Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_9032386_0gqVGH.cif"

There are 384 T-atoms per unit cell
There are 768 O-atoms per unit cell

Framework density = 1.67 T-atoms per nm^3
Material density = 0.166 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6609 Angstrom
T1  -- O2  = 1.6223 Angstrom
T1  -- O3  = 1.5940 Angstrom
T1  -- O4  = 1.6396 Angstrom
      mean = 1.6292 Angstrom
        t1 = 0.053905  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.036705  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6359 Angstrom
T2  -- O6  = 1.6368 Angstrom
T2  -- O7  = 1.6181 Angstrom
T2  -- O8  = 1.6591 Angstrom
      mean = 1.6375 Angstrom
        t1 = 0.019036  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008308  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O8  = 1.6264 Angstrom
T3  -- O9  = 1.6147 Angstrom
T3  -- O10 = 1.5847 Angstrom
T3  -- O11 = 1.6375 Angstrom
      mean = 1.6158 Angstrom
        t1 = 0.047910  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.050043  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O4  = 1.6459 Angstrom
T4  -- O12 = 1.6615 Angstrom
T4  -- O13 = 1.6401 Angstrom
T4  -- O4  = 1.6459 Angstrom
      mean = 1.6484 Angstrom
        t1 = 0.024911  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005582  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O11 = 1.6395 Angstrom
T5  -- O13 = 1.6343 Angstrom
T5  -- O14 = 1.6504 Angstrom
T5  -- O11 = 1.6395 Angstrom
      mean = 1.6409 Angstrom
        t1 = 0.021874  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006783  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5847 A <--> 1.6615 A
          Mean   = 1.6318 A
          StdDev = 0.0207 A

       t1 Range  = 0.0190 <-- 0.0335 --> 0.0539
       t2 Range  = 0.0056 <-- 0.0215 --> 0.0500

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.675 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.306 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 123.206 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.647 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.224 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  97.642 deg; O3  -- O4  = 2 A
       97.642 deg <-- 109.284 deg --> 123.206 deg

O5  -- T2  -- O6  = 109.168 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.856 deg; O5  -- O7  = 3 A
O5  -- T2  -- O8  = 110.663 deg; O5  -- O8  = 3 A
O6  -- T2  -- O7  = 109.360 deg; O6  -- O7  = 3 A
O6  -- T2  -- O8  = 109.780 deg; O6  -- O8  = 3 A
O7  -- T2  -- O8  = 108.991 deg; O7  -- O8  = 3 A
       108.856 deg <-- 109.470 deg --> 110.663 deg

O8  -- T3  -- O9  = 110.396 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 100.296 deg; O8  -- O10 = 2 A
O8  -- T3  -- O11 = 122.109 deg; O8  -- O11 = 3 A
O9  -- T3  -- O10 = 110.515 deg; O9  -- O10 = 3 A
O9  -- T3  -- O11 = 110.099 deg; O9  -- O11 = 3 A
O10 -- T3  -- O11 = 102.260 deg; O10 -- O11 = 3 A
       100.296 deg <-- 109.279 deg --> 122.109 deg

O4  -- T4  -- O12 = 109.070 deg; O4  -- O12 = 3 A
O4  -- T4  -- O13 = 110.752 deg; O4  -- O13 = 3 A
O4  -- T4  -- O4  = 107.094 deg; O4  -- O4  = 3 A
O12 -- T4  -- O13 = 110.032 deg; O12 -- O13 = 3 A
O12 -- T4  -- O4  = 109.070 deg; O12 -- O4  = 3 A
O13 -- T4  -- O4  = 110.752 deg; O13 -- O4  = 3 A
       107.094 deg <-- 109.462 deg --> 110.752 deg

O11 -- T5  -- O13 = 111.479 deg; O11 -- O13 = 3 A
O11 -- T5  -- O14 = 108.893 deg; O11 -- O14 = 3 A
O11 -- T5  -- O11 = 106.118 deg; O11 -- O11 = 3 A
O13 -- T5  -- O14 = 109.864 deg; O13 -- O14 = 3 A
O13 -- T5  -- O11 = 111.479 deg; O13 -- O11 = 3 A
O14 -- T5  -- O11 = 108.893 deg; O14 -- O11 = 3 A
       106.118 deg <-- 109.454 deg --> 111.479 deg

        O-T-O SUMMARY
          Range  = 97.6423 deg <--> 123.2064 deg
          Mean   = 109.3913 deg
          StdDev = 5.1239 deg

        O--O SUMMARY
          Range  = 2.4340 A <--> 2.9033 A
          Mean   = 2.6668 A
          StdDev = 0.0951 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  87.943 deg; T1  -- T1  = 3.9547 A
T1  - O1  - T1  - O3  - T4  = 143.673 deg; T1  -- T4  = 5.1096 A
T1  - O1  - T1  - O4  - T1  =  92.057 deg; T1  -- T1  = 3.9547 A
T1  - O2  - T1  - O3  - T4  =  56.399 deg; T1  -- T4  = 2.7801 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2218 A
T4  - O3  - T1  - O4  - T1  =  94.415 deg; T4  -- T1  = 4.1619 A

T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.4362 A
T2  - O5  - T2  - O7  - T3  =  85.648 deg; T2  -- T3  = 4.0922 A
T2  - O5  - T2  - O8  - T2  =  90.000 deg; T2  -- T2  = 4.5058 A
T2  - O6  - T2  - O7  - T3  = 135.916 deg; T2  -- T3  = 5.3053 A
T2  - O6  - T2  - O8  - T2  = 135.000 deg; T2  -- T2  = 5.6369 A
T3  - O7  - T2  - O8  - T2  =  88.916 deg; T3  -- T2  = 4.0884 A

