Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_8999661_inNsMX.cif"

There are 384 T-atoms per unit cell
There are 768 O-atoms per unit cell

Framework density = 1.99 T-atoms per nm^3
Material density = 0.199 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6078 Angstrom
T1  -- O2  = 1.6296 Angstrom
T1  -- O3  = 1.6956 Angstrom
T1  -- O4  = 1.6424 Angstrom
      mean = 1.6439 Angstrom
        t1 = 0.035628  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017991  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6658 Angstrom
T2  -- O5  = 1.6202 Angstrom
T2  -- O6  = 1.5883 Angstrom
T2  -- O7  = 1.6368 Angstrom
      mean = 1.6278 Angstrom
        t1 = 0.048515  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.035930  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6467 Angstrom
T3  -- O8  = 1.6236 Angstrom
T3  -- O9  = 1.6216 Angstrom
T3  -- O10 = 1.6648 Angstrom
      mean = 1.6392 Angstrom
        t1 = 0.027210  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014564  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.6347 Angstrom
T4  -- O10 = 1.6347 Angstrom
T4  -- O11 = 1.6074 Angstrom
T4  -- O11 = 1.6074 Angstrom
      mean = 1.6210 Angstrom
        t1 = 0.023079  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014817  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6416 Angstrom
T5  -- O12 = 1.6566 Angstrom
T5  -- O13 = 1.6248 Angstrom
T5  -- O7  = 1.6416 Angstrom
      mean = 1.6412 Angstrom
        t1 = 0.020545  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004473  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5883 A <--> 1.6956 A
          Mean   = 1.6355 A
          StdDev = 0.0254 A

       t1 Range  = 0.0205 <-- 0.0310 --> 0.0485
       t2 Range  = 0.0045 <-- 0.0176 --> 0.0359

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.334 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.649 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.994 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.671 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 105.066 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 115.953 deg; O3  -- O4  = 3 A
       105.066 deg <-- 109.445 deg --> 115.953 deg

O3  -- T2  -- O5  = 110.641 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 104.218 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 121.449 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 110.001 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.382 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 100.120 deg; O6  -- O7  = 2 A
       100.120 deg <-- 109.302 deg --> 121.449 deg

O4  -- T3  -- O8  = 108.878 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 108.139 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 115.087 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 108.526 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 107.359 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 108.692 deg; O9  -- O10 = 3 A
       107.359 deg <-- 109.447 deg --> 115.087 deg

O10 -- T4  -- O10 = 116.224 deg; O10 -- O10 = 3 A
O10 -- T4  -- O11 = 108.117 deg; O10 -- O11 = 3 A
O10 -- T4  -- O11 = 107.498 deg; O10 -- O11 = 3 A
O10 -- T4  -- O11 = 107.498 deg; O10 -- O11 = 3 A
O10 -- T4  -- O11 = 108.117 deg; O10 -- O11 = 3 A
O11 -- T4  -- O11 = 109.252 deg; O11 -- O11 = 3 A
       107.498 deg <-- 109.451 deg --> 116.224 deg

O7  -- T5  -- O12 = 109.381 deg; O7  -- O12 = 3 A
O7  -- T5  -- O13 = 110.206 deg; O7  -- O13 = 3 A
O7  -- T5  -- O7  = 107.049 deg; O7  -- O7  = 3 A
O12 -- T5  -- O13 = 110.546 deg; O12 -- O13 = 3 A
O12 -- T5  -- O7  = 109.381 deg; O12 -- O7  = 3 A
O13 -- T5  -- O7  = 110.207 deg; O13 -- O7  = 3 A
       107.049 deg <-- 109.461 deg --> 110.546 deg

        O-T-O SUMMARY
          Range  = 100.1199 deg <--> 121.4488 deg
          Mean   = 109.4007 deg
          StdDev = 3.9626 deg

        O--O SUMMARY
          Range  = 2.4729 A <--> 2.8808 A
          Mean   = 2.6692 A
          StdDev = 0.0797 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  88.468 deg; T1  -- T2  = 4.1033 A
T1  - O1  - T1  - O3  - T3  =  88.683 deg; T1  -- T3  = 4.1813 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4966 A
T2  - O2  - T1  - O3  - T3  = 176.128 deg; T2  -- T3  = 5.4663 A
T2  - O2  - T1  - O4  - T1  =  86.738 deg; T2  -- T1  = 4.0401 A
T3  - O3  - T1  - O4  - T1  =  90.641 deg; T3  -- T1  = 4.2531 A

T1  - O3  - T2  - O5  - T2  =  91.532 deg; T1  -- T2  = 4.1033 A
T1  - O3  - T2  - O6  - T5  = 147.829 deg; T1  -- T5  = 5.2727 A
T1  - O3  - T2  - O7  - T2  =  93.262 deg; T1  -- T2  = 4.0401 A
T2  - O5  - T2  - O6  - T5  =  57.265 deg; T2  -- T5  = 2.8075 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.1812 A
T5  - O6  - T2  - O7  - T2  =  94.260 deg; T5  -- T2  = 4.1646 A

