Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_9799297_gQBpcN.cif"

There are 336 T-atoms per unit cell
There are 672 O-atoms per unit cell

Framework density = 1.60 T-atoms per nm^3
Material density = 0.160 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6624 Angstrom
T1  -- O2  = 1.6228 Angstrom
T1  -- O3  = 1.5951 Angstrom
T1  -- O4  = 1.6401 Angstrom
      mean = 1.6301 Angstrom
        t1 = 0.054826  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037220  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.5365 Angstrom
T2  -- O6  = 1.6967 Angstrom
T2  -- O7  = 1.6391 Angstrom
T2  -- O8  = 1.6441 Angstrom
      mean = 1.6291 Angstrom
        t1 = 0.092805  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.058998  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6460 Angstrom
T3  -- O9  = 1.6677 Angstrom
T3  -- O10 = 1.6336 Angstrom
T3  -- O4  = 1.6460 Angstrom
      mean = 1.6483 Angstrom
        t1 = 0.025331  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005629  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6220 Angstrom
T4  -- O10 = 1.6281 Angstrom
T4  -- O11 = 1.6360 Angstrom
T4  -- O7  = 1.6220 Angstrom
      mean = 1.6270 Angstrom
        t1 = 0.025819  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019174  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O8  = 1.6702 Angstrom
T5  -- O11 = 1.6597 Angstrom
T5  -- O12 = 1.6084 Angstrom
T5  -- O8  = 1.6702 Angstrom
      mean = 1.6522 Angstrom
        t1 = 0.034120  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014171  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5365 A <--> 1.6967 A
          Mean   = 1.6351 A
          StdDev = 0.0367 A

       t1 Range  = 0.0253 <-- 0.0466 --> 0.0928
       t2 Range  = 0.0056 <-- 0.0270 --> 0.0590

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.600 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.228 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 123.658 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.504 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.055 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  97.612 deg; O3  -- O4  = 2 A
       97.612 deg <-- 109.276 deg --> 123.658 deg

O5  -- T2  -- O6  = 102.017 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 110.177 deg; O5  -- O7  = 3 A
O5  -- T2  -- O8  =  88.616 deg; O5  -- O8  = 2 A
O6  -- T2  -- O7  = 112.157 deg; O6  -- O7  = 3 A
O6  -- T2  -- O8  = 129.757 deg; O6  -- O8  = 3 A
O7  -- T2  -- O8  = 109.470 deg; O7  -- O8  = 3 A
       88.616 deg <-- 108.699 deg --> 129.757 deg

O4  -- T3  -- O9  = 109.506 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 110.124 deg; O4  -- O10 = 3 A
O4  -- T3  -- O4  = 106.805 deg; O4  -- O4  = 3 A
O9  -- T3  -- O10 = 110.693 deg; O9  -- O10 = 3 A
O9  -- T3  -- O4  = 109.506 deg; O9  -- O4  = 3 A
O10 -- T3  -- O4  = 110.124 deg; O10 -- O4  = 3 A
       106.805 deg <-- 109.460 deg --> 110.693 deg

O7  -- T4  -- O10 = 112.808 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 106.116 deg; O7  -- O11 = 3 A
O7  -- T4  -- O7  = 104.672 deg; O7  -- O7  = 3 A
O10 -- T4  -- O11 = 113.605 deg; O10 -- O11 = 3 A
O10 -- T4  -- O7  = 112.808 deg; O10 -- O7  = 3 A
O11 -- T4  -- O7  = 106.116 deg; O11 -- O7  = 3 A
       104.672 deg <-- 109.354 deg --> 113.605 deg

O8  -- T5  -- O11 = 106.348 deg; O8  -- O11 = 3 A
O8  -- T5  -- O12 = 110.022 deg; O8  -- O12 = 3 A
O8  -- T5  -- O8  = 115.556 deg; O8  -- O8  = 3 A
O11 -- T5  -- O12 = 108.187 deg; O11 -- O12 = 3 A
O11 -- T5  -- O8  = 106.348 deg; O11 -- O8  = 3 A
O12 -- T5  -- O8  = 110.022 deg; O12 -- O8  = 3 A
       106.348 deg <-- 109.414 deg --> 115.556 deg

