Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_8024873_r7tTvu.cif"

There are 432 T-atoms per unit cell
There are 864 O-atoms per unit cell

Framework density = 2.41 T-atoms per nm^3
Material density = 0.241 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6120 Angstrom
T1  -- O2  = 1.6409 Angstrom
T1  -- O3  = 1.6508 Angstrom
T1  -- O4  = 1.6641 Angstrom
      mean = 1.6420 Angstrom
        t1 = 0.022140  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007489  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6364 Angstrom
T2  -- O5  = 1.6066 Angstrom
T2  -- O6  = 1.6445 Angstrom
T2  -- O7  = 1.6249 Angstrom
      mean = 1.6281 Angstrom
        t1 = 0.021407  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026407  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6518 Angstrom
T3  -- O8  = 1.6362 Angstrom
T3  -- O9  = 1.6280 Angstrom
T3  -- O10 = 1.6362 Angstrom
      mean = 1.6381 Angstrom
        t1 = 0.019689  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010785  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6251 Angstrom
T4  -- O10 = 1.6265 Angstrom
T4  -- O11 = 1.6347 Angstrom
T4  -- O12 = 1.6098 Angstrom
      mean = 1.6240 Angstrom
        t1 = 0.021687  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013420  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O4  = 1.6265 Angstrom
T5  -- O4  = 1.6265 Angstrom
T5  -- O13 = 1.5931 Angstrom
T5  -- O13 = 1.5931 Angstrom
      mean = 1.6098 Angstrom
        t1 = 0.025060  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017187  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5931 A <--> 1.6641 A
          Mean   = 1.6305 A
          StdDev = 0.0171 A

       t1 Range  = 0.0197 <-- 0.0220 --> 0.0251
       t2 Range  = 0.0075 <-- 0.0151 --> 0.0264

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.819 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.377 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.664 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.250 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.866 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.835 deg; O3  -- O4  = 3 A
       108.664 deg <-- 109.468 deg --> 110.250 deg

O3  -- T2  -- O5  = 108.132 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 114.402 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.680 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 106.704 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.318 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.483 deg; O6  -- O7  = 3 A
       106.704 deg <-- 109.453 deg --> 114.402 deg

O6  -- T3  -- O8  = 109.463 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 111.598 deg; O6  -- O9  = 3 A
O6  -- T3  -- O10 = 106.164 deg; O6  -- O10 = 3 A
O8  -- T3  -- O9  = 109.627 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.528 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 110.393 deg; O9  -- O10 = 3 A
       106.164 deg <-- 109.462 deg --> 111.598 deg

O7  -- T4  -- O10 = 106.984 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 110.007 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.346 deg; O7  -- O12 = 3 A
O10 -- T4  -- O11 = 115.116 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 105.963 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.243 deg; O11 -- O12 = 3 A
       105.963 deg <-- 109.443 deg --> 115.116 deg

O4  -- T5  -- O4  = 117.034 deg; O4  -- O4  = 3 A
O4  -- T5  -- O13 = 107.711 deg; O4  -- O13 = 3 A
O4  -- T5  -- O13 = 107.160 deg; O4  -- O13 = 3 A
O4  -- T5  -- O13 = 107.160 deg; O4  -- O13 = 3 A
O4  -- T5  -- O13 = 107.711 deg; O4  -- O13 = 3 A
O13 -- T5  -- O13 = 109.978 deg; O13 -- O13 = 3 A
       107.160 deg <-- 109.459 deg --> 117.034 deg

        O-T-O SUMMARY
          Range  = 105.9635 deg <--> 117.0343 deg
          Mean   = 109.4601 deg
          StdDev = 2.5204 deg

        O--O SUMMARY
          Range  = 2.5840 A <--> 2.7741 A
          Mean   = 2.6596 A
          StdDev = 0.0513 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 113.970 deg; T1  -- T2  = 5.1211 A
T1  - O1  - T1  - O3  - T5  =  89.398 deg; T1  -- T5  = 4.2555 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.5218 A
T2  - O2  - T1  - O3  - T5  = 156.529 deg; T2  -- T5  = 5.6288 A
T2  - O2  - T1  - O4  - T1  =  88.478 deg; T2  -- T1  = 4.2637 A
T5  - O3  - T1  - O4  - T1  =  89.398 deg; T5  -- T1  = 4.2555 A

T1  - O3  - T2  - O5  - T3  = 173.563 deg; T1  -- T3  = 5.6515 A
T1  - O3  - T2  - O6  - T4  = 126.973 deg; T1  -- T4  = 5.2279 A
T1  - O3  - T2  - O7  - T2  =  91.522 deg; T1  -- T2  = 4.2637 A
T3  - O5  - T2  - O6  - T4  =  58.166 deg; T3  -- T4  = 2.7698 A
T3  - O5  - T2  - O7  - T2  =  92.370 deg; T3  -- T2  = 4.1874 A
T4  - O6  - T2  - O7  - T2  =  90.044 deg; T4  -- T2  = 4.2296 A

