Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_9014299_O4QGkq.cif"

There are 384 T-atoms per unit cell
There are 768 O-atoms per unit cell

Framework density = 1.66 T-atoms per nm^3
Material density = 0.166 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6422 Angstrom
T1  -- O2  = 1.6299 Angstrom
T1  -- O3  = 1.6250 Angstrom
T1  -- O4  = 1.6945 Angstrom
      mean = 1.6479 Angstrom
        t1 = 0.033920  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.028907  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6606 Angstrom
T2  -- O5  = 1.6229 Angstrom
T2  -- O6  = 1.5860 Angstrom
T2  -- O7  = 1.6382 Angstrom
      mean = 1.6269 Angstrom
        t1 = 0.048624  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037603  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O8  = 1.6426 Angstrom
T3  -- O9  = 1.6076 Angstrom
T3  -- O10 = 1.6427 Angstrom
T3  -- O11 = 1.6363 Angstrom
      mean = 1.6323 Angstrom
        t1 = 0.028746  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025130  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6413 Angstrom
T4  -- O12 = 1.6530 Angstrom
T4  -- O13 = 1.6449 Angstrom
T4  -- O7  = 1.6413 Angstrom
      mean = 1.6451 Angstrom
        t1 = 0.024040  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008477  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O11 = 1.6314 Angstrom
T5  -- O13 = 1.6352 Angstrom
T5  -- O14 = 1.6057 Angstrom
T5  -- O11 = 1.6314 Angstrom
      mean = 1.6259 Angstrom
        t1 = 0.020625  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016573  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5860 A <--> 1.6945 A
          Mean   = 1.6357 A
          StdDev = 0.0230 A

       t1 Range  = 0.0206 <-- 0.0312 --> 0.0486
       t2 Range  = 0.0085 <-- 0.0233 --> 0.0376

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.367 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 104.641 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 114.163 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.290 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.463 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.807 deg; O3  -- O4  = 3 A
       104.641 deg <-- 109.455 deg --> 114.163 deg

O4  -- T2  -- O5  = 111.004 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 103.811 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 121.122 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.599 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 110.085 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  =  99.985 deg; O6  -- O7  = 2 A
       99.985 deg <-- 109.267 deg --> 121.122 deg

O8  -- T3  -- O9  = 107.621 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 113.316 deg; O8  -- O10 = 3 A
O8  -- T3  -- O11 = 110.932 deg; O8  -- O11 = 3 A
O9  -- T3  -- O10 = 108.150 deg; O9  -- O10 = 3 A
O9  -- T3  -- O11 = 103.673 deg; O9  -- O11 = 3 A
O10 -- T3  -- O11 = 112.531 deg; O10 -- O11 = 3 A
       103.673 deg <-- 109.370 deg --> 113.316 deg

O7  -- T4  -- O12 = 108.225 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 = 111.017 deg; O7  -- O13 = 3 A
O7  -- T4  -- O7  = 107.151 deg; O7  -- O7  = 3 A
O12 -- T4  -- O13 = 111.057 deg; O12 -- O13 = 3 A
O12 -- T4  -- O7  = 108.225 deg; O12 -- O7  = 3 A
O13 -- T4  -- O7  = 111.017 deg; O13 -- O7  = 3 A
       107.151 deg <-- 109.449 deg --> 111.057 deg

O11 -- T5  -- O13 = 112.647 deg; O11 -- O13 = 3 A
O11 -- T5  -- O14 = 107.098 deg; O11 -- O14 = 3 A
O11 -- T5  -- O11 = 108.615 deg; O11 -- O11 = 3 A
O13 -- T5  -- O14 = 108.440 deg; O13 -- O14 = 3 A
O13 -- T5  -- O11 = 112.647 deg; O13 -- O11 = 3 A
O14 -- T5  -- O11 = 107.098 deg; O14 -- O11 = 3 A
       107.098 deg <-- 109.425 deg --> 112.647 deg

        O-T-O SUMMARY
          Range  = 99.9848 deg <--> 121.1215 deg
          Mean   = 109.4336 deg
          StdDev = 3.9515 deg

        O--O SUMMARY
          Range  = 2.4698 A <--> 2.8728 A
          Mean   = 2.6710 A
          StdDev = 0.0801 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.2057 A
T1  - O1  - T1  - O3  - T2  = 176.224 deg; T1  -- T2  = 5.4296 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2057 A
T1  - O2  - T1  - O3  - T2  =  88.245 deg; T1  -- T2  = 4.1263 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.5264 A
T2  - O3  - T1  - O4  - T1  =  86.658 deg; T2  -- T1  = 4.0679 A

T1  - O4  - T2  - O5  - T2  =  91.755 deg; T1  -- T2  = 4.1263 A
T1  - O4  - T2  - O6  - T4  = 147.829 deg; T1  -- T4  = 5.2802 A
T1  - O4  - T2  - O7  - T2  =  93.342 deg; T1  -- T2  = 4.0679 A
T2  - O5  - T2  - O6  - T4  =  57.065 deg; T2  -- T4  = 2.7912 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.1877 A
T4  - O6  - T2  - O7  - T2  =  94.272 deg; T4  -- T2  = 4.1612 A

