Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_8042086_MNhRDv.cif"

There are 432 T-atoms per unit cell
There are 864 O-atoms per unit cell

Framework density = 2.43 T-atoms per nm^3
Material density = 0.242 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6367 Angstrom
T1  -- O2  = 1.6091 Angstrom
T1  -- O3  = 1.6261 Angstrom
T1  -- O4  = 1.6231 Angstrom
      mean = 1.6237 Angstrom
        t1 = 0.022262  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.028135  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6374 Angstrom
T2  -- O5  = 1.6366 Angstrom
T2  -- O6  = 1.6272 Angstrom
T2  -- O7  = 1.6519 Angstrom
      mean = 1.6383 Angstrom
        t1 = 0.019698  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005880  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6244 Angstrom
T3  -- O7  = 1.6426 Angstrom
T3  -- O8  = 1.6040 Angstrom
T3  -- O9  = 1.6281 Angstrom
      mean = 1.6248 Angstrom
        t1 = 0.020429  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012233  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.6361 Angstrom
T4  -- O10 = 1.6327 Angstrom
T4  -- O11 = 1.6325 Angstrom
T4  -- O12 = 1.6623 Angstrom
      mean = 1.6409 Angstrom
        t1 = 0.020001  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004034  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.6255 Angstrom
T5  -- O12 = 1.6255 Angstrom
T5  -- O13 = 1.5927 Angstrom
T5  -- O13 = 1.5927 Angstrom
      mean = 1.6091 Angstrom
        t1 = 0.024755  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017905  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5927 A <--> 1.6623 A
          Mean   = 1.6294 A
          StdDev = 0.0158 A

       t1 Range  = 0.0197 <-- 0.0214 --> 0.0248
       t2 Range  = 0.0040 <-- 0.0136 --> 0.0281

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.322 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 115.196 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.086 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 105.905 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.246 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 106.885 deg; O3  -- O4  = 3 A
       105.905 deg <-- 109.440 deg --> 115.196 deg

O3  -- T2  -- O5  = 109.546 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 110.338 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 106.108 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.752 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.520 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 111.504 deg; O6  -- O7  = 3 A
       106.108 deg <-- 109.461 deg --> 111.504 deg

O4  -- T3  -- O7  = 108.672 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 109.435 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.650 deg; O4  -- O9  = 3 A
O7  -- T3  -- O8  = 106.889 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 114.514 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 107.564 deg; O8  -- O9  = 3 A
       106.889 deg <-- 109.454 deg --> 114.514 deg

O9  -- T4  -- O10 = 109.806 deg; O9  -- O10 = 3 A
O9  -- T4  -- O11 = 109.605 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 109.708 deg; O9  -- O12 = 3 A
O10 -- T4  -- O11 = 108.744 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.639 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.320 deg; O11 -- O12 = 3 A
       108.744 deg <-- 109.470 deg --> 109.806 deg

O12 -- T5  -- O12 = 116.944 deg; O12 -- O12 = 3 A
O12 -- T5  -- O13 = 107.203 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 107.660 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 107.660 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 107.203 deg; O12 -- O13 = 3 A
O13 -- T5  -- O13 = 110.097 deg; O13 -- O13 = 3 A
       107.203 deg <-- 109.461 deg --> 116.944 deg

        O-T-O SUMMARY
          Range  = 105.9054 deg <--> 116.9445 deg
          Mean   = 109.4560 deg
          StdDev = 2.5264 deg

        O--O SUMMARY
          Range  = 2.5821 A <--> 2.7710 A
          Mean   = 2.6575 A
          StdDev = 0.0507 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  92.466 deg; T1  -- T2  = 4.1957 A
T1  - O1  - T1  - O3  - T3  =  89.901 deg; T1  -- T3  = 4.2185 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.0696 A
T2  - O2  - T1  - O3  - T3  =  57.347 deg; T2  -- T3  = 2.7430 A
T2  - O2  - T1  - O4  - T1  = 175.638 deg; T2  -- T1  = 5.4810 A
T3  - O3  - T1  - O4  - T1  = 119.093 deg; T3  -- T1  = 4.8725 A

T1  - O3  - T2  - O5  - T2  = 131.354 deg; T1  -- T2  = 5.1964 A
T1  - O3  - T2  - O6  - T3  =  64.364 deg; T1  -- T3  = 2.9372 A
T1  - O3  - T2  - O7  - T2  =  87.534 deg; T1  -- T2  = 4.1957 A
T2  - O5  - T2  - O6  - T3  = 163.958 deg; T2  -- T3  = 5.6182 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.3921 A
T3  - O6  - T2  - O7  - T2  =  87.403 deg; T3  -- T2  = 4.1729 A

