Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_9843119_uQsuHa.cif"

There are 336 T-atoms per unit cell
There are 672 O-atoms per unit cell

Framework density = 2.54 T-atoms per nm^3
Material density = 0.254 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5941 Angstrom
T1  -- O2  = 1.6420 Angstrom
T1  -- O3  = 1.7329 Angstrom
T1  -- O4  = 1.6426 Angstrom
      mean = 1.6529 Angstrom
        t1 = 0.060677  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037212  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6984 Angstrom
T2  -- O5  = 1.7055 Angstrom
T2  -- O6  = 1.7047 Angstrom
T2  -- O7  = 1.5595 Angstrom
      mean = 1.6670 Angstrom
        t1 = 0.085585  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.068925  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6410 Angstrom
T3  -- O8  = 1.6625 Angstrom
T3  -- O9  = 1.7011 Angstrom
T3  -- O4  = 1.6410 Angstrom
      mean = 1.6614 Angstrom
        t1 = 0.041912  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019752  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.5899 Angstrom
T4  -- O10 = 1.4841 Angstrom
T4  -- O11 = 1.6102 Angstrom
T4  -- O7  = 1.5899 Angstrom
      mean = 1.5685 Angstrom
        t1 = 0.075030  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.056367  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.6523 Angstrom
T5  -- O12 = 1.5524 Angstrom
T5  -- O13 = 1.6574 Angstrom
T5  -- O13 = 1.6574 Angstrom
      mean = 1.6299 Angstrom
        t1 = 0.070781  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.066913  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4841 A <--> 1.7329 A
          Mean   = 1.6428 A
          StdDev = 0.0600 A

       t1 Range  = 0.0419 <-- 0.0668 --> 0.0856
       t2 Range  = 0.0198 <-- 0.0498 --> 0.0689

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.648 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 104.477 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 105.350 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 117.395 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 101.363 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 118.843 deg; O3  -- O4  = 3 A
       101.363 deg <-- 109.346 deg --> 118.843 deg

O3  -- T2  -- O5  = 113.493 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 117.358 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  =  92.282 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 118.688 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.185 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 101.781 deg; O6  -- O7  = 3 A
       92.282 deg <-- 108.631 deg --> 118.688 deg

O4  -- T3  -- O8  = 106.295 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 110.963 deg; O4  -- O9  = 3 A
O4  -- T3  -- O4  = 107.220 deg; O4  -- O4  = 3 A
O8  -- T3  -- O9  = 114.687 deg; O8  -- O9  = 3 A
O8  -- T3  -- O4  = 106.295 deg; O8  -- O4  = 3 A
O9  -- T3  -- O4  = 110.963 deg; O9  -- O4  = 3 A
       106.295 deg <-- 109.404 deg --> 114.687 deg

O7  -- T4  -- O10 =  96.759 deg; O7  -- O10 = 2 A
O7  -- T4  -- O11 = 114.235 deg; O7  -- O11 = 3 A
O7  -- T4  -- O7  = 117.566 deg; O7  -- O7  = 3 A
O10 -- T4  -- O11 = 114.501 deg; O10 -- O11 = 3 A
O10 -- T4  -- O7  =  96.759 deg; O10 -- O7  = 2 A
O11 -- T4  -- O7  = 114.235 deg; O11 -- O7  = 3 A
       96.759 deg <-- 109.009 deg --> 117.566 deg

O9  -- T5  -- O12 = 100.065 deg; O9  -- O12 = 2 A
O9  -- T5  -- O13 = 118.815 deg; O9  -- O13 = 3 A
O9  -- T5  -- O13 = 118.815 deg; O9  -- O13 = 3 A
O12 -- T5  -- O13 =  99.782 deg; O12 -- O13 = 2 A
O12 -- T5  -- O13 =  99.782 deg; O12 -- O13 = 2 A
O13 -- T5  -- O13 = 113.713 deg; O13 -- O13 = 3 A
       99.782 deg <-- 108.495 deg --> 118.815 deg

        O-T-O SUMMARY
          Range  = 92.2823 deg <--> 118.8425 deg
          Mean   = 108.5632 deg
          StdDev = 7.6120 deg

        O--O SUMMARY
          Range  = 2.2991 A <--> 2.9336 A
          Mean   = 2.6554 A
          StdDev = 0.1778 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 117.474 deg; T1  -- T2  = 5.1407 A
T1  - O1  - T1  - O3  - T3  =  56.916 deg; T1  -- T3  = 2.8016 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3248 A
T2  - O2  - T1  - O3  - T3  = 172.336 deg; T2  -- T3  = 5.7437 A
T2  - O2  - T1  - O4  - T1  =  92.499 deg; T2  -- T1  = 4.3438 A
T3  - O3  - T1  - O4  - T1  =  92.709 deg; T3  -- T1  = 4.2435 A

T1  - O3  - T2  - O5  - T2  = 131.104 deg; T1  -- T2  = 5.5604 A
T1  - O3  - T2  - O6  - T4  =  79.151 deg; T1  -- T4  = 3.8176 A
T1  - O3  - T2  - O7  - T2  =  87.501 deg; T1  -- T2  = 4.3438 A
T2  - O5  - T2  - O6  - T4  =  82.209 deg; T2  -- T4  = 4.0696 A
T2  - O5  - T2  - O7  - T2  = 135.000 deg; T2  -- T2  = 5.9756 A
T4  - O6  - T2  - O7  - T2  =  84.456 deg; T4  -- T2  = 4.2738 A

