Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_8019150_tCS2M5.cif"

There are 432 T-atoms per unit cell
There are 864 O-atoms per unit cell

Framework density = 2.42 T-atoms per nm^3
Material density = 0.242 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5865 Angstrom
T1  -- O2  = 1.6474 Angstrom
T1  -- O3  = 1.6268 Angstrom
T1  -- O4  = 1.6240 Angstrom
      mean = 1.6212 Angstrom
        t1 = 0.022473  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021969  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6470 Angstrom
T2  -- O5  = 1.6371 Angstrom
T2  -- O6  = 1.6278 Angstrom
T2  -- O7  = 1.6504 Angstrom
      mean = 1.6406 Angstrom
        t1 = 0.020343  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004915  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6211 Angstrom
T3  -- O7  = 1.6378 Angstrom
T3  -- O8  = 1.6080 Angstrom
T3  -- O9  = 1.6291 Angstrom
      mean = 1.6240 Angstrom
        t1 = 0.020208  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011976  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.6374 Angstrom
T4  -- O10 = 1.6334 Angstrom
T4  -- O11 = 1.6328 Angstrom
T4  -- O12 = 1.6660 Angstrom
      mean = 1.6424 Angstrom
        t1 = 0.021189  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005153  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.6267 Angstrom
T5  -- O12 = 1.6267 Angstrom
T5  -- O13 = 1.5916 Angstrom
T5  -- O13 = 1.5916 Angstrom
      mean = 1.6092 Angstrom
        t1 = 0.026263  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018908  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5865 A <--> 1.6660 A
          Mean   = 1.6295 A
          StdDev = 0.0190 A

       t1 Range  = 0.0202 <-- 0.0221 --> 0.0263
       t2 Range  = 0.0049 <-- 0.0126 --> 0.0220

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.219 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.472 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 112.550 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 114.410 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.136 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.159 deg; O3  -- O4  = 3 A
       106.472 deg <-- 109.491 deg --> 114.410 deg

O3  -- T2  -- O5  = 109.897 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 110.114 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 106.465 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.510 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.630 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 111.181 deg; O6  -- O7  = 3 A
       106.465 deg <-- 109.466 deg --> 111.181 deg

O4  -- T3  -- O7  = 108.118 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 109.539 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.378 deg; O4  -- O9  = 3 A
O7  -- T3  -- O8  = 107.093 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 114.930 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 107.681 deg; O8  -- O9  = 3 A
       107.093 deg <-- 109.457 deg --> 114.930 deg

O9  -- T4  -- O10 = 109.832 deg; O9  -- O10 = 3 A
O9  -- T4  -- O11 = 109.394 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 109.992 deg; O9  -- O12 = 3 A
O10 -- T4  -- O11 = 108.718 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.632 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.250 deg; O11 -- O12 = 3 A
       108.718 deg <-- 109.470 deg --> 109.992 deg

O12 -- T5  -- O12 = 117.405 deg; O12 -- O12 = 3 A
O12 -- T5  -- O13 = 107.107 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 107.525 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 107.525 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 107.107 deg; O12 -- O13 = 3 A
O13 -- T5  -- O13 = 110.086 deg; O13 -- O13 = 3 A
       107.107 deg <-- 109.459 deg --> 117.405 deg

        O-T-O SUMMARY
          Range  = 106.4649 deg <--> 117.4045 deg
          Mean   = 109.5104 deg
          StdDev = 2.5680 deg

        O--O SUMMARY
          Range  = 2.5743 A <--> 2.7800 A
          Mean   = 2.6588 A
          StdDev = 0.0521 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 174.461 deg; T1  -- T2  = 5.5447 A
T1  - O1  - T1  - O3  - T3  = 119.254 deg; T1  -- T3  = 5.0058 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.0338 A
T2  - O2  - T1  - O3  - T3  =  57.538 deg; T2  -- T3  = 2.7268 A
T2  - O2  - T1  - O4  - T1  =  94.487 deg; T2  -- T1  = 4.0765 A
T3  - O3  - T1  - O4  - T1  =  90.755 deg; T3  -- T1  = 4.1292 A

T1  - O3  - T2  - O5  - T2  = 131.592 deg; T1  -- T2  = 5.1604 A
T1  - O3  - T2  - O6  - T3  =  65.853 deg; T1  -- T3  = 2.9490 A
T1  - O3  - T2  - O7  - T2  =  85.513 deg; T1  -- T2  = 4.0765 A
T2  - O5  - T2  - O6  - T3  = 161.864 deg; T2  -- T3  = 5.6141 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.4125 A
T3  - O6  - T2  - O7  - T2  =  86.378 deg; T3  -- T2  = 4.1263 A

