Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_22_2_31993_BlmBOl.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 17.43 T-atoms per nm^3
Material density = 1.739 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6187 Angstrom
T1  -- O2  = 1.6186 Angstrom
T1  -- O3  = 1.6178 Angstrom
T1  -- O4  = 1.6100 Angstrom
      mean = 1.6163 Angstrom
        t1 = 0.004214  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001143  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6100 Angstrom
T2  -- O5  = 1.6187 Angstrom
T2  -- O6  = 1.6186 Angstrom
T2  -- O7  = 1.6178 Angstrom
      mean = 1.6163 Angstrom
        t1 = 0.004214  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001197  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6100 A <--> 1.6187 A
          Mean   = 1.6163 A
          StdDev = 0.0036 A

       t1 Range  = 0.0042 <-- 0.0042 --> 0.0042
       t2 Range  = 0.0011 <-- 0.0012 --> 0.0012

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.783 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.138 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.500 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.137 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.501 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.767 deg; O3  -- O4  = 3 A
       109.137 deg <-- 109.471 deg --> 109.783 deg

O4  -- T2  -- O5  = 109.500 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.501 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 109.767 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.783 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.135 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.140 deg; O6  -- O7  = 3 A
       109.135 deg <-- 109.471 deg --> 109.783 deg

        O-T-O SUMMARY
          Range  = 109.1352 deg <--> 109.7831 deg
          Mean   = 109.5106 deg
          StdDev = 0.2329 deg

        O--O SUMMARY
          Range  = 2.6367 A <--> 2.6483 A
          Mean   = 2.6389 A
          StdDev = 0.0036 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  97.556 deg; T1  -- T2  = 4.8008 A
T1  - O1  - T1  - O3  - T1  = 130.185 deg; T1  -- T1  = 5.6860 A
T1  - O1  - T1  - O4  - T1  = 130.185 deg; T1  -- T1  = 5.6860 A
T2  - O2  - T1  - O3  - T1  = 108.699 deg; T2  -- T1  = 5.1415 A
T2  - O2  - T1  - O4  - T1  = 108.700 deg; T2  -- T1  = 5.1415 A
T1  - O3  - T1  - O4  - T1  =  80.370 deg; T1  -- T1  = 4.0092 A

T1  - O4  - T2  - O5  - T2  = 108.699 deg; T1  -- T2  = 5.1415 A
T1  - O4  - T2  - O6  - T2  = 108.700 deg; T1  -- T2  = 5.1415 A
T1  - O4  - T2  - O7  - T2  =  97.556 deg; T1  -- T2  = 4.8008 A
T2  - O5  - T2  - O6  - T2  =  80.370 deg; T2  -- T2  = 4.0092 A
T2  - O5  - T2  - O7  - T2  = 130.185 deg; T2  -- T2  = 5.6860 A
T2  - O6  - T2  - O7  - T2  = 130.185 deg; T2  -- T2  = 5.6860 A

        T-T-T SUMMARY
          Range  = 80.3701 deg <--> 130.1853 deg
          Mean   = 108.0889 deg
          StdDev = 16.8608 deg

        T--T SUMMARY
          Range  = 4.0092 A <--> 5.6860 A
          Mean   = 5.0472 A
          StdDev = 0.5556 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 147.335 deg ; T1  -- T1   3.1067 A

T1  -- O2  -- T1  = 147.335 deg ; T1  -- T1   3.1067 A

T1  -- O3  -- T1  = 155.577 deg ; T1  -- T1   3.1624 A

T1  -- O4  -- T2  = 180.000 deg ; T1  -- T2   3.2201 A

T2  -- O5  -- T2  = 147.329 deg ; T2  -- T2   3.1067 A

T2  -- O6  -- T2  = 147.342 deg ; T2  -- T2   3.1067 A

T2  -- O7  -- T2  = 155.577 deg ; T2  -- T2   3.1624 A


        T-O-T SUMMARY
          Range  = 147.3286° <--> 180.0000 deg
          Mean   = 154.3563 deg
          StdDev = 11.1194 deg

        T--T SUMMARY
          Range  = 3.1067 A <--> 3.2201 A
          Mean   = 3.1388 A
          StdDev = 0.0413 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 23 44 67 95 134 168 215 271 320 380 454 520 599 682
TD10 = 1033
Circuit symbol = 4.5_{2}.5.8_{4}.5.8_{4}
Weight = 28
Vertex symbol  = 4.5_{2}.5.8_{2}.5.8_{2}
Weight = 28

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 23 44 67 95 134 168 215 271 320 380 454 520 599 682
TD10 = 1033
Circuit symbol = 4.5_{2}.5.8_{4}.5.8_{4}
Weight = 28
Vertex symbol  = 4.5_{2}.5.8_{2}.5.8_{2}
Weight = 28

<TD10> = 1033.000
Average ring size = 5.8065