T3  - O8  - T3  - O9  - T3  =  90.000 deg; T3  -- T3  = 4.2167 A
T3  - O8  - T3  - O10 - T5  =  58.233 deg; T3  -- T5  = 2.8661 A
T3  - O8  - T3  - O11 - T3  =  90.000 deg; T3  -- T3  = 4.1991 A
T3  - O9  - T3  - O10 - T5  = 124.639 deg; T3  -- T5  = 5.1462 A
T3  - O9  - T3  - O11 - T3  = 135.000 deg; T3  -- T3  = 5.4183 A
T5  - O10 - T3  - O11 - T3  =  92.588 deg; T5  -- T3  = 4.1827 A

T2  - O7  - T4  - O12 - T4  =  85.728 deg; T2  -- T4  = 4.1612 A
T2  - O7  - T4  - O13 - T5  = 146.538 deg; T2  -- T5  = 5.5117 A
T2  - O7  - T4  - O7  - T2  =  65.870 deg; T2  -- T2  = 3.0350 A
T4  - O12 - T4  - O13 - T5  =  88.814 deg; T4  -- T5  = 4.3907 A
T4  - O12 - T4  - O7  - T2  =  85.728 deg; T4  -- T2  = 4.1612 A
T5  - O13 - T4  - O7  - T2  = 146.538 deg; T5  -- T2  = 5.5117 A

T3  - O11 - T5  - O13 - T4  = 148.184 deg; T3  -- T4  = 5.6068 A
T3  - O11 - T5  - O14 - T5  =  87.412 deg; T3  -- T5  = 4.1827 A
T3  - O11 - T5  - O11 - T3  =  63.535 deg; T3  -- T3  = 3.0179 A
T4  - O13 - T5  - O14 - T5  =  91.186 deg; T4  -- T5  = 4.3907 A
T4  - O13 - T5  - O11 - T3  = 148.184 deg; T4  -- T3  = 5.6068 A
T5  - O14 - T5  - O11 - T3  =  87.412 deg; T5  -- T3  = 4.1827 A

        T-T-T SUMMARY
          Range  = 57.0648 deg <--> 176.2244 deg
          Mean   = 101.9128 deg
          StdDev = 29.1535 deg

        T--T SUMMARY
          Range  = 2.7912 A <--> 5.6068 A
          Mean   = 4.3993 A
          StdDev = 0.7689 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 112.338 deg ; T1  -- T1   2.7283 A

T1  -- O2  -- T1  = 158.127 deg ; T1  -- T1   3.2007 A

T1  -- O3  -- T1  = 159.991 deg ; T1  -- T1   3.2007 A

T1  -- O4  -- T2  = 107.407 deg ; T1  -- T2   2.7042 A

T2  -- O5  -- T2  = 125.489 deg ; T2  -- T2   2.8854 A

T2  -- O6  -- T2  = 146.195 deg ; T2  -- T2   3.0350 A

T2  -- O7  -- T4  = 116.665 deg ; T2  -- T4   2.7912 A

T3  -- O8  -- T3  = 125.431 deg ; T3  -- T3   2.9197 A

T3  -- O9  -- T3  = 139.646 deg ; T3  -- T3   3.0179 A

T3  -- O10 -- T3  = 127.384 deg ; T3  -- T3   2.9450 A

T3  -- O11 -- T5  = 122.594 deg ; T3  -- T5   2.8661 A

T4  -- O12 -- T4  = 173.916 deg ; T4  -- T4   3.3013 A

T4  -- O13 -- T5  = 129.268 deg ; T4  -- T5   2.9639 A

T5  -- O14 -- T5  = 163.616 deg ; T5  -- T5   3.1786 A


        T-O-T SUMMARY
          Range  = 107.4065° <--> 173.9164 deg
          Mean   = 133.9732 deg
          StdDev = 18.9421 deg

        T--T SUMMARY
          Range  = 2.7042 A <--> 3.3013 A
          Mean   = 2.9613 A
          StdDev = 0.1723 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7283 Angstrom
T1  -- T2  = 2.7042 Angstrom
T2  -- T1  = 2.7042 Angstrom
T2  -- T4  = 2.7912 Angstrom
T4  -- T2  = 2.7912 Angstrom
T4  -- T2  = 2.7912 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 7 6 7 9 12 15 17 20 23 24 22 20 20 24
TD10 = 105
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.*
Weight = 10

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 6 7 8 8 10 12 14 18 20 21 21 22 22 24 28
TD10 = 108
Circuit symbol = 3.4.4.4.4.5
Weight = 9
Vertex symbol  = 3.4.4.4.4.*
Weight = 9

T3 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 10 13 14 15 16 14 14 14 16 22 26 32 38 42
TD10 = 122
Circuit symbol = 3.6.4.4.4.5
Weight = 8
Vertex symbol  = 3.8.4.4.4.*
Weight = 13

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 8 9 11 10 13 15 18 20 18 20 22 26 30 30
TD10 = 116
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.*.4.*
Weight = 8

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 9 11 12 13 13 16 16 16 18 18 24 30 34 38
TD10 = 118
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.*.4.*
Weight = 8

<TD10> = 113.000
Average ring size = 3.8974