T2  - O6  - T3  - O8  - T3  = 163.936 deg; T2  -- T3  = 5.6315 A
T2  - O6  - T3  - O9  - T4  =  64.208 deg; T2  -- T4  = 2.9354 A
T2  - O6  - T3  - O10 - T3  =  87.630 deg; T2  -- T3  = 4.1874 A
T3  - O8  - T3  - O9  - T4  = 131.584 deg; T3  -- T4  = 5.2024 A
T3  - O8  - T3  - O10 - T3  =  90.000 deg; T3  -- T3  = 4.3936 A
T4  - O9  - T3  - O10 - T3  =  87.691 deg; T4  -- T3  = 4.1999 A

T2  - O7  - T4  - O10 - T3  =  57.626 deg; T2  -- T3  = 2.7535 A
T2  - O7  - T4  - O11 - T4  =  89.956 deg; T2  -- T4  = 4.2296 A
T2  - O7  - T4  - O12 - T4  = 119.031 deg; T2  -- T4  = 4.8666 A
T3  - O10 - T4  - O11 - T4  =  92.309 deg; T3  -- T4  = 4.1999 A
T3  - O10 - T4  - O12 - T4  = 175.911 deg; T3  -- T4  = 5.4766 A
T4  - O11 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 4.0783 A

T1  - O4  - T5  - O4  - T1  = 178.296 deg; T1  -- T1  = 5.6834 A
T1  - O4  - T5  - O13 - T5  =  90.602 deg; T1  -- T5  = 4.2555 A
T1  - O4  - T5  - O13 - T5  =  90.602 deg; T1  -- T5  = 4.2555 A
T1  - O4  - T5  - O13 - T5  =  90.602 deg; T1  -- T5  = 4.2555 A
T1  - O4  - T5  - O13 - T5  =  90.602 deg; T1  -- T5  = 4.2555 A
T5  - O13 - T5  - O13 - T5  =  90.000 deg; T5  -- T5  = 4.4373 A

        T-T-T SUMMARY
          Range  = 57.6259 deg <--> 178.2963 deg
          Mean   = 104.5793 deg
          StdDev = 33.9274 deg

        T--T SUMMARY
          Range  = 2.7535 A <--> 5.6834 A
          Mean   = 4.4376 A
          StdDev = 0.7751 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 165.244 deg ; T1  -- T1   3.1974 A

T1  -- O2  -- T1  = 153.948 deg ; T1  -- T1   3.1974 A

T1  -- O3  -- T2  = 124.331 deg ; T1  -- T2   2.9069 A

T1  -- O4  -- T5  = 119.456 deg ; T1  -- T5   2.8420 A

T2  -- O5  -- T2  = 142.532 deg ; T2  -- T2   3.0429 A

T2  -- O6  -- T3  = 113.302 deg ; T2  -- T3   2.7535 A

T2  -- O7  -- T4  = 129.161 deg ; T2  -- T4   2.9354 A

T3  -- O8  -- T3  = 176.274 deg ; T3  -- T3   3.2707 A

T3  -- O9  -- T3  = 128.579 deg ; T3  -- T3   2.9337 A

T3  -- O10 -- T4  = 116.189 deg ; T3  -- T4   2.7698 A

T4  -- O11 -- T4  = 111.994 deg ; T4  -- T4   2.7103 A

T4  -- O12 -- T4  = 142.361 deg ; T4  -- T4   3.0474 A

T5  -- O13 -- T5  = 159.976 deg ; T5  -- T5   3.1376 A


        T-O-T SUMMARY
          Range  = 111.9941° <--> 176.2738 deg
          Mean   = 136.2688 deg
          StdDev = 20.3351 deg

        T--T SUMMARY
          Range  = 2.7103 A <--> 3.2707 A
          Mean   = 2.9741 A
          StdDev = 0.1781 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T3  = 2.7535 Angstrom
T3  -- T2  = 2.7535 Angstrom
T3  -- T4  = 2.7698 Angstrom
T4  -- T3  = 2.7698 Angstrom
T4  -- T4  = 2.7103 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 8 10 11 13 16 20 24 28 30 31 33 38 46 55 65
TD10 = 165
Circuit symbol = 4.4.4.6.4.6_{2}
Weight = 12
Vertex symbol  = 4.4.4.6.4.*
Weight = 12

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 10 11 14 17 19 23 26 29 31 36 42 46 52 62
TD10 = 161
Circuit symbol = 3.4.4.6.4.6_{2}
Weight = 11
Vertex symbol  = 3.4.4.6.4.*
Weight = 11

T3 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 10 13 14 16 21 24 23 26 34 39 42 48 55 60
TD10 = 159
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.16.4.*
Weight = 21

T4 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 9 11 14 18 20 21 23 26 30 36 44 49 52 58
TD10 = 154
Circuit symbol = 3.4.4.6.4.6_{2}
Weight = 11
Vertex symbol  = 3.4.4.6.4.16
Weight = 24

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 10 12 12 14 20 26 28 30 32 32 34 44 58 66
TD10 = 164
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.*
Weight = 10

<TD10> = 160.222
Average ring size = 4.2727