T1  - O4  - T3  - O7  - T2  =  56.610 deg; T1  -- T2  = 2.6983 A
T1  - O4  - T3  - O8  - T4  = 124.030 deg; T1  -- T4  = 5.1796 A
T1  - O4  - T3  - O9  - T3  =  89.245 deg; T1  -- T3  = 4.1292 A
T2  - O7  - T3  - O8  - T4  = 173.094 deg; T2  -- T4  = 5.6330 A
T2  - O7  - T3  - O9  - T3  =  93.622 deg; T2  -- T3  = 4.1263 A
T4  - O8  - T3  - O9  - T3  =  93.264 deg; T4  -- T3  = 4.2497 A

T3  - O9  - T4  - O10 - T4  =  86.736 deg; T3  -- T4  = 4.2497 A
T3  - O9  - T4  - O11 - T5  = 152.772 deg; T3  -- T5  = 5.6030 A
T3  - O9  - T4  - O12 - T4  = 116.652 deg; T3  -- T4  = 5.1372 A
T4  - O10 - T4  - O11 - T5  =  88.720 deg; T4  -- T5  = 4.2822 A
T4  - O10 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 4.5126 A
T5  - O11 - T4  - O12 - T4  =  90.159 deg; T5  -- T4  = 4.2295 A

T4  - O12 - T5  - O12 - T4  = 178.415 deg; T4  -- T4  = 5.6966 A
T4  - O12 - T5  - O13 - T5  =  91.280 deg; T4  -- T5  = 4.2822 A
T4  - O12 - T5  - O13 - T5  =  89.841 deg; T4  -- T5  = 4.2295 A
T4  - O12 - T5  - O13 - T5  =  89.842 deg; T4  -- T5  = 4.2295 A
T4  - O12 - T5  - O13 - T5  =  91.280 deg; T4  -- T5  = 4.2822 A
T5  - O13 - T5  - O13 - T5  =  90.000 deg; T5  -- T5  = 4.4327 A

        T-T-T SUMMARY
          Range  = 56.6097 deg <--> 178.4147 deg
          Mean   = 102.7047 deg
          StdDev = 31.3967 deg

        T--T SUMMARY
          Range  = 2.6983 A <--> 5.6966 A
          Mean   = 4.3965 A
          StdDev = 0.7738 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 127.992 deg ; T1  -- T1   2.8518 A

T1  -- O2  -- T1  = 119.969 deg ; T1  -- T1   2.8529 A

T1  -- O3  -- T2  = 111.014 deg ; T1  -- T2   2.6983 A

T1  -- O4  -- T3  = 130.665 deg ; T1  -- T3   2.9490 A

T2  -- O5  -- T2  = 178.513 deg ; T2  -- T2   3.2740 A

T2  -- O6  -- T2  = 130.653 deg ; T2  -- T2   2.9583 A

T2  -- O7  -- T3  = 112.043 deg ; T2  -- T3   2.7268 A

T3  -- O8  -- T3  = 131.263 deg ; T3  -- T3   2.9295 A

T3  -- O9  -- T4  = 126.462 deg ; T3  -- T4   2.9164 A

T4  -- O10 -- T4  = 145.356 deg ; T4  -- T4   3.1186 A

T4  -- O11 -- T4  = 174.302 deg ; T4  -- T4   3.2616 A

T4  -- O12 -- T5  = 119.782 deg ; T4  -- T5   2.8486 A

T5  -- O13 -- T5  = 159.898 deg ; T5  -- T5   3.1344 A


        T-O-T SUMMARY
          Range  = 111.0136° <--> 178.5130 deg
          Mean   = 135.0370 deg
          StdDev = 21.1535 deg

        T--T SUMMARY
          Range  = 2.6983 A <--> 3.2740 A
          Mean   = 2.9562 A
          StdDev = 0.1770 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.6983 Angstrom
T2  -- T1  = 2.6983 Angstrom
T2  -- T3  = 2.7268 Angstrom
T3  -- T2  = 2.7268 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 9 11 14 18 20 21 23 26 30 36 44 49 52 58
TD10 = 154
Circuit symbol = 3.4.4.6.4.6_{2}
Weight = 11
Vertex symbol  = 3.4.4.6.4.16
Weight = 24

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 10 13 14 16 21 24 23 26 34 39 42 48 55 60
TD10 = 159
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.16.4.*
Weight = 21

T3 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 10 11 14 17 19 23 26 29 31 36 42 46 52 62
TD10 = 161
Circuit symbol = 3.4.4.6.4.6_{2}
Weight = 11
Vertex symbol  = 3.4.4.6.4.*
Weight = 11

T4 (Si): multiplicity = 96
Coordination Sequence =
    1 4 8 10 11 13 16 20 24 28 30 31 33 38 46 55 65
TD10 = 165
Circuit symbol = 4.4.4.6.4.6_{2}
Weight = 12
Vertex symbol  = 4.4.4.6.4.*
Weight = 12

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 10 12 12 14 20 26 28 30 32 32 34 44 58 66
TD10 = 164
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.*
Weight = 10

<TD10> = 160.222
Average ring size = 4.2727