Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_2_2_542093_g5MK2C.cif"

There are 4 T-atoms per unit cell
There are 8 O-atoms per unit cell

Framework density = 24.49 T-atoms per nm^3
Material density = 2.444 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6168 Angstrom
T1  -- O3  = 1.6246 Angstrom
T1  -- O4  = 1.6224 Angstrom
T1  -- O2  = 1.6150 Angstrom
      mean = 1.6197 Angstrom
        t1 = 0.006319  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001226  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6233 Angstrom
T2  -- O6  = 1.6153 Angstrom
T2  -- O5  = 1.6164 Angstrom
T2  -- O3  = 1.6234 Angstrom
      mean = 1.6196 Angstrom
        t1 = 0.006269  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002414  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6150 A <--> 1.6246 A
          Mean   = 1.6197 A
          StdDev = 0.0040 A

       t1 Range  = 0.0063 <-- 0.0063 --> 0.0063
       t2 Range  = 0.0012 <-- 0.0018 --> 0.0024

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 109.735 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.408 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 109.543 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 109.379 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 109.005 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 109.757 deg; O4  -- O2  = 3 A
       109.005 deg <-- 109.471 deg --> 109.757 deg

O4  -- T2  -- O6  = 109.578 deg; O4  -- O6  = 3 A
O4  -- T2  -- O5  = 109.980 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 109.229 deg; O4  -- O3  = 3 A
O6  -- T2  -- O5  = 109.468 deg; O6  -- O5  = 3 A
O6  -- T2  -- O3  = 109.503 deg; O6  -- O3  = 3 A
O5  -- T2  -- O3  = 109.066 deg; O5  -- O3  = 3 A
       109.066 deg <-- 109.471 deg --> 109.980 deg

        O-T-O SUMMARY
          Range  = 109.0047 deg <--> 109.9799 deg
          Mean   = 109.4679 deg
          StdDev = 0.2891 deg

        O--O SUMMARY
          Range  = 2.6375 A <--> 2.6535 A
          Mean   = 2.6454 A
          StdDev = 0.0051 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T1  = 109.543 deg; T1  -- T1  = 5.2799 A
T1  - O1  - T1  - O4  - T2  = 132.275 deg; T1  -- T2  = 5.6926 A
T1  - O1  - T1  - O2  - T2  =  87.939 deg; T1  -- T2  = 4.3220 A
T1  - O3  - T1  - O4  - T2  = 100.035 deg; T1  -- T2  = 4.7686 A
T1  - O3  - T1  - O2  - T2  = 127.150 deg; T1  -- T2  = 5.5679 A
T2  - O4  - T1  - O2  - T2  = 103.276 deg; T2  -- T2  = 4.6862 A

T2  - O4  - T2  - O6  - T1  =  87.647 deg; T2  -- T1  = 4.3126 A
T2  - O4  - T2  - O5  - T1  = 132.591 deg; T2  -- T1  = 5.6954 A
T2  - O4  - T2  - O3  - T2  = 109.468 deg; T2  -- T2  = 5.2773 A
T1  - O6  - T2  - O5  - T1  = 103.276 deg; T1  -- T1  = 4.6862 A
T1  - O6  - T2  - O3  - T2  = 126.703 deg; T1  -- T2  = 5.5609 A
T1  - O5  - T2  - O3  - T2  = 100.375 deg; T1  -- T2  = 4.7780 A

        T-T-T SUMMARY
          Range  = 87.6474 deg <--> 132.5912 deg
          Mean   = 111.3338 deg
          StdDev = 15.6245 deg

        T--T SUMMARY
          Range  = 4.3126 A <--> 5.6954 A
          Mean   = 5.1021 A
          StdDev = 0.4970 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2336 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2300 A

T1  -- O3  -- T2  = 134.021 deg ; T1  -- T2   2.9901 A

T1  -- O4  -- T2  = 133.885 deg ; T1  -- T2   2.9864 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2329 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   3.2305 A


        T-O-T SUMMARY
          Range  = 133.8846° <--> 180.0000 deg
          Mean   = 164.6510 deg
          StdDev = 22.6720 deg

        T--T SUMMARY
          Range  = 2.9864 A <--> 3.2336 A
          Mean   = 3.1506 A
          StdDev = 0.1199 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 12 27 50 77 112 152 200 252 312 370 417 440 442 433 427
TD10 = 1199
Circuit symbol = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26
Vertex symbol  = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 12 27 50 77 112 152 200 252 312 371 419 440 442 436 426
TD10 = 1199
Circuit symbol = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26
Vertex symbol  = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26

<TD10> = 1199.000
Average ring size = 6.0000