Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_603227_x8NWur.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 24.73 T-atoms per nm^3
Material density = 2.468 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6318 Angstrom
T1  -- O2  = 1.6354 Angstrom
T1  -- O3  = 1.6211 Angstrom
T1  -- O4  = 1.6313 Angstrom
      mean = 1.6299 Angstrom
        t1 = 0.029365  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.022464  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6296 Angstrom
T2  -- O6  = 1.6082 Angstrom
T2  -- O3  = 1.6250 Angstrom
T2  -- O4  = 1.6262 Angstrom
      mean = 1.6222 Angstrom
        t1 = 0.031213  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.020100  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6082 A <--> 1.6354 A
          Mean   = 1.6261 A
          StdDev = 0.0082 A

       t1 Range  = 0.0294 <-- 0.0303 --> 0.0312
       t2 Range  = 0.0201 <-- 0.0213 --> 0.0225

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 117.065 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.981 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.326 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 106.055 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 106.056 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 113.597 deg; O3  -- O4  = 3 A
       105.981 deg <-- 109.513 deg --> 117.065 deg

O5  -- T2  -- O6  = 117.537 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  = 107.307 deg; O5  -- O3  = 3 A
O5  -- T2  -- O4  = 107.758 deg; O5  -- O4  = 3 A
O6  -- T2  -- O3  = 106.181 deg; O6  -- O3  = 3 A
O6  -- T2  -- O4  = 103.696 deg; O6  -- O4  = 3 A
O3  -- T2  -- O4  = 114.671 deg; O3  -- O4  = 3 A
       103.696 deg <-- 109.525 deg --> 117.537 deg

        O-T-O SUMMARY
          Range  = 103.6956 deg <--> 117.5372 deg
          Mean   = 108.8117 deg
          StdDev = 4.2456 deg

        O--O SUMMARY
          Range  = 2.5434 A <--> 2.7868 A
          Mean   = 2.6428 A
          StdDev = 0.0703 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 117.065 deg; T1  -- T1  = 5.5735 A
T1  - O1  - T1  - O3  - T2  = 119.978 deg; T1  -- T2  = 5.3424 A
T1  - O1  - T1  - O4  - T2  = 102.658 deg; T1  -- T2  = 4.8295 A
T1  - O2  - T1  - O3  - T2  =  81.084 deg; T1  -- T2  = 4.0128 A
T1  - O2  - T1  - O4  - T2  =  85.054 deg; T1  -- T2  = 4.1799 A
T2  - O3  - T1  - O4  - T2  = 136.937 deg; T2  -- T2  = 5.3978 A

T2  - O5  - T2  - O6  - T2  = 117.537 deg; T2  -- T2  = 5.5371 A
T2  - O5  - T2  - O3  - T1  =  80.968 deg; T2  -- T1  = 4.0128 A
T2  - O5  - T2  - O4  - T1  =  85.348 deg; T2  -- T1  = 4.1799 A
T2  - O6  - T2  - O3  - T1  = 120.923 deg; T2  -- T1  = 5.3305 A
T2  - O6  - T2  - O4  - T1  = 101.629 deg; T2  -- T1  = 4.7411 A
T1  - O3  - T2  - O4  - T1  = 136.937 deg; T1  -- T1  = 5.3978 A

        T-T-T SUMMARY
          Range  = 80.9676 deg <--> 136.9373 deg
          Mean   = 106.2562 deg
          StdDev = 20.9361 deg

        T--T SUMMARY
          Range  = 4.0128 A <--> 5.5735 A
          Mean   = 4.8163 A
          StdDev = 0.6072 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2636 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2709 A

T1  -- O3  -- T2  = 127.230 deg ; T1  -- T2   2.9080 A

T1  -- O4  -- T2  = 125.409 deg ; T1  -- T2   2.8948 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2591 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   3.2164 A


        T-O-T SUMMARY
          Range  = 125.4094° <--> 180.0000 deg
          Mean   = 162.1065 deg
          StdDev = 26.4361 deg

        T--T SUMMARY
          Range  = 2.8948 A <--> 3.2709 A
          Mean   = 3.1355 A
          StdDev = 0.1739 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 40 62 90 122 160 202 250 299 347 390 428 461 491
TD10 = 962
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.10_{12}
Weight = 31

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 21 40 62 90 122 160 202 250 299 347 390 428 461 491
TD10 = 962
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.10_{12}
Weight = 31

<TD10> = 962.000
Average ring size = 7.7273