Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_9752810_g2LQB7.cif"

There are 336 T-atoms per unit cell
There are 672 O-atoms per unit cell

Framework density = 2.21 T-atoms per nm^3
Material density = 0.220 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6065 Angstrom
T1  -- O2  = 1.6713 Angstrom
T1  -- O3  = 1.7041 Angstrom
T1  -- O4  = 1.6611 Angstrom
      mean = 1.6608 Angstrom
        t1 = 0.041076  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025432  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6471 Angstrom
T2  -- O5  = 1.5513 Angstrom
T2  -- O6  = 1.7218 Angstrom
T2  -- O7  = 1.7061 Angstrom
      mean = 1.6565 Angstrom
        t1 = 0.082982  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.073179  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6240 Angstrom
T3  -- O4  = 1.6240 Angstrom
T3  -- O8  = 1.5908 Angstrom
T3  -- O8  = 1.5908 Angstrom
      mean = 1.6074 Angstrom
        t1 = 0.025775  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016855  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O6  = 1.6484 Angstrom
T4  -- O9  = 1.6755 Angstrom
T4  -- O10 = 1.4842 Angstrom
T4  -- O6  = 1.6484 Angstrom
      mean = 1.6141 Angstrom
        t1 = 0.091043  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.090325  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6459 Angstrom
T5  -- O10 = 1.4868 Angstrom
T5  -- O11 = 1.6635 Angstrom
T5  -- O7  = 1.6459 Angstrom
      mean = 1.6105 Angstrom
        t1 = 0.085878  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.079716  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4842 A <--> 1.7218 A
          Mean   = 1.6381 A
          StdDev = 0.0616 A

       t1 Range  = 0.0258 <-- 0.0654 --> 0.0910
       t2 Range  = 0.0169 <-- 0.0571 --> 0.0903

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.032 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 115.092 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 106.932 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 111.777 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.349 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 107.475 deg; O3  -- O4  = 3 A
       106.032 deg <-- 109.443 deg --> 115.092 deg

O3  -- T2  -- O5  =  98.254 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 119.393 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 118.124 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 100.505 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  =  99.004 deg; O5  -- O7  = 2 A
O6  -- T2  -- O7  = 114.884 deg; O6  -- O7  = 3 A
       98.254 deg <-- 108.361 deg --> 119.393 deg

O4  -- T3  -- O4  = 117.132 deg; O4  -- O4  = 3 A
O4  -- T3  -- O8  = 108.282 deg; O4  -- O8  = 3 A
O4  -- T3  -- O8  = 106.451 deg; O4  -- O8  = 3 A
O4  -- T3  -- O8  = 106.451 deg; O4  -- O8  = 3 A
O4  -- T3  -- O8  = 108.282 deg; O4  -- O8  = 3 A
O8  -- T3  -- O8  = 110.184 deg; O8  -- O8  = 3 A
       106.451 deg <-- 109.464 deg --> 117.132 deg

O6  -- T4  -- O9  = 119.945 deg; O6  -- O9  = 3 A
O6  -- T4  -- O10 =  95.591 deg; O6  -- O10 = 2 A
O6  -- T4  -- O6  = 113.395 deg; O6  -- O6  = 3 A
O9  -- T4  -- O10 = 104.394 deg; O9  -- O10 = 2 A
O9  -- T4  -- O6  = 119.945 deg; O9  -- O6  = 3 A
O10 -- T4  -- O6  =  95.591 deg; O10 -- O6  = 2 A
       95.591 deg <-- 108.144 deg --> 119.945 deg

O7  -- T5  -- O10 =  96.061 deg; O7  -- O10 = 2 A
O7  -- T5  -- O11 = 118.699 deg; O7  -- O11 = 3 A
O7  -- T5  -- O7  = 114.753 deg; O7  -- O7  = 3 A
O10 -- T5  -- O11 = 105.740 deg; O10 -- O11 = 3 A
O10 -- T5  -- O7  =  96.061 deg; O10 -- O7  = 2 A
O11 -- T5  -- O7  = 118.699 deg; O11 -- O7  = 3 A
       96.061 deg <-- 108.335 deg --> 118.699 deg

        O-T-O SUMMARY
          Range  = 95.5915 deg <--> 119.9446 deg
          Mean   = 108.9036 deg
          StdDev = 8.1091 deg

        O--O SUMMARY
          Range  = 2.3231 A <--> 2.9088 A
          Mean   = 2.6528 A
          StdDev = 0.1892 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 132.646 deg; T1  -- T2  = 5.6780 A
T1  - O1  - T1  - O3  - T3  =  89.247 deg; T1  -- T3  = 4.2584 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.5348 A
T2  - O2  - T1  - O3  - T3  = 137.866 deg; T2  -- T3  = 5.4462 A
T2  - O2  - T1  - O4  - T1  =  86.859 deg; T2  -- T1  = 4.2638 A
T3  - O3  - T1  - O4  - T1  =  89.258 deg; T3  -- T1  = 4.2580 A

T1  - O3  - T2  - O5  - T4  = 131.528 deg; T1  -- T4  = 5.2363 A
T1  - O3  - T2  - O6  - T5  = 135.903 deg; T1  -- T5  = 5.2994 A
T1  - O3  - T2  - O7  - T2  =  93.141 deg; T1  -- T2  = 4.2638 A
T4  - O5  - T2  - O6  - T5  =  64.268 deg; T4  -- T5  = 2.9116 A
T4  - O5  - T2  - O7  - T2  =  58.437 deg; T4  -- T2  = 2.7493 A
T5  - O6  - T2  - O7  - T2  =  58.115 deg; T5  -- T2  = 2.7245 A

