - O5  - T2  - O4  - T1  =  81.884 deg; T2  -- T1  = 4.0271 A
T1  - O3  - T2  - O6  - T2  = 125.092 deg; T1  -- T2  = 5.4035 A
T1  - O3  - T2  - O4  - T1  = 135.603 deg; T1  -- T1  = 5.3561 A
T2  - O6  - T2  - O4  - T1  =  97.876 deg; T2  -- T1  = 4.6357 A

        T-T-T SUMMARY
          Range  = 81.7562 deg <--> 135.6032 deg
          Mean   = 107.7450 deg
          StdDev = 20.7529 deg

        T--T SUMMARY
          Range  = 4.0271 A <--> 5.6038 A
          Mean   = 4.8609 A
          StdDev = 0.6225 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2711 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2407 A

T1  -- O3  -- T2  = 123.012 deg ; T1  -- T2   2.8644 A

T1  -- O4  -- T2  = 127.776 deg ; T1  -- T2   2.9205 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2156 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   3.2221 A


        T-O-T SUMMARY
          Range  = 123.0118° <--> 180.0000 deg
          Mean   = 161.7979 deg
          StdDev = 26.9245 deg

        T--T SUMMARY
          Range  = 2.8644 A <--> 3.2711 A
          Mean   = 3.1224 A
          StdDev = 0.1717 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 40 62 90 122 160 202 250 278 292 310 328 346 366
TD10 = 962
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.10_{12}
Weight = 31

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 40 62 90 122 160 202 250 280 294 310 327 345 367
TD10 = 962
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.10_{12}
Weight = 31

<TD10> = 962.000
Average ring size = 7.7273