Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_9021375_N_jW3W.cif"

There are 384 T-atoms per unit cell
There are 768 O-atoms per unit cell

Framework density = 1.66 T-atoms per nm^3
Material density = 0.166 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6654 Angstrom
T1  -- O2  = 1.5552 Angstrom
T1  -- O3  = 1.6415 Angstrom
T1  -- O4  = 1.6482 Angstrom
      mean = 1.6276 Angstrom
        t1 = 0.054348  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037204  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6387 Angstrom
T2  -- O6  = 1.6360 Angstrom
T2  -- O7  = 1.6305 Angstrom
T2  -- O8  = 1.6978 Angstrom
      mean = 1.6507 Angstrom
        t1 = 0.030467  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011141  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O8  = 1.6325 Angstrom
T3  -- O9  = 1.6164 Angstrom
T3  -- O10 = 1.5771 Angstrom
T3  -- O11 = 1.6387 Angstrom
      mean = 1.6162 Angstrom
        t1 = 0.048963  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.044934  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O4  = 1.6499 Angstrom
T4  -- O12 = 1.6698 Angstrom
T4  -- O13 = 1.6434 Angstrom
T4  -- O4  = 1.6499 Angstrom
      mean = 1.6532 Angstrom
        t1 = 0.028884  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006756  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O11 = 1.6420 Angstrom
T5  -- O13 = 1.6360 Angstrom
T5  -- O14 = 1.6437 Angstrom
T5  -- O11 = 1.6420 Angstrom
      mean = 1.6409 Angstrom
        t1 = 0.021844  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007291  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5552 A <--> 1.6978 A
          Mean   = 1.6354 A
          StdDev = 0.0318 A

       t1 Range  = 0.0218 <-- 0.0369 --> 0.0543
       t2 Range  = 0.0068 <-- 0.0215 --> 0.0449

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 105.180 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.502 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 123.409 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.007 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 101.049 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  = 107.436 deg; O3  -- O4  = 3 A
       101.049 deg <-- 109.264 deg --> 123.409 deg

O5  -- T2  -- O6  = 108.283 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 110.095 deg; O5  -- O7  = 3 A
O5  -- T2  -- O8  = 110.077 deg; O5  -- O8  = 3 A
O6  -- T2  -- O7  = 107.483 deg; O6  -- O7  = 3 A
O6  -- T2  -- O8  = 111.908 deg; O6  -- O8  = 3 A
O7  -- T2  -- O8  = 108.956 deg; O7  -- O8  = 3 A
       107.483 deg <-- 109.467 deg --> 111.908 deg

O8  -- T3  -- O9  = 110.526 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 102.087 deg; O8  -- O10 = 2 A
O8  -- T3  -- O11 = 121.874 deg; O8  -- O11 = 3 A
O9  -- T3  -- O10 = 110.373 deg; O9  -- O10 = 3 A
O9  -- T3  -- O11 = 110.366 deg; O9  -- O11 = 3 A
O10 -- T3  -- O11 = 100.378 deg; O10 -- O11 = 2 A
       100.378 deg <-- 109.267 deg --> 121.874 deg

O4  -- T4  -- O12 = 110.043 deg; O4  -- O12 = 3 A
O4  -- T4  -- O13 = 110.192 deg; O4  -- O13 = 3 A
O4  -- T4  -- O4  = 106.133 deg; O4  -- O4  = 3 A
O12 -- T4  -- O13 = 110.165 deg; O12 -- O13 = 3 A
O12 -- T4  -- O4  = 110.043 deg; O12 -- O4  = 3 A
O13 -- T4  -- O4  = 110.192 deg; O13 -- O4  = 3 A
       106.133 deg <-- 109.461 deg --> 110.192 deg

O11 -- T5  -- O13 = 111.902 deg; O11 -- O13 = 3 A
O11 -- T5  -- O14 = 108.538 deg; O11 -- O14 = 3 A
O11 -- T5  -- O11 = 106.800 deg; O11 -- O11 = 3 A
O13 -- T5  -- O14 = 109.045 deg; O13 -- O14 = 3 A
O13 -- T5  -- O11 = 111.902 deg; O13 -- O11 = 3 A
O14 -- T5  -- O11 = 108.538 deg; O14 -- O11 = 3 A
       106.800 deg <-- 109.454 deg --> 111.902 deg

        O-T-O SUMMARY
          Range  = 100.3784 deg <--> 123.4095 deg
          Mean   = 109.4869 deg
          StdDev = 4.9192 deg

        O--O SUMMARY
          Range  = 2.4706 A <--> 2.9177 A
          Mean   = 2.6753 A
          StdDev = 0.0984 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  89.987 deg; T1  -- T1  = 3.9612 A
T1  - O1  - T1  - O3  - T4  = 146.871 deg; T1  -- T4  = 5.1332 A
T1  - O1  - T1  - O4  - T1  =  90.013 deg; T1  -- T1  = 3.9612 A
T1  - O2  - T1  - O3  - T4  =  93.789 deg; T1  -- T4  = 4.1775 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2086 A
T4  - O3  - T1  - O4  - T1  =  57.130 deg; T4  -- T1  = 2.7410 A

T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.3795 A
T2  - O5  - T2  - O7  - T3  =  87.559 deg; T2  -- T3  = 4.1591 A
T2  - O5  - T2  - O8  - T2  =  90.000 deg; T2  -- T2  = 4.5047 A
T2  - O6  - T2  - O7  - T3  = 137.683 deg; T2  -- T3  = 5.2929 A
T2  - O6  - T2  - O8  - T2  = 135.000 deg; T2  -- T2  = 5.5962 A
T3  - O7  - T2  - O8  - T2  =  87.263 deg; T3  -- T2  = 4.0520 A

