Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_9797248_0rnMo_.cif"

There are 336 T-atoms per unit cell
There are 672 O-atoms per unit cell

Framework density = 2.60 T-atoms per nm^3
Material density = 0.260 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6384 Angstrom
T1  -- O2  = 1.5734 Angstrom
T1  -- O3  = 1.6729 Angstrom
T1  -- O4  = 1.6619 Angstrom
      mean = 1.6366 Angstrom
        t1 = 0.053299  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.043794  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.5481 Angstrom
T2  -- O6  = 1.6642 Angstrom
T2  -- O7  = 1.6285 Angstrom
T2  -- O8  = 1.6272 Angstrom
      mean = 1.6170 Angstrom
        t1 = 0.090412  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.121854  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6433 Angstrom
T3  -- O9  = 1.5589 Angstrom
T3  -- O10 = 1.7062 Angstrom
T3  -- O4  = 1.6433 Angstrom
      mean = 1.6379 Angstrom
        t1 = 0.046526  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.042078  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6633 Angstrom
T4  -- O9  = 1.5580 Angstrom
T4  -- O11 = 1.5862 Angstrom
T4  -- O7  = 1.6633 Angstrom
      mean = 1.6177 Angstrom
        t1 = 0.045375  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029021  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O8  = 1.6288 Angstrom
T5  -- O10 = 1.6910 Angstrom
T5  -- O12 = 1.6648 Angstrom
T5  -- O8  = 1.6288 Angstrom
      mean = 1.6534 Angstrom
        t1 = 0.041612  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021982  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5481 A <--> 1.7062 A
          Mean   = 1.6309 A
          StdDev = 0.0437 A

       t1 Range  = 0.0416 <-- 0.0554 --> 0.0904
       t2 Range  = 0.0220 <-- 0.0517 --> 0.1219

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 102.687 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 114.758 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 111.620 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 105.984 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 101.603 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 117.836 deg; O3  -- O4  = 3 A
       101.603 deg <-- 109.081 deg --> 117.836 deg

O5  -- T2  -- O6  = 105.482 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  =  86.013 deg; O5  -- O7  = 2 A
O5  -- T2  -- O8  = 105.977 deg; O5  -- O8  = 3 A
O6  -- T2  -- O7  = 125.119 deg; O6  -- O7  = 3 A
O6  -- T2  -- O8  = 113.996 deg; O6  -- O8  = 3 A
O7  -- T2  -- O8  = 113.579 deg; O7  -- O8  = 3 A
       86.013 deg <-- 108.361 deg --> 125.119 deg

O4  -- T3  -- O9  = 104.808 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 113.900 deg; O4  -- O10 = 3 A
O4  -- T3  -- O4  = 111.966 deg; O4  -- O4  = 3 A
O9  -- T3  -- O10 = 106.414 deg; O9  -- O10 = 3 A
O9  -- T3  -- O4  = 104.808 deg; O9  -- O4  = 3 A
O10 -- T3  -- O4  = 113.900 deg; O10 -- O4  = 3 A
       104.808 deg <-- 109.299 deg --> 113.900 deg

O7  -- T4  -- O9  = 105.165 deg; O7  -- O9  = 3 A
O7  -- T4  -- O11 = 109.877 deg; O7  -- O11 = 3 A
O7  -- T4  -- O7  = 119.582 deg; O7  -- O7  = 3 A
O9  -- T4  -- O11 = 106.159 deg; O9  -- O11 = 3 A
O9  -- T4  -- O7  = 105.165 deg; O9  -- O7  = 3 A
O11 -- T4  -- O7  = 109.877 deg; O11 -- O7  = 3 A
       105.165 deg <-- 109.305 deg --> 119.582 deg

O8  -- T5  -- O10 = 106.677 deg; O8  -- O10 = 3 A
O8  -- T5  -- O12 = 107.634 deg; O8  -- O12 = 3 A
O8  -- T5  -- O8  = 109.203 deg; O8  -- O8  = 3 A
O10 -- T5  -- O12 = 118.772 deg; O10 -- O12 = 3 A
O10 -- T5  -- O8  = 106.677 deg; O10 -- O8  = 3 A
O12 -- T5  -- O8  = 107.634 deg; O12 -- O8  = 3 A
       106.677 deg <-- 109.433 deg --> 118.772 deg

        O-T-O SUMMARY
          Range  = 86.0131 deg <--> 125.1188 deg
          Mean   = 109.1602 deg
          StdDev = 7.0967 deg

        O--O SUMMARY
          Range  = 2.1675 A <--> 2.9223 A
          Mean   = 2.6591 A
          StdDev = 0.1526 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  89.894 deg; T1  -- T1  = 4.0595 A
T1  - O1  - T1  - O3  - T3  = 132.037 deg; T1  -- T3  = 5.2025 A
T1  - O1  - T1  - O4  - T1  =  90.106 deg; T1  -- T1  = 4.0595 A
T1  - O2  - T1  - O3  - T3  = 123.100 deg; T1  -- T3  = 5.2676 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2615 A
T3  - O3  - T1  - O4  - T1  =  59.604 deg; T3  -- T1  = 2.9727 A

T2  - O5  - T2  - O6  - T4  = 145.874 deg; T2  -- T4  = 5.1678 A
T2  - O5  - T2  - O7  - T5  =  91.599 deg; T2  -- T5  = 4.0408 A
T2  - O5  - T2  - O8  - T2  =  90.000 deg; T2  -- T2  = 3.9488 A
T4  - O6  - T2  - O7  - T5  =  82.537 deg; T4  -- T5  = 3.7409 A
T4  - O6  - T2  - O8  - T2  =  57.852 deg; T4  -- T2  = 2.7203 A
T5  - O7  - T2  - O8  - T2  =  60.564 deg; T5  -- T2  = 2.9454 A

