Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_24_2_10353_OFllzP.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 16.29 T-atoms per nm^3
Material density = 1.626 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6161 Angstrom
T1  -- O2  = 1.6203 Angstrom
T1  -- O3  = 1.6182 Angstrom
T1  -- O4  = 1.6202 Angstrom
      mean = 1.6187 Angstrom
        t1 = 0.005555  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000938  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6181 Angstrom
T2  -- O5  = 1.6161 Angstrom
T2  -- O6  = 1.6202 Angstrom
T2  -- O4  = 1.6203 Angstrom
      mean = 1.6187 Angstrom
        t1 = 0.005550  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000913  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6161 A <--> 1.6203 A
          Mean   = 1.6187 A
          StdDev = 0.0017 A

       t1 Range  = 0.0056 <-- 0.0056 --> 0.0056
       t2 Range  = 0.0009 <-- 0.0009 --> 0.0009

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.218 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.745 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.331 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.328 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.515 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.690 deg; O3  -- O4  = 3 A
       109.218 deg <-- 109.471 deg --> 109.745 deg

O3  -- T2  -- O5  = 109.750 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.323 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.689 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.215 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.333 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.517 deg; O6  -- O4  = 3 A
       109.215 deg <-- 109.471 deg --> 109.750 deg

        O-T-O SUMMARY
          Range  = 109.2146 deg <--> 109.7496 deg
          Mean   = 109.4942 deg
          StdDev = 0.1900 deg

        O--O SUMMARY
          Range  = 2.6383 A <--> 2.6477 A
          Mean   = 2.6438 A
          StdDev = 0.0033 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  90.001 deg; T2  -- T1  = 4.4482 A
T2  - O1  - T1  - O3  - T2  =  90.000 deg; T2  -- T2  = 4.3281 A
T2  - O1  - T1  - O4  - T1  = 129.087 deg; T2  -- T1  = 5.5405 A
T1  - O2  - T1  - O3  - T2  = 126.007 deg; T1  -- T2  = 5.5738 A
T1  - O2  - T1  - O4  - T1  = 128.895 deg; T1  -- T1  = 5.6575 A
T2  - O3  - T1  - O4  - T1  =  89.999 deg; T2  -- T1  = 4.3146 A

T1  - O3  - T2  - O5  - T2  = 129.084 deg; T1  -- T2  = 5.5404 A
T1  - O3  - T2  - O6  - T2  =  89.999 deg; T1  -- T2  = 4.4482 A
T1  - O3  - T2  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3281 A
T2  - O5  - T2  - O6  - T2  = 128.895 deg; T2  -- T2  = 5.6575 A
T2  - O5  - T2  - O4  - T1  =  90.001 deg; T2  -- T1  = 4.3146 A
T2  - O6  - T2  - O4  - T1  = 126.010 deg; T2  -- T1  = 5.5740 A

        T-T-T SUMMARY
          Range  = 89.9988 deg <--> 129.0871 deg
          Mean   = 108.9573 deg
          StdDev = 19.0936 deg

        T--T SUMMARY
          Range  = 4.3146 A <--> 5.6575 A
          Mean   = 4.9702 A
          StdDev = 0.6200 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 167.116 deg ; T1  -- T1   3.2117 A

T1  -- O2  -- T1  = 141.421 deg ; T1  -- T1   3.0587 A

T1  -- O3  -- T2  = 143.966 deg ; T1  -- T2   3.0776 A

T1  -- O4  -- T2  = 139.796 deg ; T1  -- T2   3.0431 A

T2  -- O5  -- T2  = 167.102 deg ; T2  -- T2   3.2118 A

T2  -- O6  -- T2  = 141.427 deg ; T2  -- T2   3.0586 A


        T-O-T SUMMARY
          Range  = 139.7958° <--> 167.1160 deg
          Mean   = 150.1379 deg
          StdDev = 12.1897 deg

        T--T SUMMARY
          Range  = 3.0431 A <--> 3.2118 A
          Mean   = 3.1102 A
          StdDev = 0.0732 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 312 361 414 472
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 312 361 414 472
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

<TD10> = 726.000
Average ring size = 5.6000