T1  - O4  - T3  - O8  - T3  =  89.359 deg; T1  -- T3  = 4.2531 A
T1  - O4  - T3  - O9  - T4  = 177.124 deg; T1  -- T4  = 5.5828 A
T1  - O4  - T3  - O10 - T3  =  91.317 deg; T1  -- T3  = 4.1813 A
T3  - O8  - T3  - O9  - T4  =  89.242 deg; T3  -- T4  = 4.2525 A
T3  - O8  - T3  - O10 - T3  =  90.000 deg; T3  -- T3  = 4.4521 A
T4  - O9  - T3  - O10 - T3  =  91.196 deg; T4  -- T3  = 4.1809 A

T3  - O10 - T4  - O10 - T3  = 179.380 deg; T3  -- T3  = 5.5902 A
T3  - O10 - T4  - O11 - T4  =  90.758 deg; T3  -- T4  = 4.2525 A
T3  - O10 - T4  - O11 - T4  =  88.804 deg; T3  -- T4  = 4.1809 A
T3  - O10 - T4  - O11 - T4  =  88.804 deg; T3  -- T4  = 4.1809 A
T3  - O10 - T4  - O11 - T4  =  90.758 deg; T3  -- T4  = 4.2525 A
T4  - O11 - T4  - O11 - T4  =  90.000 deg; T4  -- T4  = 4.4803 A

T2  - O7  - T5  - O12 - T5  =  85.740 deg; T2  -- T5  = 4.1646 A
T2  - O7  - T5  - O13 - T5  = 130.166 deg; T2  -- T5  = 5.3519 A
T2  - O7  - T5  - O7  - T2  =  65.471 deg; T2  -- T2  = 3.0363 A
T5  - O12 - T5  - O13 - T5  = 135.000 deg; T5  -- T5  = 5.8985 A
T5  - O12 - T5  - O7  - T2  =  85.740 deg; T5  -- T2  = 4.1646 A
T5  - O13 - T5  - O7  - T2  = 130.166 deg; T5  -- T2  = 5.3519 A

        T-T-T SUMMARY
          Range  = 57.2646 deg <--> 179.3803 deg
          Mean   = 103.4896 deg
          StdDev = 31.0977 deg

        T--T SUMMARY
          Range  = 2.8075 A <--> 5.8985 A
          Mean   = 4.4283 A
          StdDev = 0.6398 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 162.848 deg ; T1  -- T1   3.1796 A

T1  -- O2  -- T1  = 154.614 deg ; T1  -- T1   3.1796 A

T1  -- O3  -- T2  = 105.740 deg ; T1  -- T2   2.6800 A

T1  -- O4  -- T3  = 116.006 deg ; T1  -- T3   2.7894 A

T2  -- O5  -- T2  = 125.028 deg ; T2  -- T2   2.8746 A

T2  -- O6  -- T2  = 145.831 deg ; T2  -- T2   3.0363 A

T2  -- O7  -- T5  = 117.820 deg ; T2  -- T5   2.8075 A

T3  -- O8  -- T3  = 140.007 deg ; T3  -- T3   3.0514 A

T3  -- O9  -- T3  = 176.901 deg ; T3  -- T3   3.2420 A

T3  -- O10 -- T4  = 115.800 deg ; T3  -- T4   2.7951 A

T4  -- O11 -- T4  = 160.440 deg ; T4  -- T4   3.1680 A

T5  -- O12 -- T5  = 166.905 deg ; T5  -- T5   3.2917 A

T5  -- O13 -- T5  = 144.187 deg ; T5  -- T5   3.0923 A


        T-O-T SUMMARY
          Range  = 105.7399° <--> 176.9013 deg
          Mean   = 138.8139 deg
          StdDev = 22.3629 deg

        T--T SUMMARY
          Range  = 2.6800 A <--> 3.2917 A
          Mean   = 2.9923 A
          StdDev = 0.1932 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.6800 Angstrom
T1  -- T3  = 2.7894 Angstrom
T2  -- T1  = 2.6800 Angstrom
T3  -- T1  = 2.7894 Angstrom
T3  -- T4  = 2.7951 Angstrom
T4  -- T3  = 2.7951 Angstrom
T4  -- T3  = 2.7951 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 7 8 12 15 15 16 20 23 24 22 24 30 40 44
TD10 = 128
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.*
Weight = 10

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 6 8 12 15 16 16 15 16 20 21 24 30 40 46 48
TD10 = 129
Circuit symbol = 3.4.4.4.4.5
Weight = 9
Vertex symbol  = 3.4.4.4.4.*
Weight = 9

T3 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 8 7 8 11 15 20 23 24 24 24 22 24 28 40
TD10 = 128
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.*
Weight = 10

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 8 8 6 8 16 22 24 24 24 24 24 20 24 36
TD10 = 128
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.*
Weight = 10

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 8 12 15 16 16 16 16 14 16 22 30 40 46 48 48
TD10 = 134
Circuit symbol = 3.8.4.10.4.10
Weight = 12
Vertex symbol  = 3.8.4.*.4.*
Weight = 12

<TD10> = 129.000
Average ring size = 3.9494