Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_24_1_7_oSxdGf.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.7789 Angstrom
T1  -- O1  = 1.4531 Angstrom
T1  -- O2  = 1.7652 Angstrom
T1  -- O3  = 1.5450 Angstrom
T1  -- O1  = 2.0121 Angstrom
      mean = 1.7109 Angstrom

        T-O SUMMARY
          Range  = 1.4531 A <--> 2.0121 A
          Mean   = 1.7109 A
          StdDev = 0.1986 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  93.216 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  = 106.004 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  91.441 deg; O1  -- O3  = 2 A
O1  -- T1  -- O1  = 122.227 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  =  89.052 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 158.992 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  =  81.408 deg; O1  -- O1  = 2 A
O2  -- T1  -- O3  =  69.980 deg; O2  -- O3  = 2 A
O2  -- T1  -- O1  = 131.134 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 113.063 deg; O3  -- O1  = 3 A
       69.980 deg <-- 105.652 deg --> 158.992 deg

        O-T-O SUMMARY
          Range  = 69.9803 deg <--> 158.9919 deg
          Mean   = 107.5291 deg
          StdDev = 24.5426 deg

        O--O SUMMARY
          Range  = 1.9067 A <--> 3.4406 A
          Mean   = 2.7141 A
          StdDev = 0.4579 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  55.880 deg; T1  -- T1  = 2.4469 A
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 2.9557 A
T1  - O1  - T1  - O3  - T1  =  55.880 deg; T1  -- T1  = 2.4469 A
T1  - O1  - T1  - O1  - T1  =  90.000 deg; T1  -- T1  = 2.9557 A
T1  - O1  - T1  - O2  - T1  =  34.120 deg; T1  -- T1  = 1.6580 A
T1  - O1  - T1  - O3  - T1  = 102.886 deg; T1  -- T1  = 4.6227 A
T1  - O1  - T1  - O1  - T1  = 130.500 deg; T1  -- T1  = 4.9110 A
T1  - O2  - T1  - O3  - T1  = 130.500 deg; T1  -- T1  = 4.9110 A
T1  - O2  - T1  - O1  - T1  = 141.674 deg; T1  -- T1  = 4.6227 A
T1  - O3  - T1  - O1  - T1  =  34.120 deg; T1  -- T1  = 1.6580 A

        T-T-T SUMMARY
          Range  = 34.1202 deg <--> 141.6735 deg
          Mean   = 84.2431 deg
          StdDev = 38.0249 deg

        T--T SUMMARY
          Range  = 1.6580 A <--> 4.9110 A
          Mean   = 3.2351 A
          StdDev = 1.2410 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  60.737 deg ; T1  -- T1   1.6580 A
T1  -- O1  -- T1  = 102.285 deg ; T1  -- T1   2.9557 A
T1  -- O1  -- T1  =  88.308 deg ; T1  -- T1   2.4469 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.5304 A

T1  -- O3  -- T1  = 104.725 deg ; T1  -- T1   2.4469 A


        T-O-T SUMMARY
          Range  = 60.7369° <--> 180.0000 deg
          Mean   = 107.2110 deg
          StdDev = 40.1174 deg

        T--T SUMMARY
          Range  = 1.6580 A <--> 3.5304 A
          Mean   = 2.6076 A
          StdDev = 0.6286 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.2677 A
O1  -- O1  = 2.2993 A
O2  -- O3  = 1.9067 A
O2  -- O3  = 1.9067 A

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 oxygen-bridged T-atoms within 3.50 A
  T1  -- T1  = 1.6580 Angstrom
  T1  -- T1  = 2.9557 Angstrom
  T1  -- T1  = 2.4469 Angstrom
  T1  -- T1  = 2.9557 Angstrom
  T1  -- T1  = 2.4469 Angstrom