Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_9238887_9xYNmE.cif"

There are 384 T-atoms per unit cell
There are 768 O-atoms per unit cell

Framework density = 1.65 T-atoms per nm^3
Material density = 0.165 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5948 Angstrom
T1  -- O2  = 1.6440 Angstrom
T1  -- O3  = 1.6242 Angstrom
T1  -- O4  = 1.6588 Angstrom
      mean = 1.6305 Angstrom
        t1 = 0.018632  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013521  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6317 Angstrom
T2  -- O5  = 1.6113 Angstrom
T2  -- O6  = 1.6233 Angstrom
T2  -- O7  = 1.6939 Angstrom
      mean = 1.6400 Angstrom
        t1 = 0.032989  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029553  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6611 Angstrom
T3  -- O8  = 1.6255 Angstrom
T3  -- O9  = 1.5873 Angstrom
T3  -- O10 = 1.6430 Angstrom
      mean = 1.6292 Angstrom
        t1 = 0.047983  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037594  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.6419 Angstrom
T4  -- O11 = 1.6628 Angstrom
T4  -- O12 = 1.7091 Angstrom
T4  -- O10 = 1.6419 Angstrom
      mean = 1.6639 Angstrom
        t1 = 0.044930  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.023173  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.6633 Angstrom
T5  -- O13 = 1.5536 Angstrom
T5  -- O14 = 1.6593 Angstrom
T5  -- O14 = 1.6593 Angstrom
      mean = 1.6339 Angstrom
        t1 = 0.072126  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.068868  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5536 A <--> 1.7091 A
          Mean   = 1.6372 A
          StdDev = 0.0327 A

       t1 Range  = 0.0186 <-- 0.0433 --> 0.0721
       t2 Range  = 0.0135 <-- 0.0345 --> 0.0689

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.792 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.854 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.527 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.988 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.197 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.435 deg; O3  -- O4  = 3 A
       108.527 deg <-- 109.465 deg --> 111.197 deg

O4  -- T2  -- O5  = 108.546 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 104.583 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 114.735 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.633 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.836 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.375 deg; O6  -- O7  = 3 A
       104.583 deg <-- 109.451 deg --> 114.735 deg

O7  -- T3  -- O8  = 111.081 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 103.760 deg; O7  -- O9  = 3 A
O7  -- T3  -- O10 = 120.762 deg; O7  -- O10 = 3 A
O8  -- T3  -- O9  = 109.326 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 110.266 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 100.404 deg; O9  -- O10 = 2 A
       100.404 deg <-- 109.266 deg --> 120.762 deg

O10 -- T4  -- O11 = 106.088 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 111.678 deg; O10 -- O12 = 3 A
O10 -- T4  -- O10 = 106.395 deg; O10 -- O10 = 3 A
O11 -- T4  -- O12 = 114.375 deg; O11 -- O12 = 3 A
O11 -- T4  -- O10 = 106.088 deg; O11 -- O10 = 3 A
O12 -- T4  -- O10 = 111.678 deg; O12 -- O10 = 3 A
       106.088 deg <-- 109.384 deg --> 114.375 deg

O12 -- T5  -- O13 =  99.606 deg; O12 -- O13 = 2 A
O12 -- T5  -- O14 = 119.117 deg; O12 -- O14 = 3 A
O12 -- T5  -- O14 = 119.117 deg; O12 -- O14 = 3 A
O13 -- T5  -- O14 =  99.989 deg; O13 -- O14 = 2 A
O13 -- T5  -- O14 =  99.989 deg; O13 -- O14 = 2 A
O14 -- T5  -- O14 = 113.144 deg; O14 -- O14 = 3 A
       99.606 deg <-- 108.494 deg --> 119.117 deg

        O-T-O SUMMARY
          Range  = 99.6064 deg <--> 120.7620 deg
          Mean   = 109.1833 deg
          StdDev = 4.9766 deg

        O--O SUMMARY
          Range  = 2.4582 A <--> 2.8723 A
          Mean   = 2.6742 A
          StdDev = 0.1072 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 135.000 deg; T1  -- T1  = 5.6606 A
T1  - O1  - T1  - O3  - T2  =  89.975 deg; T1  -- T2  = 4.2205 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4964 A
T1  - O2  - T1  - O3  - T2  = 135.025 deg; T1  -- T2  = 5.2890 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3350 A
T2  - O3  - T1  - O4  - T1  =  89.975 deg; T2  -- T1  = 4.2205 A

T1  - O4  - T2  - O5  - T2  =  90.025 deg; T1  -- T2  = 4.2205 A
T1  - O4  - T2  - O6  - T3  = 176.651 deg; T1  -- T3  = 5.4697 A
T1  - O4  - T2  - O7  - T2  =  90.025 deg; T1  -- T2  = 4.2205 A
T2  - O5  - T2  - O6  - T3  =  88.430 deg; T2  -- T3  = 4.1094 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.4929 A
T3  - O6  - T2  - O7  - T2  =  87.003 deg; T3  -- T2  = 4.0572 A

