Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_22_2_211365_guNnlJ.cif"

There are 20 T-atoms per unit cell
There are 40 O-atoms per unit cell

Framework density = 15.66 T-atoms per nm^3
Material density = 1.562 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6213 Angstrom
T1  -- O2  = 1.6004 Angstrom
T1  -- O3  = 1.6214 Angstrom
T1  -- O4  = 1.6321 Angstrom
      mean = 1.6188 Angstrom
        t1 = 0.022043  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013814  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6264 Angstrom
T2  -- O4  = 1.6264 Angstrom
T2  -- O4  = 1.6264 Angstrom
T2  -- O4  = 1.6264 Angstrom
      mean = 1.6264 Angstrom
        t1 = 0.010286  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001354  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6004 A <--> 1.6321 A
          Mean   = 1.6203 A
          StdDev = 0.0108 A

       t1 Range  = 0.0103 <-- 0.0162 --> 0.0220
       t2 Range  = 0.0014 <-- 0.0076 --> 0.0138

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.783 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.844 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 112.574 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.691 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 103.909 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 112.757 deg; O3  -- O4  = 3 A
       103.909 deg <-- 109.426 deg --> 112.757 deg

O4  -- T2  -- O4  = 109.199 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 109.739 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 109.477 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 109.476 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 109.739 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 109.199 deg; O4  -- O4  = 3 A
       109.199 deg <-- 109.471 deg --> 109.739 deg

        O-T-O SUMMARY
          Range  = 103.9089 deg <--> 112.7565 deg
          Mean   = 109.4978 deg
          StdDev = 2.2376 deg

        O--O SUMMARY
          Range  = 2.5457 A <--> 2.7092 A
          Mean   = 2.6516 A
          StdDev = 0.0424 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  83.008 deg; T1  -- T1  = 4.1613 A
T1  - O1  - T1  - O3  - T2  = 129.411 deg; T1  -- T2  = 5.5260 A
T1  - O1  - T1  - O4  - T1  = 131.307 deg; T1  -- T1  = 5.6043 A
T1  - O2  - T1  - O3  - T2  = 129.659 deg; T1  -- T2  = 5.5247 A
T1  - O2  - T1  - O4  - T1  = 131.701 deg; T1  -- T1  = 5.6060 A
T2  - O3  - T1  - O4  - T1  =  59.558 deg; T2  -- T1  = 2.9678 A

T1  - O4  - T2  - O4  - T1  = 137.834 deg; T1  -- T1  = 5.5384 A
T1  - O4  - T2  - O4  - T1  =  60.885 deg; T1  -- T1  = 3.0074 A
T1  - O4  - T2  - O4  - T1  = 138.190 deg; T1  -- T1  = 5.5450 A
T1  - O4  - T2  - O4  - T1  = 138.190 deg; T1  -- T1  = 5.5450 A
T1  - O4  - T2  - O4  - T1  =  60.885 deg; T1  -- T1  = 3.0074 A
T1  - O4  - T2  - O4  - T1  = 137.834 deg; T1  -- T1  = 5.5384 A

        T-T-T SUMMARY
          Range  = 59.5577 deg <--> 138.1904 deg
          Mean   = 111.1832 deg
          StdDev = 34.1383 deg

        T--T SUMMARY
          Range  = 2.9678 A <--> 5.6060 A
          Mean   = 4.7586 A
          StdDev = 1.1578 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 151.596 deg ; T1  -- T1   3.1435 A

T1  -- O2  -- T1  = 139.972 deg ; T1  -- T1   3.0074 A

T1  -- O3  -- T1  = 150.511 deg ; T1  -- T1   3.1360 A

T1  -- O4  -- T2  = 131.235 deg ; T1  -- T2   2.9678 A


        T-O-T SUMMARY
          Range  = 131.2351° <--> 151.5965 deg
          Mean   = 143.3287 deg
          StdDev = 8.3945 deg

        T--T SUMMARY
          Range  = 2.9678 A <--> 3.1435 A
          Mean   = 3.0637 A
          StdDev = 0.0780 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 40 55 80 115 138 183 229 260 328 382 421 515 574
TD10 = 873
Circuit symbol = 3.4.8.9_{5}.8.9_{5}
Weight = 31
Vertex symbol  = 3.4.8.9_{4}.8.9_{4}
Weight = 31

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 8 20 40 52 82 116 132 184 236 252 322 396 416 500 592
TD10 = 875
Circuit symbol = 3.3.9_{4}.9_{4}.9_{4}.9_{4}
Weight = 37
Vertex symbol  = 3.3.9_{4}.9_{4}.9_{4}.9_{4}
Weight = 37

<TD10> = 873.400
Average ring size = 7.0714