T1  - O4  - T3  - O4  - T1  = 177.885 deg; T1  -- T1  = 5.6870 A
T1  - O4  - T3  - O8  - T3  =  90.753 deg; T1  -- T3  = 4.2584 A
T1  - O4  - T3  - O8  - T3  =  90.742 deg; T1  -- T3  = 4.2580 A
T1  - O4  - T3  - O8  - T3  =  90.742 deg; T1  -- T3  = 4.2580 A
T1  - O4  - T3  - O8  - T3  =  90.753 deg; T1  -- T3  = 4.2584 A
T3  - O8  - T3  - O8  - T3  =  90.000 deg; T3  -- T3  = 4.4298 A

T2  - O6  - T4  - O9  - T4  = 131.094 deg; T2  -- T4  = 5.2398 A
T2  - O6  - T4  - O10 - T5  =  57.451 deg; T2  -- T5  = 2.7245 A
T2  - O6  - T4  - O6  - T2  =  63.125 deg; T2  -- T2  = 2.8782 A
T4  - O9  - T4  - O10 - T5  =  89.636 deg; T4  -- T5  = 4.1713 A
T4  - O9  - T4  - O6  - T2  = 131.094 deg; T4  -- T2  = 5.2398 A
T5  - O10 - T4  - O6  - T2  =  57.451 deg; T5  -- T2  = 2.7245 A

T2  - O7  - T5  - O10 - T4  =  58.280 deg; T2  -- T4  = 2.7493 A
T2  - O7  - T5  - O11 - T5  = 132.074 deg; T2  -- T5  = 5.2033 A
T2  - O7  - T5  - O7  - T2  =  63.769 deg; T2  -- T2  = 2.8782 A
T4  - O10 - T5  - O11 - T5  =  90.364 deg; T4  -- T5  = 4.1713 A
T4  - O10 - T5  - O7  - T2  =  58.280 deg; T4  -- T2  = 2.7493 A
T5  - O11 - T5  - O7  - T2  = 132.074 deg; T5  -- T2  = 5.2033 A

        T-T-T SUMMARY
          Range  = 57.4513 deg <--> 177.8851 deg
          Mean   = 95.0541 deg
          StdDev = 32.2982 deg

        T--T SUMMARY
          Range  = 2.7245 A <--> 5.6870 A
          Mean   = 4.1243 A
          StdDev = 1.0235 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 172.418 deg ; T1  -- T1   3.2061 A

T1  -- O2  -- T1  = 147.252 deg ; T1  -- T1   3.2071 A

T1  -- O3  -- T2  = 126.451 deg ; T1  -- T2   2.9920 A

T1  -- O4  -- T3  = 119.930 deg ; T1  -- T3   2.8440 A

T2  -- O5  -- T2  = 136.150 deg ; T2  -- T2   2.8782 A

T2  -- O6  -- T4  = 109.313 deg ; T2  -- T4   2.7493 A

T2  -- O7  -- T5  = 108.728 deg ; T2  -- T5   2.7245 A

T3  -- O8  -- T3  = 159.813 deg ; T3  -- T3   3.1324 A

T4  -- O9  -- T4  = 127.517 deg ; T4  -- T4   3.0056 A

T4  -- O10 -- T5  = 157.054 deg ; T4  -- T5   2.9116 A

T5  -- O11 -- T5  = 126.323 deg ; T5  -- T5   2.9686 A


        T-O-T SUMMARY
          Range  = 108.7276° <--> 172.4180 deg
          Mean   = 133.9549 deg
          StdDev = 20.5834 deg

        T--T SUMMARY
          Range  = 2.7245 A <--> 3.2071 A
          Mean   = 2.9567 A
          StdDev = 0.1700 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T4  = 2.7493 Angstrom
T2  -- T5  = 2.7245 Angstrom
T4  -- T2  = 2.7493 Angstrom
T4  -- T2  = 2.7493 Angstrom
T5  -- T2  = 2.7245 Angstrom
T5  -- T2  = 2.7245 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 8 9 9 9 10 14 18 24 26 26 26 28 36 46 56
TD10 = 132
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.24_{128}.4.*
Weight = 50

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 5 7 9 11 13 12 16 18 22 28 32 34 34 40 44
TD10 = 118
Circuit symbol = 3.4.3.5.3.5
Weight = 6
Vertex symbol  = 3.4.3.24_{64}.3.24_{64}
Weight = 46

T3 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 10 10 8 8 12 20 24 28 28 24 24 32 48 60
TD10 = 132
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.*
Weight = 10

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 5 6 10 12 14 14 12 14 22 32 36 38 36 32 36
TD10 = 114
Circuit symbol = 3.4.3.5.3.5
Weight = 6
Vertex symbol  = 3.4.3.24_{64}.3.24_{64}
Weight = 48

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 5 6 10 12 14 14 12 14 22 32 36 38 36 32 36
TD10 = 114
Circuit symbol = 3.4.3.5.3.5
Weight = 6
Vertex symbol  = 3.4.3.24_{64}.3.24_{64}
Weight = 48

<TD10> = 122.857
Average ring size = 19.8012