Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_23_2_32459_AQnMJI.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 21.42 T-atoms per nm^3
Material density = 2.137 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6215 Angstrom
T1  -- O2  = 1.6222 Angstrom
T1  -- O3  = 1.6201 Angstrom
T1  -- O4  = 1.6212 Angstrom
      mean = 1.6213 Angstrom
        t1 = 0.007025  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000548  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6214 Angstrom
T2  -- O4  = 1.6209 Angstrom
T2  -- O5  = 1.6194 Angstrom
T2  -- O3  = 1.6206 Angstrom
      mean = 1.6206 Angstrom
        t1 = 0.006644  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001144  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6194 A <--> 1.6222 A
          Mean   = 1.6209 A
          StdDev = 0.0008 A

       t1 Range  = 0.0066 <-- 0.0068 --> 0.0070
       t2 Range  = 0.0005 <-- 0.0008 --> 0.0011

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.555 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.429 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.611 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.362 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.433 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.437 deg; O3  -- O4  = 3 A
       109.362 deg <-- 109.471 deg --> 109.611 deg

O2  -- T2  -- O4  = 109.510 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.736 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 109.439 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 109.239 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 109.417 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 109.485 deg; O5  -- O3  = 3 A
       109.239 deg <-- 109.471 deg --> 109.736 deg

        O-T-O SUMMARY
          Range  = 109.2394 deg <--> 109.7364 deg
          Mean   = 109.4712 deg
          StdDev = 0.1206 deg

        O--O SUMMARY
          Range  = 2.6419 A <--> 2.6504 A
          Mean   = 2.6469 A
          StdDev = 0.0023 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  89.963 deg; T2  -- T2  = 4.2701 A
T2  - O1  - T1  - O3  - T1  = 150.560 deg; T2  -- T1  = 5.8450 A
T2  - O1  - T1  - O4  - T2  =  89.952 deg; T2  -- T2  = 4.2701 A
T2  - O2  - T1  - O3  - T1  = 116.803 deg; T2  -- T1  = 5.1735 A
T2  - O2  - T1  - O4  - T2  = 110.832 deg; T2  -- T2  = 4.9990 A
T1  - O3  - T1  - O4  - T2  =  91.408 deg; T1  -- T2  = 4.3478 A

T1  - O2  - T2  - O4  - T1  =  90.037 deg; T1  -- T1  = 4.2733 A
T1  - O2  - T2  - O5  - T2  = 114.728 deg; T1  -- T2  = 5.1353 A
T1  - O2  - T2  - O3  - T1  =  90.048 deg; T1  -- T1  = 4.2733 A
T1  - O4  - T2  - O5  - T2  = 134.737 deg; T1  -- T2  = 5.6572 A
T1  - O4  - T2  - O3  - T1  = 110.832 deg; T1  -- T1  = 4.9990 A
T2  - O5  - T2  - O3  - T1  = 106.590 deg; T2  -- T1  = 4.9135 A

        T-T-T SUMMARY
          Range  = 89.9523 deg <--> 150.5596 deg
          Mean   = 108.0408 deg
          StdDev = 18.8920 deg

        T--T SUMMARY
          Range  = 4.2701 A <--> 5.8450 A
          Mean   = 4.8464 A
          StdDev = 0.5402 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 139.069 deg ; T1  -- T1   3.0383 A

T1  -- O2  -- T2  = 135.783 deg ; T1  -- T2   3.0051 A

T1  -- O3  -- T2  = 139.017 deg ; T1  -- T2   3.0357 A

T1  -- O4  -- T2  = 138.945 deg ; T1  -- T2   3.0363 A

T2  -- O5  -- T2  = 145.451 deg ; T2  -- T2   3.0928 A


        T-O-T SUMMARY
          Range  = 135.7831° <--> 145.4509 deg
          Mean   = 139.6529 deg
          StdDev = 3.1974 deg

        T--T SUMMARY
          Range  = 3.0051 A <--> 3.0928 A
          Mean   = 3.0416 A
          StdDev = 0.0288 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{5}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{5}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

<TD10> = 833.000
Average ring size = 5.3333