T1  - O4  - T3  - O8  - T3  =  87.291 deg; T1  -- T3  = 4.2435 A
T1  - O4  - T3  - O9  - T5  = 146.186 deg; T1  -- T5  = 5.5378 A
T1  - O4  - T3  - O4  - T1  =  66.169 deg; T1  -- T1  = 3.0586 A
T3  - O8  - T3  - O9  - T5  =  85.814 deg; T3  -- T5  = 4.3020 A
T3  - O8  - T3  - O4  - T1  =  87.291 deg; T3  -- T1  = 4.2435 A
T5  - O9  - T3  - O4  - T1  = 146.186 deg; T5  -- T1  = 5.5378 A

T2  - O7  - T4  - O10 - T4  =  95.544 deg; T2  -- T4  = 4.2738 A
T2  - O7  - T4  - O11 - T4  =  97.791 deg; T2  -- T4  = 4.0696 A
T2  - O7  - T4  - O7  - T2  = 144.596 deg; T2  -- T2  = 5.7852 A
T4  - O10 - T4  - O11 - T4  = 135.000 deg; T4  -- T4  = 4.6752 A
T4  - O10 - T4  - O7  - T2  =  95.544 deg; T4  -- T2  = 4.2738 A
T4  - O11 - T4  - O7  - T2  =  97.791 deg; T4  -- T2  = 4.0696 A

T3  - O9  - T5  - O12 - T5  =  94.186 deg; T3  -- T5  = 4.3020 A
T3  - O9  - T5  - O13 - T5  = 134.437 deg; T3  -- T5  = 5.2686 A
T3  - O9  - T5  - O13 - T5  = 134.437 deg; T3  -- T5  = 5.2686 A
T5  - O12 - T5  - O13 - T5  =  58.049 deg; T5  -- T5  = 2.7273 A
T5  - O12 - T5  - O13 - T5  =  58.049 deg; T5  -- T5  = 2.7273 A
T5  - O13 - T5  - O13 - T5  =  63.901 deg; T5  -- T5  = 2.8865 A

        T-T-T SUMMARY
          Range  = 56.9156 deg <--> 172.3365 deg
          Mean   = 102.3874 deg
          StdDev = 30.0140 deg

        T--T SUMMARY
          Range  = 2.7273 A <--> 5.9756 A
          Mean   = 4.4459 A
          StdDev = 0.9034 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 147.090 deg ; T1  -- T1   3.0576 A

T1  -- O2  -- T1  = 137.298 deg ; T1  -- T1   3.0586 A

T1  -- O3  -- T2  = 118.898 deg ; T1  -- T2   2.9550 A

T1  -- O4  -- T3  = 117.121 deg ; T1  -- T3   2.8016 A

T2  -- O5  -- T2  = 152.795 deg ; T2  -- T2   3.3153 A

T2  -- O6  -- T2  = 135.214 deg ; T2  -- T2   3.1523 A

T2  -- O7  -- T4  = 149.194 deg ; T2  -- T4   3.0364 A

T3  -- O8  -- T3  = 175.541 deg ; T3  -- T3   3.3224 A

T3  -- O9  -- T5  = 125.861 deg ; T3  -- T5   2.9861 A

T4  -- O10 -- T4  = 133.644 deg ; T4  -- T4   2.7286 A

T4  -- O11 -- T4  =  92.646 deg ; T4  -- T4   2.3291 A

T5  -- O12 -- T5  = 136.767 deg ; T5  -- T5   2.8865 A

T5  -- O13 -- T5  = 110.725 deg ; T5  -- T5   2.7273 A


        T-O-T SUMMARY
          Range  = 92.6459° <--> 175.5408 deg
          Mean   = 134.5202 deg
          StdDev = 18.1860 deg

        T--T SUMMARY
          Range  = 2.3291 A <--> 3.3224 A
          Mean   = 2.9867 A
          StdDev = 0.2299 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O7  -- O10 = 2.2991 A
T4  -- T4  = 2.7286 Angstrom
T4  -- T4  = 2.3291 Angstrom
T5  -- T5  = 2.7273 Angstrom
T5  -- T5  = 2.7273 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 10 12 16 15 14 19 22 24 28 34 42 40 40 48
TD10 = 144
Circuit symbol = 3.4.4.5.4.6_{2}
Weight = 10
Vertex symbol  = 3.4.4.5.4.*
Weight = 10

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 9 13 15 14 13 13 16 24 32 38 40 36 34 34 42
TD10 = 154
Circuit symbol = 4.4.4.7_{2}.5.6
Weight = 11
Vertex symbol  = 4.4.4.*.5.8
Weight = 15

T3 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 7 12 15 17 19 19 19 18 20 30 38 48 54 54
TD10 = 138
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.*.4.*
Weight = 8

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 8 11 12 12 10 11 13 16 24 32 38 40 36 34 34
TD10 = 122
Circuit symbol = 4.4.4.4.5.6_{2}
Weight = 11
Vertex symbol  = 4.4.4.4.5.8
Weight = 16

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 5 8 9 14 21 23 19 15 15 20 24 36 52 62 60
TD10 = 134
Circuit symbol = 3.4.3.5.3.5
Weight = 6
Vertex symbol  = 3.4.3.*.3.*
Weight = 6

<TD10> = 141.429
Average ring size = 4.0597