T2  - O8  - T3  - O9  - T3  =  92.441 deg; T2  -- T3  = 4.1591 A
T2  - O8  - T3  - O10 - T5  = 148.825 deg; T2  -- T5  = 5.3247 A
T2  - O8  - T3  - O11 - T3  =  92.737 deg; T2  -- T3  = 4.0520 A
T3  - O9  - T3  - O10 - T5  =  57.279 deg; T3  -- T5  = 2.7896 A
T3  - O9  - T3  - O11 - T3  =  90.000 deg; T3  -- T3  = 4.1554 A
T5  - O10 - T3  - O11 - T3  =  94.342 deg; T5  -- T3  = 4.1426 A

T1  - O4  - T4  - O12 - T4  =  86.211 deg; T1  -- T4  = 4.1775 A
T1  - O4  - T4  - O13 - T5  = 146.786 deg; T1  -- T5  = 5.5410 A
T1  - O4  - T4  - O4  - T1  =  65.741 deg; T1  -- T1  = 2.9753 A
T4  - O12 - T4  - O13 - T5  =  89.456 deg; T4  -- T5  = 4.4944 A
T4  - O12 - T4  - O4  - T1  =  86.211 deg; T4  -- T1  = 4.1775 A
T5  - O13 - T4  - O4  - T1  = 146.786 deg; T5  -- T1  = 5.5410 A

T3  - O11 - T5  - O13 - T4  = 146.990 deg; T3  -- T4  = 5.5904 A
T3  - O11 - T5  - O14 - T5  =  85.658 deg; T3  -- T5  = 4.1426 A
T3  - O11 - T5  - O11 - T3  =  65.442 deg; T3  -- T3  = 3.0158 A
T4  - O13 - T5  - O14 - T5  =  90.544 deg; T4  -- T5  = 4.4944 A
T4  - O13 - T5  - O11 - T3  = 146.990 deg; T4  -- T3  = 5.5904 A
T5  - O14 - T5  - O11 - T3  =  85.658 deg; T5  -- T3  = 4.1426 A

        T-T-T SUMMARY
          Range  = 57.1295 deg <--> 148.8251 deg
          Mean   = 100.8552 deg
          StdDev = 28.7738 deg

        T--T SUMMARY
          Range  = 2.7410 A <--> 5.5962 A
          Mean   = 4.3621 A
          StdDev = 0.8264 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 103.420 deg ; T1  -- T1   2.6143 A

T1  -- O2  -- T1  = 146.109 deg ; T1  -- T1   2.9753 A

T1  -- O3  -- T1  = 130.101 deg ; T1  -- T1   2.9765 A

T1  -- O4  -- T4  = 112.422 deg ; T1  -- T4   2.7410 A

T2  -- O5  -- T2  = 144.375 deg ; T2  -- T2   3.1202 A

T2  -- O6  -- T2  = 166.455 deg ; T2  -- T2   3.2491 A

T2  -- O7  -- T2  = 128.450 deg ; T2  -- T2   2.9366 A

T2  -- O8  -- T3  = 110.611 deg ; T2  -- T3   2.7384 A

T3  -- O9  -- T3  = 124.323 deg ; T3  -- T3   2.8587 A

T3  -- O10 -- T3  = 145.940 deg ; T3  -- T3   3.0158 A

T3  -- O11 -- T5  = 116.490 deg ; T3  -- T5   2.7896 A

T4  -- O12 -- T4  = 177.514 deg ; T4  -- T4   3.3388 A

T4  -- O13 -- T5  = 135.992 deg ; T4  -- T5   3.0405 A

T5  -- O14 -- T5  = 172.890 deg ; T5  -- T5   3.2811 A


        T-O-T SUMMARY
          Range  = 103.4196° <--> 177.5139 deg
          Mean   = 133.7515 deg
          StdDev = 21.0770 deg

        T--T SUMMARY
          Range  = 2.6143 A <--> 3.3388 A
          Mean   = 2.9477 A
          StdDev = 0.1989 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.6143 Angstrom
T1  -- T4  = 2.7410 Angstrom
T2  -- T3  = 2.7384 Angstrom
T3  -- T2  = 2.7384 Angstrom
T3  -- T5  = 2.7896 Angstrom
T4  -- T1  = 2.7410 Angstrom
T4  -- T1  = 2.7410 Angstrom
T5  -- T3  = 2.7896 Angstrom
T5  -- T3  = 2.7896 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 6 6 7 8 10 15 18 17 17 20 21 20 20 22 28
TD10 = 109
Circuit symbol = 3.4.4.4.4.5
Weight = 9
Vertex symbol  = 3.4.4.4.4.*
Weight = 9

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 8 11 13 14 14 13 14 14 14 20 26 30 34 36 38
TD10 = 120
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.8.4.*
Weight = 14

T3 (Si): multiplicity = 96
Coordination Sequence =
    1 4 6 8 12 14 12 14 15 14 18 20 20 24 32 38 34
TD10 = 118
Circuit symbol = 3.4.4.4.4.5
Weight = 9
Vertex symbol  = 3.4.4.4.4.*
Weight = 9

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 8 6 10 13 13 16 19 19 18 20 22 20 26 32
TD10 = 116
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.*.4.*
Weight = 8

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 8 10 11 13 12 13 19 20 18 18 22 28 30 36
TD10 = 118
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.*.4.*
Weight = 8

<TD10> = 116.000
Average ring size = 3.8974