Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_9032290_QVT0La.cif"

There are 384 T-atoms per unit cell
There are 768 O-atoms per unit cell

Framework density = 1.64 T-atoms per nm^3
Material density = 0.164 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6623 Angstrom
T1  -- O2  = 1.6225 Angstrom
T1  -- O3  = 1.5933 Angstrom
T1  -- O4  = 1.6411 Angstrom
      mean = 1.6298 Angstrom
        t1 = 0.054556  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037216  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6054 Angstrom
T2  -- O6  = 1.6547 Angstrom
T2  -- O7  = 1.6308 Angstrom
T2  -- O8  = 1.6610 Angstrom
      mean = 1.6380 Angstrom
        t1 = 0.022343  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.015849  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O8  = 1.6302 Angstrom
T3  -- O9  = 1.6161 Angstrom
T3  -- O10 = 1.5784 Angstrom
T3  -- O11 = 1.6382 Angstrom
      mean = 1.6157 Angstrom
        t1 = 0.052523  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.050185  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O4  = 1.6462 Angstrom
T4  -- O12 = 1.6599 Angstrom
T4  -- O13 = 1.6431 Angstrom
T4  -- O4  = 1.6462 Angstrom
      mean = 1.6489 Angstrom
        t1 = 0.025606  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007432  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O11 = 1.6430 Angstrom
T5  -- O13 = 1.6409 Angstrom
T5  -- O14 = 1.6543 Angstrom
T5  -- O11 = 1.6430 Angstrom
      mean = 1.6453 Angstrom
        t1 = 0.024328  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006982  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5784 A <--> 1.6623 A
          Mean   = 1.6326 A
          StdDev = 0.0236 A

       t1 Range  = 0.0223 <-- 0.0359 --> 0.0546
       t2 Range  = 0.0070 <-- 0.0235 --> 0.0502

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.583 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.217 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 123.491 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.555 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.138 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  97.702 deg; O3  -- O4  = 2 A
       97.702 deg <-- 109.281 deg --> 123.491 deg

O5  -- T2  -- O6  = 107.428 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.040 deg; O5  -- O7  = 3 A
O5  -- T2  -- O8  = 110.995 deg; O5  -- O8  = 3 A
O6  -- T2  -- O7  = 110.786 deg; O6  -- O7  = 3 A
O6  -- T2  -- O8  = 109.784 deg; O6  -- O8  = 3 A
O7  -- T2  -- O8  = 109.774 deg; O7  -- O8  = 3 A
       107.428 deg <-- 109.468 deg --> 110.995 deg

O8  -- T3  -- O9  = 110.475 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 100.825 deg; O8  -- O10 = 2 A
O8  -- T3  -- O11 = 123.147 deg; O8  -- O11 = 3 A
O9  -- T3  -- O10 = 110.482 deg; O9  -- O10 = 3 A
O9  -- T3  -- O11 = 110.346 deg; O9  -- O11 = 3 A
O10 -- T3  -- O11 = 100.087 deg; O10 -- O11 = 2 A
       100.087 deg <-- 109.227 deg --> 123.147 deg

O4  -- T4  -- O12 = 108.960 deg; O4  -- O12 = 3 A
O4  -- T4  -- O13 = 111.145 deg; O4  -- O13 = 3 A
O4  -- T4  -- O4  = 106.808 deg; O4  -- O4  = 3 A
O12 -- T4  -- O13 = 109.740 deg; O12 -- O13 = 3 A
O12 -- T4  -- O4  = 108.960 deg; O12 -- O4  = 3 A
O13 -- T4  -- O4  = 111.145 deg; O13 -- O4  = 3 A
       106.808 deg <-- 109.460 deg --> 111.145 deg

O11 -- T5  -- O13 = 111.633 deg; O11 -- O13 = 3 A
O11 -- T5  -- O14 = 108.720 deg; O11 -- O14 = 3 A
O11 -- T5  -- O11 = 106.389 deg; O11 -- O11 = 3 A
O13 -- T5  -- O14 = 109.632 deg; O13 -- O14 = 3 A
O13 -- T5  -- O11 = 111.633 deg; O13 -- O11 = 3 A
O14 -- T5  -- O11 = 108.720 deg; O14 -- O11 = 3 A
       106.389 deg <-- 109.454 deg --> 111.633 deg

        O-T-O SUMMARY
          Range  = 97.7015 deg <--> 123.4907 deg
          Mean   = 109.4160 deg
          StdDev = 5.3841 deg

        O--O SUMMARY
          Range  = 2.4357 A <--> 2.9098 A
          Mean   = 2.6691 A
          StdDev = 0.1007 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  87.994 deg; T1  -- T1  = 3.9585 A
T1  - O1  - T1  - O3  - T4  = 143.855 deg; T1  -- T4  = 5.1238 A
T1  - O1  - T1  - O4  - T1  =  92.006 deg; T1  -- T1  = 3.9585 A
T1  - O2  - T1  - O3  - T4  =  56.512 deg; T1  -- T4  = 2.7860 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2210 A
T4  - O3  - T1  - O4  - T1  =  94.361 deg; T4  -- T1  = 4.1655 A

T2  - O5  - T2  - O6  - T2  = 135.000 deg; T2  -- T2  = 5.6508 A
T2  - O5  - T2  - O7  - T3  =  86.509 deg; T2  -- T3  = 4.0972 A
T2  - O5  - T2  - O8  - T2  =  90.000 deg; T2  -- T2  = 4.5125 A
T2  - O6  - T2  - O7  - T3  = 138.462 deg; T2  -- T3  = 5.3252 A
T2  - O6  - T2  - O8  - T2  =  90.000 deg; T2  -- T2  = 4.3274 A
T3  - O7  - T2  - O8  - T2  =  88.242 deg; T3  -- T2  = 4.1611 A