        O-T-O SUMMARY
          Range  = 88.6157 deg <--> 129.7567 deg
          Mean   = 109.3133 deg
          StdDev = 7.2135 deg

        O--O SUMMARY
          Range  = 2.2230 A <--> 3.0249 A
          Mean   = 2.6684 A
          StdDev = 0.1407 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  87.984 deg; T1  -- T1  = 3.9600 A
T1  - O1  - T1  - O3  - T3  = 143.874 deg; T1  -- T3  = 5.1291 A
T1  - O1  - T1  - O4  - T1  =  92.016 deg; T1  -- T1  = 3.9600 A
T1  - O2  - T1  - O3  - T3  =  56.555 deg; T1  -- T3  = 2.7925 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2255 A
T3  - O3  - T1  - O4  - T1  =  94.420 deg; T3  -- T1  = 4.1743 A

T2  - O5  - T2  - O6  - T4  = 108.466 deg; T2  -- T4  = 4.5062 A
T2  - O5  - T2  - O7  - T5  = 148.496 deg; T2  -- T5  = 5.2713 A
T2  - O5  - T2  - O8  - T2  =  90.000 deg; T2  -- T2  = 3.9436 A
T4  - O6  - T2  - O7  - T5  =  61.299 deg; T4  -- T5  = 2.7802 A
T4  - O6  - T2  - O8  - T2  =  59.718 deg; T4  -- T2  = 2.7644 A
T5  - O7  - T2  - O8  - T2  =  58.759 deg; T5  -- T2  = 2.6878 A

T1  - O4  - T3  - O9  - T3  =  85.580 deg; T1  -- T3  = 4.1743 A
T1  - O4  - T3  - O10 - T4  = 146.118 deg; T1  -- T4  = 5.6987 A
T1  - O4  - T3  - O4  - T1  =  66.890 deg; T1  -- T1  = 3.0780 A
T3  - O9  - T3  - O10 - T4  = 101.071 deg; T3  -- T4  = 5.0107 A
T3  - O9  - T3  - O4  - T1  =  85.580 deg; T3  -- T1  = 4.1743 A
T4  - O10 - T3  - O4  - T1  = 146.118 deg; T4  -- T1  = 5.6987 A

T2  - O7  - T4  - O10 - T3  = 136.685 deg; T2  -- T3  = 5.5116 A
T2  - O7  - T4  - O11 - T5  =  57.991 deg; T2  -- T5  = 2.6878 A
T2  - O7  - T4  - O7  - T2  =  60.564 deg; T2  -- T2  = 2.7879 A
T3  - O10 - T4  - O11 - T5  = 160.454 deg; T3  -- T5  = 5.8580 A
T3  - O10 - T4  - O7  - T2  = 136.685 deg; T3  -- T2  = 5.5116 A
T5  - O11 - T4  - O7  - T2  =  57.991 deg; T5  -- T2  = 2.6878 A

T2  - O8  - T5  - O11 - T4  =  60.710 deg; T2  -- T4  = 2.7644 A
T2  - O8  - T5  - O12 - T5  = 130.397 deg; T2  -- T5  = 5.0827 A
T2  - O8  - T5  - O8  - T2  =  62.482 deg; T2  -- T2  = 2.7879 A
T4  - O11 - T5  - O12 - T5  = 165.617 deg; T4  -- T5  = 5.6459 A
T4  - O11 - T5  - O8  - T2  =  60.710 deg; T4  -- T2  = 2.7644 A
T5  - O12 - T5  - O8  - T2  = 130.397 deg; T5  -- T2  = 5.0827 A

        T-T-T SUMMARY
          Range  = 56.5552 deg <--> 165.6171 deg
          Mean   = 95.5326 deg
          StdDev = 35.1986 deg