T2  - O7  - T3  - O8  - T3  =  91.570 deg; T2  -- T3  = 4.1094 A
T2  - O7  - T3  - O9  - T4  = 147.687 deg; T2  -- T4  = 5.2642 A
T2  - O7  - T3  - O10 - T3  =  92.997 deg; T2  -- T3  = 4.0572 A
T3  - O8  - T3  - O9  - T4  =  57.061 deg; T3  -- T4  = 2.7856 A
T3  - O8  - T3  - O10 - T3  =  90.000 deg; T3  -- T3  = 4.1903 A
T4  - O9  - T3  - O10 - T3  =  94.408 deg; T4  -- T3  = 4.1691 A

T3  - O10 - T4  - O11 - T4  =  85.592 deg; T3  -- T4  = 4.1691 A
T3  - O10 - T4  - O12 - T5  = 145.878 deg; T3  -- T5  = 5.5382 A
T3  - O10 - T4  - O10 - T3  =  65.878 deg; T3  -- T3  = 3.0293 A
T4  - O11 - T4  - O12 - T5  =  85.800 deg; T4  -- T5  = 4.3156 A
T4  - O11 - T4  - O10 - T3  =  85.592 deg; T4  -- T3  = 4.1691 A
T5  - O12 - T4  - O10 - T3  = 145.878 deg; T5  -- T3  = 5.5382 A

T4  - O12 - T5  - O13 - T5  =  94.200 deg; T4  -- T5  = 4.3156 A
T4  - O12 - T5  - O14 - T5  = 134.729 deg; T4  -- T5  = 5.3017 A
T4  - O12 - T5  - O14 - T5  = 134.729 deg; T4  -- T5  = 5.3017 A
T5  - O13 - T5  - O14 - T5  =  58.206 deg; T5  -- T5  = 2.7359 A
T5  - O13 - T5  - O14 - T5  =  58.206 deg; T5  -- T5  = 2.7359 A
T5  - O14 - T5  - O14 - T5  =  63.588 deg; T5  -- T5  = 2.8829 A

        T-T-T SUMMARY
          Range  = 57.0608 deg <--> 176.6508 deg
          Mean   = 100.6931 deg
          StdDev = 29.5481 deg

        T--T SUMMARY
          Range  = 2.7359 A <--> 5.6606 A
          Mean   = 4.3572 A
          StdDev = 0.7708 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 170.837 deg ; T1  -- T1   3.1794 A

T1  -- O2  -- T1  = 150.458 deg ; T1  -- T1   3.1794 A

T1  -- O3  -- T1  = 130.234 deg ; T1  -- T1   2.9468 A

T1  -- O4  -- T2  = 115.117 deg ; T1  -- T2   2.7771 A

T2  -- O5  -- T2  = 160.701 deg ; T2  -- T2   3.1769 A

T2  -- O6  -- T2  = 156.226 deg ; T2  -- T2   3.1769 A

T2  -- O7  -- T3  = 106.884 deg ; T2  -- T3   2.6950 A

T3  -- O8  -- T3  = 125.888 deg ; T3  -- T3   2.8952 A

T3  -- O9  -- T3  = 145.204 deg ; T3  -- T3   3.0293 A

T3  -- O10 -- T4  = 115.988 deg ; T3  -- T4   2.7856 A

T4  -- O11 -- T4  = 175.887 deg ; T4  -- T4   3.3234 A

T4  -- O12 -- T5  = 126.173 deg ; T4  -- T5   3.0072 A

T5  -- O13 -- T5  = 136.195 deg ; T5  -- T5   2.8829 A

T5  -- O14 -- T5  = 111.054 deg ; T5  -- T5   2.7359 A


        T-O-T SUMMARY
          Range  = 106.8841° <--> 175.8865 deg
          Mean   = 137.6827 deg
          StdDev = 21.3543 deg

        T--T SUMMARY
          Range  = 2.6950 A <--> 3.3234 A
          Mean   = 2.9847 A
          StdDev = 0.1875 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7771 Angstrom
T2  -- T1  = 2.7771 Angstrom
T2  -- T3  = 2.6950 Angstrom
T3  -- T2  = 2.6950 Angstrom
T3  -- T4  = 2.7856 Angstrom
T4  -- T3  = 2.7856 Angstrom
T4  -- T3  = 2.7856 Angstrom
T5  -- T5  = 2.7359 Angstrom
T5  -- T5  = 2.7359 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 8 12 14 14 12 12 13 14 16 20 28 36 40 38 32
TD10 = 120
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.8.4.*
Weight = 14

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 8 11 13 15 14 12 13 18 24 24 24 30 38 42
TD10 = 116
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.*
Weight = 10

T3 (Si): multiplicity = 96
Coordination Sequence =
    1 4 6 7 7 12 15 15 14 16 21 22 20 18 22 34 42
TD10 = 118
Circuit symbol = 3.4.4.4.4.5
Weight = 9
Vertex symbol  = 3.4.4.4.4.*
Weight = 9

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 6 8 10 14 16 18 21 18 19 16 18 22 30 40
TD10 = 123
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.*.4.*
Weight = 8

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 5 8 8 8 10 18 24 22 17 12 17 20 22 24 32
TD10 = 125
Circuit symbol = 3.4.3.5.3.5
Weight = 6
Vertex symbol  = 3.4.3.*.3.*
Weight = 6

<TD10> = 119.500
Average ring size = 3.8974