T2  - O8  - T3  - O9  - T3  =  91.758 deg; T2  -- T3  = 4.1611 A
T2  - O8  - T3  - O10 - T5  = 147.743 deg; T2  -- T5  = 5.3340 A
T2  - O8  - T3  - O11 - T3  =  93.491 deg; T2  -- T3  = 4.0972 A
T3  - O9  - T3  - O10 - T5  =  57.116 deg; T3  -- T5  = 2.7814 A
T3  - O9  - T3  - O11 - T3  =  90.000 deg; T3  -- T3  = 4.1554 A
T5  - O10 - T3  - O11 - T3  =  94.636 deg; T5  -- T3  = 4.1430 A

T1  - O4  - T4  - O12 - T4  =  85.639 deg; T1  -- T4  = 4.1655 A
T1  - O4  - T4  - O13 - T5  = 146.137 deg; T1  -- T5  = 5.5645 A
T1  - O4  - T4  - O4  - T1  =  66.977 deg; T1  -- T1  = 3.0745 A
T4  - O12 - T4  - O13 - T5  =  89.884 deg; T4  -- T5  = 4.4873 A
T4  - O12 - T4  - O4  - T1  =  85.639 deg; T4  -- T1  = 4.1655 A
T5  - O13 - T4  - O4  - T1  = 146.137 deg; T5  -- T1  = 5.5645 A

T3  - O11 - T5  - O13 - T4  = 146.724 deg; T3  -- T4  = 5.5687 A
T3  - O11 - T5  - O14 - T5  =  85.364 deg; T3  -- T5  = 4.1430 A
T3  - O11 - T5  - O11 - T3  =  65.767 deg; T3  -- T3  = 3.0203 A
T4  - O13 - T5  - O14 - T5  =  90.116 deg; T4  -- T5  = 4.4873 A
T4  - O13 - T5  - O11 - T3  = 146.724 deg; T4  -- T3  = 5.5687 A
T5  - O14 - T5  - O11 - T3  =  85.364 deg; T5  -- T3  = 4.1430 A

        T-T-T SUMMARY
          Range  = 56.5117 deg <--> 147.7430 deg
          Mean   = 100.6052 deg
          StdDev = 27.4539 deg

        T--T SUMMARY
          Range  = 2.7814 A <--> 5.6508 A
          Mean   = 4.3750 A
          StdDev = 0.7689 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 103.085 deg ; T1  -- T1   2.6034 A

T1  -- O2  -- T1  = 126.064 deg ; T1  -- T1   2.8921 A

T1  -- O3  -- T1  = 149.497 deg ; T1  -- T1   3.0745 A

T1  -- O4  -- T4  = 115.884 deg ; T1  -- T4   2.7860 A

T2  -- O5  -- T2  = 167.036 deg ; T2  -- T2   3.1902 A

T2  -- O6  -- T2  = 149.319 deg ; T2  -- T2   3.1915 A

T2  -- O7  -- T2  = 127.389 deg ; T2  -- T2   2.9239 A

T2  -- O8  -- T3  = 114.694 deg ; T2  -- T3   2.7711 A

T3  -- O9  -- T3  = 124.011 deg ; T3  -- T3   2.8540 A

T3  -- O10 -- T3  = 146.177 deg ; T3  -- T3   3.0203 A

T3  -- O11 -- T5  = 115.922 deg ; T3  -- T5   2.7814 A

T4  -- O12 -- T4  = 174.386 deg ; T4  -- T4   3.3159 A

T4  -- O13 -- T5  = 134.641 deg ; T4  -- T5   3.0301 A

T5  -- O14 -- T5  = 173.640 deg ; T5  -- T5   3.3036 A


        T-O-T SUMMARY
          Range  = 103.0850° <--> 174.3856 deg
          Mean   = 134.4329 deg
          StdDev = 20.9915 deg

        T--T SUMMARY
          Range  = 2.6034 A <--> 3.3159 A
          Mean   = 2.9530 A
          StdDev = 0.1980 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.6034 Angstrom
T1  -- T4  = 2.7860 Angstrom
T2  -- T3  = 2.7711 Angstrom
T3  -- T2  = 2.7711 Angstrom
T3  -- T5  = 2.7814 Angstrom
T4  -- T1  = 2.7860 Angstrom
T4  -- T1  = 2.7860 Angstrom
T5  -- T3  = 2.7814 Angstrom
T5  -- T3  = 2.7814 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 6 6 7 8 10 15 18 17 17 20 21 20 20 22 28
TD10 = 109
Circuit symbol = 3.4.4.4.4.5
Weight = 9
Vertex symbol  = 3.4.4.4.4.*
Weight = 9

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 8 11 13 14 14 13 14 14 14 20 26 30 34 36 38
TD10 = 120
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.8.4.*
Weight = 14

T3 (Si): multiplicity = 96
Coordination Sequence =
    1 4 6 8 12 14 12 14 15 14 18 20 20 24 32 38 34
TD10 = 118
Circuit symbol = 3.4.4.4.4.5
Weight = 9
Vertex symbol  = 3.4.4.4.4.*
Weight = 9

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 8 6 10 13 13 16 19 19 18 20 22 20 26 32
TD10 = 116
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.*.4.*
Weight = 8

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 8 10 11 13 12 13 19 20 18 18 22 28 30 36
TD10 = 118
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.*.4.*
Weight = 8

<TD10> = 116.000
Average ring size = 3.8974