        T--T SUMMARY
          Range  = 2.6878 A <--> 5.8580 A
          Mean   = 4.0283 A
          StdDev = 1.1418 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 103.003 deg ; T1  -- T1   2.6021 A

T1  -- O2  -- T1  = 126.241 deg ; T1  -- T1   2.8949 A

T1  -- O3  -- T1  = 149.526 deg ; T1  -- T1   3.0780 A

T1  -- O4  -- T3  = 116.375 deg ; T1  -- T3   2.7925 A

T2  -- O5  -- T2  = 130.260 deg ; T2  -- T2   2.7879 A

T2  -- O6  -- T2  = 110.555 deg ; T2  -- T2   2.7891 A

T2  -- O7  -- T4  = 115.925 deg ; T2  -- T4   2.7644 A

T2  -- O8  -- T5  = 108.374 deg ; T2  -- T5   2.6878 A

T3  -- O9  -- T3  = 171.127 deg ; T3  -- T3   3.3253 A

T3  -- O10 -- T4  = 151.836 deg ; T3  -- T4   3.1637 A

T4  -- O11 -- T5  = 115.039 deg ; T4  -- T5   2.7802 A

T5  -- O12 -- T5  = 129.575 deg ; T5  -- T5   2.9104 A


        T-O-T SUMMARY
          Range  = 103.0026° <--> 171.1274 deg
          Mean   = 124.4048 deg
          StdDev = 18.0009 deg

        T--T SUMMARY
          Range  = 2.6021 A <--> 3.3253 A
          Mean   = 2.8487 A
          StdDev = 0.1808 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O5  -- O8  = 2.2230 A
O5  -- O8  = 2.2230 A
T1  -- T1  = 2.6021 Angstrom
T1  -- T3  = 2.7925 Angstrom
T2  -- T2  = 2.7891 Angstrom
T2  -- T4  = 2.7644 Angstrom
T2  -- T5  = 2.6878 Angstrom
T2  -- T2  = 2.7879 Angstrom
T3  -- T1  = 2.7925 Angstrom
T3  -- T1  = 2.7925 Angstrom
T4  -- T2  = 2.7644 Angstrom
T4  -- T5  = 2.7802 Angstrom
T4  -- T2  = 2.7644 Angstrom
T5  -- T2  = 2.6878 Angstrom
T5  -- T4  = 2.7802 Angstrom
T5  -- T2  = 2.6878 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 6 7 8 8 10 14 18 22 22 21 23 24 26 36 44
TD10 = 120
Circuit symbol = 3.4.4.4.4.5
Weight = 9
Vertex symbol  = 3.4.4.4.4.*
Weight = 9

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 5 7 10 12 12 18 12 17 18 22 24 36 28 46 34
TD10 = 116
Circuit symbol = 3.4.3.5.3.5
Weight = 6
Vertex symbol  = 3.4.3.6.3.16_{8}
Weight = 28

T3 (Si): multiplicity = 48
Coordination Sequence =
    1 4 8 8 6 12 10 16 18 20 21 26 18 30 30 36 44
TD10 = 124
Circuit symbol = 3.6_{2}.4.8_{2}.4.8_{2}
Weight = 12
Vertex symbol  = 3.6_{2}.4.*.4.*
Weight = 12

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 6 9 8 10 14 14 16 20 18 26 24 28 34 38 36
TD10 = 120
Circuit symbol = 3.6.3.6.3.7_{2}
Weight = 9
Vertex symbol  = 3.6.3.6.3.*
Weight = 9

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 6 8 10 12 12 16 17 16 18 24 28 32 32 38 44
TD10 = 120
Circuit symbol = 3.16_{8}.3.16_{8}.3.17_{16}
Weight = 25
Vertex symbol  = 3.16_{8}.3.16_{8}.3.*
Weight = 25

<TD10> = 119.429
Average ring size = 5.9091