T1  - O4  - T3  - O7  - T2  =  58.288 deg; T1  -- T2  = 2.7715 A
T1  - O4  - T3  - O8  - T4  = 126.011 deg; T1  -- T4  = 5.2128 A
T1  - O4  - T3  - O9  - T3  =  90.099 deg; T1  -- T3  = 4.2185 A
T2  - O7  - T3  - O8  - T4  = 173.452 deg; T2  -- T4  = 5.6468 A
T2  - O7  - T3  - O9  - T3  =  92.597 deg; T2  -- T3  = 4.1729 A
T4  - O8  - T3  - O9  - T3  =  92.335 deg; T4  -- T3  = 4.2826 A

T3  - O9  - T4  - O10 - T4  =  87.665 deg; T3  -- T4  = 4.2826 A
T3  - O9  - T4  - O11 - T5  = 154.757 deg; T3  -- T5  = 5.6108 A
T3  - O9  - T4  - O12 - T4  = 114.834 deg; T3  -- T4  = 5.0872 A
T4  - O10 - T4  - O11 - T5  =  88.750 deg; T4  -- T5  = 4.2747 A
T4  - O10 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 4.5146 A
T5  - O11 - T4  - O12 - T4  =  90.136 deg; T5  -- T4  = 4.2240 A

T4  - O12 - T5  - O12 - T4  = 178.425 deg; T4  -- T4  = 5.6730 A
T4  - O12 - T5  - O13 - T5  =  91.250 deg; T4  -- T5  = 4.2747 A
T4  - O12 - T5  - O13 - T5  =  89.864 deg; T4  -- T5  = 4.2240 A
T4  - O12 - T5  - O13 - T5  =  89.864 deg; T4  -- T5  = 4.2240 A
T4  - O12 - T5  - O13 - T5  =  91.250 deg; T4  -- T5  = 4.2747 A
T5  - O13 - T5  - O13 - T5  =  90.000 deg; T5  -- T5  = 4.4356 A

        T-T-T SUMMARY
          Range  = 57.3473 deg <--> 178.4254 deg
          Mean   = 104.3232 deg
          StdDev = 33.0309 deg

        T--T SUMMARY
          Range  = 2.7430 A <--> 5.6730 A
          Mean   = 4.4370 A
          StdDev = 0.7691 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 111.985 deg ; T1  -- T1   2.7135 A

T1  -- O2  -- T1  = 140.935 deg ; T1  -- T1   3.0330 A

T1  -- O3  -- T2  = 116.263 deg ; T1  -- T2   2.7715 A

T1  -- O4  -- T3  = 129.505 deg ; T1  -- T3   2.9372 A

T2  -- O5  -- T2  = 176.202 deg ; T2  -- T2   3.2715 A

T2  -- O6  -- T2  = 128.450 deg ; T2  -- T2   2.9306 A

T2  -- O7  -- T3  = 112.736 deg ; T2  -- T3   2.7430 A

T3  -- O8  -- T3  = 140.885 deg ; T3  -- T3   3.0228 A

T3  -- O9  -- T4  = 126.354 deg ; T3  -- T4   2.9129 A

T4  -- O10 -- T4  = 146.017 deg ; T4  -- T4   3.1230 A

T4  -- O11 -- T4  = 173.779 deg ; T4  -- T4   3.2602 A

T4  -- O12 -- T5  = 119.268 deg ; T4  -- T5   2.8368 A

T5  -- O13 -- T5  = 159.894 deg ; T5  -- T5   3.1365 A


        T-O-T SUMMARY
          Range  = 111.9855° <--> 176.2019 deg
          Mean   = 136.1863 deg
          StdDev = 20.9021 deg

        T--T SUMMARY
          Range  = 2.7135 A <--> 3.2715 A
          Mean   = 2.9699 A
          StdDev = 0.1788 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7715 Angstrom
T1  -- T1  = 2.7135 Angstrom
T2  -- T1  = 2.7715 Angstrom
T2  -- T3  = 2.7430 Angstrom
T3  -- T2  = 2.7430 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 9 11 14 18 20 21 23 26 30 36 44 49 52 58
TD10 = 154
Circuit symbol = 3.4.4.6.4.6_{2}
Weight = 11
Vertex symbol  = 3.4.4.6.4.16
Weight = 24

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 10 13 14 16 21 24 23 26 34 39 42 48 55 60
TD10 = 159
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.16.4.*
Weight = 21

T3 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 10 11 14 17 19 23 26 29 31 36 42 46 52 62
TD10 = 161
Circuit symbol = 3.4.4.6.4.6_{2}
Weight = 11
Vertex symbol  = 3.4.4.6.4.*
Weight = 11

T4 (Si): multiplicity = 96
Coordination Sequence =
    1 4 8 10 11 13 16 20 24 28 30 31 33 38 46 55 65
TD10 = 165
Circuit symbol = 4.4.4.6.4.6_{2}
Weight = 12
Vertex symbol  = 4.4.4.6.4.*
Weight = 12

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 10 12 12 14 20 26 28 30 32 32 34 44 58 66
TD10 = 164
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.*
Weight = 10

<TD10> = 160.222
Average ring size = 4.2727