Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_24_1_6_j0BhwS.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 2.0315 Angstrom
T1  -- O2  = 1.8030 Angstrom
T1  -- O3  = 1.5897 Angstrom
T1  -- O1  = 1.8232 Angstrom
T1  -- O1  = 1.6116 Angstrom
      mean = 1.7718 Angstrom

        T-O SUMMARY
          Range  = 1.5897 A <--> 2.0315 A
          Mean   = 1.7718 A
          StdDev = 0.1632 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 125.123 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 118.723 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 121.849 deg; O1  -- O1  = 3 A
O1  -- T1  -- O1  =  77.611 deg; O1  -- O1  = 2 A
O2  -- T1  -- O3  =  79.397 deg; O2  -- O3  = 2 A
O2  -- T1  -- O1  = 111.766 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  =  88.498 deg; O2  -- O1  = 2 A
O3  -- T1  -- O1  =  80.248 deg; O3  -- O1  = 2 A
O3  -- T1  -- O1  = 163.364 deg; O3  -- O1  = 3 A
O1  -- T1  -- O1  =  93.916 deg; O1  -- O1  = 3 A
       77.611 deg <-- 106.050 deg --> 163.364 deg

        O-T-O SUMMARY
          Range  = 77.6108 deg <--> 163.3637 deg
          Mean   = 107.4524 deg
          StdDev = 26.0418 deg

        O--O SUMMARY
          Range  = 2.1733 A <--> 3.4048 A
          Mean   = 2.7968 A
          StdDev = 0.4638 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 134.398 deg; T1  -- T1  = 5.2823 A
T1  - O1  - T1  - O3  - T1  =  34.203 deg; T1  -- T1  = 1.7343 A
T1  - O1  - T1  - O1  - T1  =  86.708 deg; T1  -- T1  = 3.0801 A
T1  - O1  - T1  - O1  - T1  = 147.082 deg; T1  -- T1  = 4.8870 A
T1  - O2  - T1  - O3  - T1  = 104.992 deg; T1  -- T1  = 4.8870 A
T1  - O2  - T1  - O1  - T1  =  59.089 deg; T1  -- T1  = 2.6470 A
T1  - O2  - T1  - O1  - T1  =  34.204 deg; T1  -- T1  = 1.7343 A
T1  - O3  - T1  - O1  - T1  =  52.526 deg; T1  -- T1  = 2.4485 A
T1  - O3  - T1  - O1  - T1  = 133.574 deg; T1  -- T1  = 5.0871 A
T1  - O1  - T1  - O1  - T1  =  93.270 deg; T1  -- T1  = 3.0801 A

        T-T-T SUMMARY
          Range  = 34.2035 deg <--> 147.0822 deg
          Mean   = 87.1105 deg
          StdDev = 41.0126 deg

        T--T SUMMARY
          Range  = 1.7343 A <--> 5.2823 A
          Mean   = 3.4131 A
          StdDev = 1.3438 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 105.955 deg ; T1  -- T1   3.0801 A
T1  -- O1  -- T1  =  83.606 deg ; T1  -- T1   2.4485 A
T1  -- O1  -- T1  =  60.279 deg ; T1  -- T1   1.7343 A

T1  -- O2  -- T1  = 157.220 deg ; T1  -- T1   3.5350 A

T1  -- O3  -- T1  = 112.727 deg ; T1  -- T1   2.6470 A


        T-O-T SUMMARY
          Range  = 60.2787° <--> 157.2203 deg
          Mean   = 103.9574 deg
          StdDev = 32.7847 deg

        T--T SUMMARY
          Range  = 1.7343 A <--> 3.5350 A
          Mean   = 2.6890 A
          StdDev = 0.6143 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O3  = 2.2066 A
O2  -- O3  = 2.1733 A
O2  -- O3  = 2.1733 A

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 oxygen-bridged T-atoms within 3.50 A
  T1  -- T1  = 2.6470 Angstrom
  T1  -- T1  = 3.0801 Angstrom
  T1  -- T1  = 3.0801 Angstrom
  T1  -- T1  = 1.7343 Angstrom
  T1  -- T1  = 2.4485 Angstrom