T1  - O4  - T3  - O9  - T4  = 107.013 deg; T1  -- T4  = 4.8963 A
T1  - O4  - T3  - O10 - T5  = 149.037 deg; T1  -- T5  = 5.6882 A
T1  - O4  - T3  - O4  - T1  =  60.792 deg; T1  -- T1  = 3.0083 A
T4  - O9  - T3  - O10 - T5  =  76.373 deg; T4  -- T5  = 3.7409 A
T4  - O9  - T3  - O4  - T1  = 107.013 deg; T4  -- T1  = 4.8963 A
T5  - O10 - T3  - O4  - T1  = 149.037 deg; T5  -- T1  = 5.6882 A

T2  - O7  - T4  - O9  - T3  =  91.685 deg; T2  -- T3  = 4.1968 A
T2  - O7  - T4  - O11 - T4  = 135.319 deg; T2  -- T4  = 5.3526 A
T2  - O7  - T4  - O7  - T2  =  64.297 deg; T2  -- T2  = 2.8950 A
T3  - O9  - T4  - O11 - T4  = 120.890 deg; T3  -- T4  = 5.3774 A
T3  - O9  - T4  - O7  - T2  =  91.685 deg; T3  -- T2  = 4.1968 A
T4  - O11 - T4  - O7  - T2  = 135.319 deg; T4  -- T2  = 5.3526 A

T2  - O8  - T5  - O10 - T3  =  91.179 deg; T2  -- T3  = 4.1968 A
T2  - O8  - T5  - O12 - T5  =  88.401 deg; T2  -- T5  = 4.0408 A
T2  - O8  - T5  - O8  - T2  =  58.871 deg; T2  -- T2  = 2.8950 A
T3  - O10 - T5  - O12 - T5  = 179.518 deg; T3  -- T5  = 5.7793 A
T3  - O10 - T5  - O8  - T2  =  91.179 deg; T3  -- T2  = 4.1968 A
T5  - O12 - T5  - O8  - T2  =  88.401 deg; T5  -- T2  = 4.0408 A

        T-T-T SUMMARY
          Range  = 57.8515 deg <--> 179.5177 deg
          Mean   = 96.8051 deg
          StdDev = 29.7072 deg

        T--T SUMMARY
          Range  = 2.7203 A <--> 5.7793 A
          Mean   = 4.2086 A
          StdDev = 0.9138 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 112.227 deg ; T1  -- T1   2.7202 A

T1  -- O2  -- T1  = 145.878 deg ; T1  -- T1   3.0083 A

T1  -- O3  -- T1  = 128.880 deg ; T1  -- T1   3.0184 A

T1  -- O4  -- T3  = 128.158 deg ; T1  -- T3   2.9727 A

T2  -- O5  -- T2  = 138.466 deg ; T2  -- T2   2.8950 A

T2  -- O6  -- T2  = 107.576 deg ; T2  -- T2   2.6854 A

T2  -- O7  -- T4  = 111.454 deg ; T2  -- T4   2.7203 A

T2  -- O8  -- T5  = 129.539 deg ; T2  -- T5   2.9454 A

T3  -- O9  -- T4  = 179.548 deg ; T3  -- T4   3.1168 A

T3  -- O10 -- T5  = 119.163 deg ; T3  -- T5   2.9296 A

T4  -- O11 -- T4  = 150.085 deg ; T4  -- T4   3.0649 A

T5  -- O12 -- T5  = 117.718 deg ; T5  -- T5   2.8498 A


        T-O-T SUMMARY
          Range  = 107.5759° <--> 179.5476 deg
          Mean   = 128.5435 deg
          StdDev = 17.4258 deg

        T--T SUMMARY
          Range  = 2.6854 A <--> 3.1168 A
          Mean   = 2.8946 A
          StdDev = 0.1351 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O5  -- O7  = 2.1675 A
O5  -- O7  = 2.1675 A
T1  -- T1  = 2.7202 Angstrom
T2  -- T2  = 2.6854 Angstrom
T2  -- T4  = 2.7203 Angstrom
T4  -- T2  = 2.7203 Angstrom
T4  -- T2  = 2.7203 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 9 11 12 14 20 26 29 30 30 35 48 60 68 72
TD10 = 163
Circuit symbol = 3.4.4.5.4.5
Weight = 8
Vertex symbol  = 3.4.4.6.4.*
Weight = 11

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 5 7 12 13 12 17 22 21 24 34 40 42 46 54 68
TD10 = 138
Circuit symbol = 3.4.3.5.4.4_{2}
Weight = 8
Vertex symbol  = 3.4.3.16_{8}.4.4
Weight = 27

T3 (Si): multiplicity = 48
Coordination Sequence =
    1 4 8 10 10 13 15 18 25 27 27 36 38 40 56 64 68
TD10 = 158
Circuit symbol = 3.4_{2}.6.8_{2}.6.8_{2}
Weight = 11
Vertex symbol  = 3.4_{2}.6.*.6.*
Weight = 11

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 8 9 8 11 18 19 17 23 30 30 36 44 50 60 70
TD10 = 148
Circuit symbol = 3.6_{2}.4.8_{2}.4.8_{2}
Weight = 11
Vertex symbol  = 3.6_{2}.4.16_{8}.4.16_{8}
Weight = 31

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 6 8 12 14 15 16 19 26 33 36 40 42 42 56 78
TD10 = 154
Circuit symbol = 3.6_{2}.4.4.4.4
Weight = 8
Vertex symbol  = 3.*.4.4.4.4
Weight = 8

<TD10> = 151.714
Average ring size = 6.0909