T2  - O8  - T3  - O9  - T3  =  91.084 deg; T2  -- T3  = 4.0884 A
T2  - O8  - T3  - O10 - T5  = 147.158 deg; T2  -- T5  = 5.2795 A
T2  - O8  - T3  - O11 - T3  =  94.352 deg; T2  -- T3  = 4.0922 A
T3  - O9  - T3  - O10 - T5  =  57.377 deg; T3  -- T5  = 2.7810 A
T3  - O9  - T3  - O11 - T3  =  90.000 deg; T3  -- T3  = 4.1404 A
T5  - O10 - T3  - O11 - T3  =  94.527 deg; T5  -- T3  = 4.1399 A

T1  - O4  - T4  - O12 - T4  =  85.585 deg; T1  -- T4  = 4.1619 A
T1  - O4  - T4  - O13 - T5  = 145.999 deg; T1  -- T5  = 5.5365 A
T1  - O4  - T4  - O4  - T1  =  67.203 deg; T1  -- T1  = 3.0770 A
T4  - O12 - T4  - O13 - T5  =  89.766 deg; T4  -- T5  = 4.4706 A
T4  - O12 - T4  - O4  - T1  =  85.585 deg; T4  -- T1  = 4.1619 A
T5  - O13 - T4  - O4  - T1  = 145.999 deg; T5  -- T1  = 5.5365 A

T3  - O11 - T5  - O13 - T4  = 147.019 deg; T3  -- T4  = 5.5523 A
T3  - O11 - T5  - O14 - T5  =  85.473 deg; T3  -- T5  = 4.1399 A
T3  - O11 - T5  - O11 - T3  =  65.245 deg; T3  -- T3  = 2.9985 A
T4  - O13 - T5  - O14 - T5  =  90.234 deg; T4  -- T5  = 4.4706 A
T4  - O13 - T5  - O11 - T3  = 147.019 deg; T4  -- T3  = 5.5523 A
T5  - O14 - T5  - O11 - T3  =  85.473 deg; T5  -- T3  = 4.1399 A

        T-T-T SUMMARY
          Range  = 56.3987 deg <--> 147.1582 deg
          Mean   = 101.4347 deg
          StdDev = 27.7387 deg

        T--T SUMMARY
          Range  = 2.7801 A <--> 5.6369 A
          Mean   = 4.3869 A
          StdDev = 0.7838 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 102.866 deg ; T1  -- T1   2.5972 A

T1  -- O2  -- T1  = 125.972 deg ; T1  -- T1   2.8906 A

T1  -- O3  -- T1  = 149.666 deg ; T1  -- T1   3.0770 A

T1  -- O4  -- T4  = 115.592 deg ; T1  -- T4   2.7801 A

T2  -- O5  -- T2  = 142.873 deg ; T2  -- T2   3.1016 A

T2  -- O6  -- T2  = 173.556 deg ; T2  -- T2   3.2684 A

T2  -- O7  -- T2  = 135.918 deg ; T2  -- T2   2.9996 A

T2  -- O8  -- T3  = 111.942 deg ; T2  -- T3   2.7230 A

T3  -- O9  -- T3  = 124.275 deg ; T3  -- T3   2.8551 A

T3  -- O10 -- T3  = 142.195 deg ; T3  -- T3   2.9985 A

T3  -- O11 -- T5  = 116.131 deg ; T3  -- T5   2.7810 A

T4  -- O12 -- T4  = 174.161 deg ; T4  -- T4   3.3186 A

T4  -- O13 -- T5  = 133.543 deg ; T4  -- T5   3.0090 A

T5  -- O14 -- T5  = 172.715 deg ; T5  -- T5   3.2941 A


        T-O-T SUMMARY
          Range  = 102.8658° <--> 174.1612 deg
          Mean   = 134.4956 deg
          StdDev = 21.5229 deg

        T--T SUMMARY
          Range  = 2.5972 A <--> 3.3186 A
          Mean   = 2.9506 A
          StdDev = 0.2041 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.5972 Angstrom
T1  -- T4  = 2.7801 Angstrom
T2  -- T3  = 2.7230 Angstrom
T3  -- T2  = 2.7230 Angstrom
T3  -- T5  = 2.7810 Angstrom
T4  -- T1  = 2.7801 Angstrom
T4  -- T1  = 2.7801 Angstrom
T5  -- T3  = 2.7810 Angstrom
T5  -- T3  = 2.7810 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 6 6 7 8 10 16 20 19 19 21 19 20 22 22 32
TD10 = 116
Circuit symbol = 3.4.4.4.4.5
Weight = 9
Vertex symbol  = 3.4.4.4.4.*
Weight = 9

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 8 11 13 14 14 13 14 14 14 20 28 32 38 40 36
TD10 = 120
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.8.4.*
Weight = 14

T3 (Si): multiplicity = 96
Coordination Sequence =
    1 4 6 8 12 14 12 14 15 14 18 22 20 26 34 36 38
TD10 = 118
Circuit symbol = 3.4.4.4.4.5
Weight = 9
Vertex symbol  = 3.4.4.4.4.*
Weight = 9

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 8 6 10 14 14 17 22 19 18 22 18 20 30 38
TD10 = 122
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.*.4.*
Weight = 8

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 8 10 12 14 13 14 19 20 20 20 22 28 36 34
TD10 = 122
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.*.4.*
Weight = 8

<TD10> = 119.000
Average ring size = 3.8974